In order to extend the lifetime of buildings and constructions at the macro scale it is necessary to understand the damage processes of building materials at the micro scale. In particular, durability of reinforced concrete structures is one of the most important equirements for construction planning and restoration of buildings. Therefore degradation mechanisms were reproduced on laboratory specimens.
CT (Computed Tomography) is commonly used for non-destructive microstructural defect analysis for recurring tests on concrete specimens. In this work a few examples of CT applications on cementitious materials (including cement paste, mortar and concrete specimens) will be presented.
Firstly, in order to quantify the degradation processes, specimens analysed were damaged by corrosion due to carbonation and due to chloride ingress. Particular focus has been set to the analysis of cracks.
An automated crack detection tool, developed by Zuse Institut Berlin (ZIB) and BAM in ZIBAmira, has been applied for quantitative analysis of crack parameters and 3D visualization of cracks.
Furthermore the distribution of corrosion products has been evaluated inside the cement matrix and visualized in 3D data sets.
Another important factor for the ageing stability of concrete is the interfacial transition zone (ITZ). The ITZ consists of a layer of cement paste (20 to 40 μm) over every aggregate where porosity is generally increased in comparison with the bulk. This zone could be a preferential zone for transfer of aggressive species. To visualize the ITZ, a small sample of mortar with a diameter of 10mm has been prepared and scanned using the industrial μCT setup at BAM with a spatial resolution of 5μm voxel size. In addition the extracted surface of aggregates could be used for load simulations. We finally show how CT examination of drilled samples taken from building materials in conjunction with laboratory experiments is helpful for further evaluations of damage processes in concrete.
This poster presentation gives an overview of the great potential of X-ray micro computed tomography (CT) to cast light on the evolution of the microstructure in construction materials. Prevention of damage is of major economic and social importance in the development of suitable construction materials such as concrete and asphalt. Therefore a non-destructive testing method such as CT is an appropriate tool for visualization of the inner structure. Its combination with other test methods allows understanding the damage processes such as crack propagation or corrosion. We show examples of internal structure analyses on a wide range of materials: Automatic 3D crack detection and the visualization of corrosion products inside of steel reinforced concrete, pore and shape analysis of lightweight aggregates and the visualization of deformation of high-pressure loaded aerated concrete specimens, distribution of aggregates inside concrete, and determination of the surface of porous asphalt core samples. Segmented structures serve, e.g., as input data for simulation of transport phenomena or virtual load tests.
Corrosion is the major degradation pathway affecting reinforced concrete structures. In the long-term, the rust layer might become thick and slow down the diffusion of oxygen from the atmosphere to the steel. With this in mind, the mineralogy, microstructure and diffusion properties of an old and thick corrosion product layer were investigated. Despite the presence of macropores, the gas diffusion coefficient was found to be low. The impact of the layer on the oxygen diffusion was evaluated using Fick’s law. The results showed that the layer could reduce the flux of oxygen only in a specific configuration.
Functionally graded porous scaffolds (FGPS) constructed with pores of different size arranged as spatially continuous structure based on sheet-based gyroid with three different scaling factors of 0.05, 0.1 and 0.2 were produced by electron beam powder bed fusion. The pore dimensions of the obtained scaffolds satisfy the values required for optimal bone tissue ingrowth. Agglomerates of residual powder were found inside all structures, which required post-manufacturing treatment. Using X-ray Computed Tomography powder agglomerations were visualized and average wall thickness, wall-to-wall distances, micro- and macro-porosities were evaluated. The initial cleaning by powder recovery system (PRS) was insufficient for complete powder removal. Additional treatment by dry ultrasonic vibration (USV) was applied and was found successful for gyroids with the scaling factors of 0.05 and 0.1. Mechanical properties of the samples, including quasi-elastic gradients and first maximum compressive strengths of the structures before and after USV were evaluated to prove that additional treatment does not produce structural damage. The estimated quasi-elastic gradients for gyroids with different scaling factors lie in a range between 2.5 and 2.9 GPa, while the first maximum compressive strength vary from 52.5 for to 59.8 MPa, compressive offset stress vary from 46.2 for to 53.2 MPa.
The osseointegration in/around additively manufactured (AM) lattice structures of a new titanium alloy, Ti–19Nb–14Zr, was evaluated. Different lattices with increasingly high sidewalls gradually closing them were manufactured and implanted in sheep. After removal, the bone–interface implant (BII) and bone–implant contact (BIC) were studied from 3D X-ray computed tomography images. Measured BII of less than 10 µm and BIC of 95% are evidence of excellent osseointegration.
Since AMnaturally leads to a high-roughness surface finish, the wettability of the implant is increased.
The new alloy possesses an increased affinity to the bone. The lattice provides crevices in which the biological tissue can jump in and cling. The combination of these factors is pushing ossification beyond its natural limits. Therefore, the quality and speed of the ossification and osseointegration in/around these Ti–19Nb–14Zr laterally closed lattice implants open the possibility of bone spline key of prostheses. This enables the stabilization of the implant into the bone while keeping the possibility of punctual hooks allowing the implant to be removed more easily if required. Thus, this new titanium alloy and such laterally closed lattice structures are appropriate candidates to be implemented in a new generation of implants.