The friction and wear behaviour of thin hard coatings, such as TiN and the promising class of C-based coatings (a-C, a-C:H, and diamond for example), are compared under oscillating and reciprocating sliding conditions. The typical effects of test parameters, such as stroke, frequency, normal force, relative humidity and test duration, are described as a basis for the proper selection of test conditions or, conversely, for the selection of suitable coatings for particular practical applications.
Friction and wear data from over 1000 vibrating tests using thin hard coatings against 100Cr6 and against Al2O3 have been compiled in a database. This allows easy manipulation and comparison of test results. Using selection criteria and filter procedures (e. g., lifetime of coatings, friction limits, and critical wear rate), suitable coating systems for different test conditions can be chosen from the database. The effects of test parameters on friction and wear behaviour and changes have anyway to be known for meaningful tribotesting, as well as for the selection of coatings.
Fundamentals of Tribotesting
(2000)
Tribology is an experiment-oriented branch of a complex, interdisciplinary science, in which testing plays a major role in the solution of technical problems, in the field as well as in the development of tribomaterials. Various test methods are used for this purpose, and the results are sensitive to the choice of test method and test conditions.
In this paper, the effects of test parameters on friction and wear results are considered, some selected results of model tests with different types of materials are presented, and guidelines are derived, that help improve the reliability and level of confidence of tribological tests performed in laboratories.
Amorphous SiO2 and Si3N4 plasma-enhanced chemical vapour deposited (PECVD) coatings were deposited on two different substrate materials (fused silica and borosilicate glass), with three coating thicknesses (0.1, 0.5, and 1.0 µm). The mechanical properties (hardness and elastic modulus) were determined by depth-sensing indentation, with loads from 700 mN down to 0.1 mN. Tribological behaviour was studied in instrumented oscillating sliding tests at room temperature with a ball-on-flat arrangement, in which the coated disc was tested against an alumina ball, at a load of 1 N. Interpretation of the measurement of hardness and modulus of the coatings has to take into consideration the influence of layer thickness and the effect of the substrate. Tensile film stress and crack generation were only observed for Si3N4 on fused silica above a threshold thickness. Friction and wear measurements show that the coating has an effect on friction, while wear is affected by the thin coatings only for a short running-in phase. The morphology of the wear scars indicates that the coatings have good adhesion. Despite crack generation, delamination effects were not observed. Indentation patterns similarly showed excellent lateral homogeneity of the mechanical properties over the entire film surface, and indicated that load-displacement curves may be used to characterise the system.