Single- and multi-shot ablation thresholds of gold films in the thickness range of 311400 nm were determined employing a Ti:sapphire laser delivering pulses of 28 fs duration, 793 nm center wavelength at 1 kHz repetition rate. The gold layers were deposited on BK7 glass by an electron beam evaporation process and characterized by atomic force microscopy and ellipsometry. A linear dependence of the ablation threshold fluence Fth on the layer thickness d was found for d ≤ 180 nm. If a film thickness of about 180 nm was reached, the damage threshold remained constant at its bulk value. For different numbers of pulses per spot (N-on-1), bulk damage thresholds of ~0.7 J cm-2 (1-on-1), 0.5 J cm-2 (10-on-1), 0.4 J cm-2 (100-on-1), 0.25 J cm-2 (1000-on-1), and 0.2 J cm-2 (10000-on-1) were obtained experimentally indicating an incubation behavior. A characteristic layer thickness of Lc 180 nm can be defined which is a measure for the heat penetration depth within the electron gas before electronphonon relaxation occurs. Lc is by more than an order of magnitude larger than the optical absorption length of α-1 12 nm at 793 nm wavelength.
Hydrogen-Containing Amorphous Carbon Layers as Optical Materials in the Near-IR Spectral Range
(2007)
Hydrogenated amorphous carbon layers were deposited on various substrates by means of a plasma CVD process with a RF substrate bias as well as an ECR plasma source. The optical properties of the a-C:H layers were obtained via spectroscopic ellipsometry and correlated with their mechanical and chemical properties. The layers from pure RF plasma exhibit a higher absorption constant in the visible spectral range and a higher refractive index. All layers are nearly transparent in the NIR spectral range making them candidates for optical thin layer systems. The laser damage behaviour of the a-C:H layers was investigated with ultrashort pulses. The damage thresholds were consistent with the absorption constants of the layers. Interesting damage morphologies were observed indicating a sensitivity of this experiment to sub-structures in the layer.