- Corrosion (2)
- Aluminium (1)
- Corrosion testing (1)
- Free weathering (1)
- Grinding (1)
- Marine atmosphere (1)
- Stainless steels (1)
Organisationseinheit der BAM
Nine different stainless steel alloys were exposed for 5 years under marine environment and their corrosion behaviour was compared and assessed. The investigation of four different surface finishes for all alloys tested further enabled to consider industry-specific features of the surface finish for the material comparison. The results of the exposure tests yield conclusions regarding the influence of alloy composition, surface finish and exposure duration under marine environment. The three duplex stainless steels revealed excellent corrosion resistance even in case of crevices during the 5 years of exposure under the given exposure conditions. Also the molybdenum-alloyed ferritic steel 1.4521 showed good corrosion resistance comparable to the classical austenitic materials 1.4301 and 1.4404.
The corrosion resistance of aluminium surfaces is closely linked to the surfacecstate after a grinding process. For years, iron‐containing abrasive materials were suspected to lead to increased corrosion susceptibility after processing of aluminium surfaces. To prove a possible correlation between the iron content of an abrasive and the corrosion behaviour of aluminium components, scientific investigations and experimentally practical corrosion tests are necessary.
For the current investigation, specimens of a technical Al‐Si alloy from the same batch were used. The test specimens were mechanically ground with various resin‐bonded model abrasives containing different iron contents. The performed corrosion tests did not reveal a negative influence of the different iron‐containing abrasives on the corrosion behaviour of the Al–Si alloy.
However, the most sensitive measuring method (electrochemical noise)
showed differences in the surface activity depending on the type of abrasive.
Im Zusammenhang mit Planungs- und Entwicklungsaufgaben, den Forderungen in Normen und Regelwerken, in betrieblichen Arbeitsanweisungen, den Vorgaben für Zulieferteile oder bei der Auseinandersetzung mit Schadensfällen stellen sich häufig Fragen zum Korrosionsschutz sowie zu entsprechenden Prüf- und Untersuchungsverfahren. Die daraus gewonnenen Ergebnisse sollen z. B. eine Eignung von Werkstoffen oder Schutzsystemen unter spezifischen Einsatzbedingungen, die Dauerhaftigkeit des Schutzes, den Nachweis einer gleichbleibenden Qualität, die Vergleichbarkeit bekannter mit neuen Korrosionsschutzkonzepten oder den Wirkungsnachweis für gezielte Systemeingriffe belegen. Schnell wird deutlich, dass sich aus dem Blickwinkel verschiedener Branchen ganz unterschiedliche Anforderungsprofile ergeben, die ihren Niederschlag dann in unterschiedlichen Strategien der Prüf- und Untersuchungsverfahren finden.