Filtern
Dokumenttyp
Schlagworte
- LTCC (7)
- Inclusions (4)
- Sintering (4)
- Glass matrix composites (3)
- Sintering kinetics (3)
- Glass ceramic composites (2)
- Modeling (2)
- Modelling (2)
- Sintern (2)
- Al2O3-inclusions (1)
- Alumina dissolution (1)
- Crystallization (1)
- Debindering (1)
- Densification (1)
- Effective Viscosity (1)
- Glas Matrix Composites (1)
- Glasig-kristalline Sinterwerkstoffe (1)
- Glasmatrix-Komposit (1)
- Glaspulver (1)
- Glass Matrix Composites (1)
- Glass ceramics (1)
- Horizontaldilatometer (1)
- Kinetic Modelling (1)
- Komposite (1)
- Kristallisation (1)
- Mixing (1)
- Multilayer-Technik (1)
- Powders (1)
- Rietveld analysis (1)
- Rigid Inclusion (1)
- Schwindungsverhalten (1)
- Simulation (1)
- Sintering Kinetics (1)
- Solid-state reaction (1)
- Thermo gravimetry (1)
- Viscosity (1)
The sintering of Low Temperature Co-fired Ceramics prepared from alumoborosilicate
glass- and Al2O3 powders of similar small particle size was studied by dilatometry, heating microscopy,
microstructure analysis, glass- and effective viscosity measurements. The steric effect of
Al3O3 inclusions was studied using a gnon-reactiveh model composite. With increasing Al3O3 volume
fraction (Φ ≤ 0.45), sintering decelerates and its final stage shifts to higher temperature. The
attainable shrinkage is reduced as Al2O3 particle clusters bearing residual pores become more frequent.
The kinetics of sintering could be described formally superposing the weighed contributions
of differentially sized and randomly composed glass-crystal particle clusters and assuming a sintering
rate controlled by the effective matrix viscosity, which increases with Φ and with progressive
wetting of Al2O3 particles during densification. The "reactive" model composite shows significant
dissolution of Al2O3 into the glass, which has two opposed effects on sintering: reducing Φ and increasing
glass viscosity. For the present case (Φ = 0.25), the latter effect dominates and sintering is
retarded by Al2O3 dissolution. Crystallization of wollastonite starts after full densification. Dissolution
of Al2O3 was found to promote the subsequent growth of anorthite.
We studied sintering of LTCC-type glass matrix composites (GMCs) consisting of small glass and alumina particles of equal size. Primarily, crystals act as rigid inclusions, decelerating the densification rate. In later stages, they also dissolve, partially increasing the viscosity. Release of alumina finally induces crystallization of alumosilicates, which enables post-firing stability. To study both effects, two model GMCs were prepared: an α-Al2O3 + barium alumoborosilicate glass (BABS)GMC, which shows neither significant dissolution nor crystallization, and an α-Al2O3 + calcium alumoborosilicate glass (CABS)GMC, which dissolves readily and promotes crystallization. The kinetics of shrinkage for both GMC were modeled by utilizing Frenkel theory for the early stage and MackenzieShuttleworth theory for the late stage, assuming that sintering is superimposed by the weighted contributions of triparticle glasscrystal clusters, their random occurrence (ideal mixing), and a shrinkage rate controlled by the GMC effective viscosity. In agreement with modeling, the experimental results showed that the shrinkage rate of BABSGMC decreases progressively for crystal volume fractions Φ > 0.15. The attainable shrinkage is reduced by up to 8% for Φ = 0.45. For the CABSGMC with Φ = 0.25, a reduction of Φ to 0.20 was evident due to partial α-Al2O3 dissolution. This effect was found able to increase the sintering temperature by ~5060 K.
Green compacts of ceramics, glass ceramic composites and sinter glass ceramics contain
different amounts of organic materials added as pressing aids or binders. Before sintering, these
organics have to burn out completely. In oxidising atmospheres, the debindering process is mostly
exothermic and therefore difficult to control. This uncontrolled heat production due to locally enhanced
debindering and respective gas release may cause damages in the green compact microstructure.
Therefore, debindering is usually operated with very low heating rates (< 3 K/min) which requires
long processing times of many hours. In this paper, we will show that it is possible to reduce
the processing time for debindering dramatically by using the decomposition rate of the organic
binder, detected by the weight loss of the sample, as a control factor of the furnace.
Sintering of LTCC
(2008)
Low Temperature Co-fired Ceramic materials (LTCC) have attracted growing interest in recent years since they are promising candidates for highly integrated ceramic packaging. This paper surveys materials concepts of related glass ceramic composites (GCC) and discusses unsolved problems and challenges. The densification of GCC based on "viscous sintering" may be affected by steric effects and partial dissolution of dispersed crystal particles, crystallization and phase boundary reactions.
Über das Sintern von LTCC
(2007)