The viscosity of silica glasses with different water contents was measured by penetration of sapphire microspheres in the range from 1012-1014·7 Pas at ambient pressure. Commercial silica glasses were used together with hydrous silica glasses, which were prepared by melting glass powder plus water in an internally heated pressure vessel at 2-3 kbar and 1350-1450°C. The temperature dependence of the viscosity of silica glasses with total water contents Cw of 5·4×10-4, 7·0×10-4, 1·00×10-2, and 1·55×10-2(Cw in mass fractions) can be described by Arrhenius equations. From the results, the linear dependence of the T12 isokom (K) with the logarithm of the water content was determined as T12=192-409 logCw. The analysis of the compositional dependence of the T12 isokom in the H2O-Na2O-SiO2 system reveals a temperature depression of up to 200 K for mixed water- and sodium-bearing glasses compared to H2O-SiO2 and Na2O-SiO2 glasses with same molar silica content. From these findings we conclude that protons may contribute significantly to the mixed alkali effect in glasses.