The origin of the intrinsic wear resistance of NbC-based materials is investigated through an assessment of the tribological performance of fully dense, crack-free spark plasma sintered Nb2O5 (here as a reduced polymorph: monoclinic Nb12O29 or NbO2.416). The most likely wear mechanism on NbC is the tribo-oxidation to Nb2O5. The unlubricated (dry) friction and wear behavior of alumina (99.7%) mated against rotating disks of crack-free niobium(V)oxide (Nb2O5) under unidirectional sliding (0.03–10m/s; 22°C and 400°C) and oscillation (f=20 Hz, dx=200 mm, 2/50/98% rel. humidity, n=105/106 cycles) will be presented. The microstructure and mechanical properties of the crack-free Nb2O5 are assessed. The tribological data obtained are benchmarked with different NbC grades, ceramics, cermets and thermally sprayed coatings.
In the present work it was shown that the addition of VC or a combination of VC + Ti(C0.7N0.3) was efficient in reducing the NbC grain growth during liquid phase sintering, when compared to NbC-Ni equivalents. A finest NbC grain size of 1.48 µm was obtained in the NbC-15 Ti(C0.7N0.3)-10 Ni-7.5 VC cermet, exhibiting a hardness of 1486 +/- 7 kg/mm2 and a fracture toughness of 8.7 +/- 0.1 MPa m 1/2.
The tribological profile of alumina (99.7%) mated against binder-less niobium carbide (NbC) rotating disks were determined unidirectional sliding tests (0.17.5 m/s; 22 °C and 400 °C) as well as in oscillation tests (f=20 Hz, Δx=0.2 mm, 2/50/98% rel. humidity, n=105/106 cycles) under un-lubricated (dry) conditions. In addition, the microstructure and mechanical properties of NbC were determined as well. The reason for testing hot-pressed NbC was to avoid side effects generated by sintering additives and/or second phases. The tribological data obtained were benchmarked with different ceramics, cermets and thermally sprayed coatings. NbC exhibited low wear rates under dry sliding associated with high load carrying capacity. The tribological profile established revealed a strong position of NbC under tribological considerations and for closed tribo-systems against traditional references, such as WC, Cr3C2, (Ti,Mo)(C,N), etc.
Thc tribological behavior under dry sliding of a Fe3Al-NbC composite prepared by pyrometallurgical synthesis is compared to NbC-based hard metals bonded by cobalt or Fe3Al. The dry sliding wear resistance (0,1-7/10 m/s) of the present Fe3Al-NbC with 60% NbC was close to those known of NbC-based hard metals. No grain pull-outs or fragmentations of the NbC grains were seen in the wear tracks, as a metallurgical interphase was formed between matrix and NbC grains.
The tribological behavior under dry sliding of a Fe3Al-NbC composite prepared by pyro-metallurgical synthesis is compared to different SPS sintered NbC-based hardmetals bonded by cobalt or Fe3AI. The dry sliding wear resistance (0. 1-7 /10 m/s) of the present Fe3Al-NbC with -60 % NbC was close to those known ofNbC-based hard metals. No grain pull-outs or fragmentations of the NbC grains were seen in the wear tracks of the Fe3Al-NbC composite, as a metallurgical interphase was formed between matrix and NbC grains. The physical prope1ties of melt grown NbC match those known from powder metallurgically sintered NbC using powders converted from Nb205.
NbC has a relatively high hardness (19.6 GPa) and melting temperature (3600 °C) and is usually applied as a grain growth inhibitor in WC–Co hardmetals. The current study reports on the influence of the sintering technology and overall chemical composition on the microstructure and mechanical properties of NbC-based hardmetals, using Co as a binder. The partial replacement of NbC by 5 wt.% WC, Mo2C, VC or TiC allows one to significantly improve the hardness and toughness of the NbC–Co materials. The influence of different binders, i.e., Co, 316L stainless steel and Fe3Al on the microstructure and mechanical properties of NbC-based hardmetals was also investigated. The powder mixtures were sintered in the solid state by PECS and liquid state by conventional vacuum sintering. Detailed microstructural analysis was conducted by EPMA elemental mapping and WDS point analysis. Mechanical properties, including Vickers hardness and indentation toughness were assessed.