This paper presents the progress of successful location of grouting faults in tendon ducts with ultrasonic imaging. The examples were obtained in the research group FOR 384 funded by DFG (German Research Foundation). The co-operation of experimental research and modeling allowed imaging and identification of grouted and ungrouted areas of tendon ducts (including strands) in a large test specimen (40 m²). In addition to the criteria for indicating grouting faults in post-tensioned ducts known until now the phase evaluation of reflected ultrasonic pulses is described. Experiments and modeling of wave propagation are presented for reflections at metal plates in concrete (thickness range 0.5 mm to 40 mm) and for tendon ducts including strands.
The main part of the progress was achieved by automated measurements using dry contact transducers, 3D-SAFT reconstruction including phase evaluation and modeling considering wave propagation for typical elastic parameters and exact experimental site conditions. The results for shear waves as well as for pressure waves are compared in the frequency range from 50 kHz to 120 kHz.
Non-destructive and minor destructive testing methods enable a classification of historic structures, building processes, applied building technologies and materials. Therefore, these methods should be part of the global investigation of historic buildings which is usually required before the planning of any building intervention. The case study presented herein encompasses experimental work carried out at the St. Servatius Church in Quedlinburg, Germany. Within a comprehensive restoration campaign, non-destructive on-site investigations were carried out with radar and ultrasonics. The results were combined with plans, views and cores recorded in advance.
For almost 15 years, carbon fibre-reinforced polymer (CFRP) plates and sheets have been used for strengthening and repair of civil engineering structures. CFRP plates were applied to upgrade structures for change in use or increasing traffic load. CFRP laminates have also been used to repair deteriorated structures such as multi-storey parking or bridges. The execution quality and condition of the strengthening measure in terms of bond integrity were neither monitored nor tested systematically. Inspectors eventually applied simple hammer knocking during regular main inspection for subjective noise distinction as a measure for eventual insufficient bond. This paper presents the feasibility and the limitations of low-frequency transversal ultrasonic waves with dry-coupling point-contact sensors for inspection and defect detection between CFRP laminate and concrete surfaces. The German Centre of Competence in Civil Engineering (DIBt) has initiated a national research project [Helmerich et al. (2012). Condition analysis of bonded CFRP-applications on concrete structures by means of non-destructive testing [in German: Zustandsuntersuchung von CFK-Klebeverstärkungen an Betonbauteilen mittels zerstörungsfreier Prüfung (ZfP)]. Final, internal project report], carried out at the Federal Institute for Materials Research and Testing (BAM), Germany. The aim of the project was to present a potential non-destructive testing method for bond defect detection as a measure for the durability of the strengthening system more than 10 years after application.
Trans-European corridors for transport of people and goods require strengthening of bridges to carry increased axle loads in terms of absolute axle loads and of their frequency. Most of the bridges along highways are reinforced or prestressed concrete bridges.
Since the late 1990s, CFRP laminates have been applied to box girder and T-beam bridges to increase the overall capacity. Although regular inspections are carried out, no special method was available to test the bond condition of CFRP laminates after being in Service for more than ten years. The German Center of Competence in Civil Engineering is aware of this need and funded a research project to investigate the bond condition by means of advanced non-destructive testing (NDT).