Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (79)
- Vortrag (49)
- Beitrag zu einem Tagungsband (18)
- Beitrag zu einem Sammelband (13)
- Posterpräsentation (12)
- Buchkapitel (2)
- Forschungsbericht (1)
Sprache
- Englisch (110)
- Deutsch (61)
- Mongolisch (3)
Schlagworte
- Glass (24)
- Sintering (20)
- Crystallization (10)
- LTCC (9)
- Foaming (7)
- Sintern (7)
- Viscosity (7)
- Glas (6)
- Water content (5)
- Crystal growth (4)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (49)
Electric contacts based on silver-glass dispersions are key components in optoelectronic microsystems and control modules for medical, information & communication and energy technology in our networked society. Driven by the complexity of modern production processes and ever shorter time-to-market requirements, the fast and specific development of tailored silver-glass dispersions has become a bottleneck of technology development. Nevertheless, the underlying mechanisms of silver dissolution, transport, and reprecipitation, and the resulting micro structure evolution during firing are poorly understood. The broad literature on the precipitation of colloidal silver particles and the related processes of silver dissolution and diffusion mostly refer to very small volume fractions of silver. Transferring these results to the sintering of glass-containing silver dispersions, is therefore highly questionable. In this case, silver dissolution, electrical contact between silver particles, transport and reprecipitation take place under special conditions. This includes short diffusion lengths (particle size < 10 μm), the presence of three-phase contacts silver - glass - sintering atmosphere, as well as silver reprecipitation at the sintering contacts as the driving force of silver transport. Here, a dynamic balance of the silver concentration can be expected to result from the ratio between silver dissolution and reprecipitation. The aim of the project is to gain basic insight into the mechanisms of dissolution, transport and reprecipitation of silver in sintering silver glass dispersions. In this context, the main focus is on gaining basic knowledge about the dissolution of metallic silver in low melting oxide glasses as the limiting factor of the sintering of silver-glass composites. In particular, we will strive to gain insight into the effect of the oxygen content of the sintering atmosphere, of the oxygen dissolved in the silver particles, of silver oxide on the surface of the silver powder, of the electric contact between the silver particles, as well as the basicity of the glass. Furthermore, we strive for insights into the silver mobility and the silver concentration that can be attained (silver solubility) in oxide glasses with a low melting point. Summing up all these aspects, a closed explanatory model for silver dissolution, transport and reprecipitation during the sintering of glass silver dispersions will be introduced.
Electric contacts based on silver-glass dispersions are key components in optoelectronic microsystems and control modules for medical, information & communication and energy technology in our networked society. Driven by the complexity of modern production processes and ever shorter time-to-market requirements, the fast and specific development of tailored silver-glass dispersions has become a bottleneck of technology development. Nevertheless, the underlying mechanisms of silver dissolution, transport, and reprecipitation, and the resulting micro structure evolution during firing are poorly understood. The broad literature on the precipitation of colloidal silver particles and the related processes of silver dissolution and diffusion mostly refer to very small volume fractions of silver. Transferring these results to the sintering of glass-containing silver dispersions, is therefore highly questionable. In this case, silver dissolution, electrical contact between silver particles, transport and reprecipitation take place under special conditions. This includes short diffusion lengths (particle size < 10 μm), the presence of three-phase contacts silver - glass - sintering atmosphere, as well as silver reprecipitation at the sintering contacts as the driving force of silver transport. Here, a dynamic balance of the silver concentration can be expected to result from the ratio between silver dissolution and reprecipitation. The aim of the project is to gain basic insight into the mechanisms of dissolution, transport and reprecipitation of silver in sintering silver glass dispersions. In this context, the main focus is on gaining basic knowledge about the dissolution of metallic silver in low melting oxide glasses as the limiting factor of the sintering of silver-glass composites. In particular, we will strive to gain insight into the effect of the oxygen content of the sintering atmosphere, of the oxygen dissolved in the silver particles, of silver oxide on the surface of the silver powder, of the electric contact between the silver particles, as well as the basicity of the glass. Furthermore, we strive for insights into the silver mobility and the silver concentration that can be attained (silver solubility) in oxide glasses with a low melting point. Summing up all these aspects, a closed explanatory model for silver dissolution, transport and reprecipitation during the sintering of glass silver dispersions will be introduced.
The sintering of Low Temperature Co-fired Ceramics prepared from alumoborosilicate
glass- and Al2O3 powders of similar small particle size was studied by dilatometry, heating microscopy,
microstructure analysis, glass- and effective viscosity measurements. The steric effect of
Al3O3 inclusions was studied using a gnon-reactiveh model composite. With increasing Al3O3 volume
fraction (Φ ≤ 0.45), sintering decelerates and its final stage shifts to higher temperature. The
attainable shrinkage is reduced as Al2O3 particle clusters bearing residual pores become more frequent.
The kinetics of sintering could be described formally superposing the weighed contributions
of differentially sized and randomly composed glass-crystal particle clusters and assuming a sintering
rate controlled by the effective matrix viscosity, which increases with Φ and with progressive
wetting of Al2O3 particles during densification. The "reactive" model composite shows significant
dissolution of Al2O3 into the glass, which has two opposed effects on sintering: reducing Φ and increasing
glass viscosity. For the present case (Φ = 0.25), the latter effect dominates and sintering is
retarded by Al2O3 dissolution. Crystallization of wollastonite starts after full densification. Dissolution
of Al2O3 was found to promote the subsequent growth of anorthite.
Two fluorescent dyes were incorporated into sol-gel derived SiO2 matrices. The dye was added to SiO2 precursors of different degrees of pre-condensation and the spectroscopic properties of the immobilized dye were measured at various aging and drying stages of the resulting gels. The significant influence of the processing parameters on the spectroscopic properties is manifested in the relative intensity of a second red shifted emission band (550560 nm), which was observed besides the typical coumarin emission band (495 nm). The appearance of this long wavelength emission might be attributed to dye aggregation or to other reactions with the ambient matrix forced by micro porosity phenomena.
Evidence is provided that the tridymite component observed in the X-ray diffraction patterns of some sewage sludge ashes (SSAs) should not be interpreted as the tridymite modification of SiO2 but as the tridymite form of AlPO4. This proof is based on a combined X-ray Powder Diffraction (XRD), X-ray fluorescence (XRF) and Mossbauer spectroscopy investigation of two SSAs produced at two fluidized bed incineration facilities, located in different municipalities and operated differently. The structural and chemical characterization was carried out on the 'as received' SSA samples as well as on the residues of these two SSAs pretreated by leaching in citric acid. In addition, direct proof is presented that the tridymite form of AlPO4 does crystallize from X-ray amorphous precursors under conditions that mimic the huge heating rate and short retention time (just seconds at T ≈ 850 °C) typical for fluidized bed incinerators.
Barium silicate glass powders 4 h milled in CO2 and Ar and sintered in air are studied with microscopy, total carbon analysis, differential thermal Analysis (DTA), vacuum hot extraction mass spectroscopy (VHE-MS), Fourier-transformed infrared (FTIR) spectroscopy, X-ray photoelectron spectroscopy (XPS), and time-of-flight secondary-ion mass spectrometry (TOF-SIMS). Intensive foaming of powder compacts is evident, and VHE studies prove that foaming is predominantly caused by carbonaceous species for both milling gases. DTA Shows that the decomposition of BaCO3 particles mix-milled with glass powders occurs at similar temperatures as foaming of compacts. However, no carbonate at the glass surface could be detected by FTIR spectroscopy, XPS, and TOF-SIMS after heating to the temperature of sintering. Instead, CO2 molecules unable to rotate identified by FTIR spectroscopy after milling, probably trapped by mechanical dissolution into the glass bulk. Such a mechanism or microencapsulation in cracks and particle aggregates can explain the contribution of Ar to foaming after intense milling in Ar atmosphere. The amount of CO2 molecules and Ar, however, cannot fully explain the extent of foaming. Carbonates mechanically dissolved beneath the surface or encapsulated in cracks and micropores of particle aggregates are therefore probably the major foaming source.