The object of this research project related to investigations into the qualification of flux-cored wire electrodes for the laser-GMA hybrid welding of high-alloyed steels. Because of its annular metal shell and the powdery filling, this type of wire electrode permits stable, low-spatter metal transfer comparable with that in the spray arc, particularly in the upper range of the attainable deposition rates. In contrast with this, controlled metal transfer during the deposition of solid wire electrodes is achieved using pulsed arc technology. When these filler materials are welded, the properties specific to the material and to the process have a significant influence on the weld metallurgy as well as on the process stability. Tests were carried out on the AISI 403L (X2CrNi1911) high-alloyed base material in order to investigate the transferability of the attainable material properties from GMA welding to laser-GMA hybrid welding. Four wire electrodes were used according to DIN EN 12072 and DIN EN ISO 17633: a T 19 9 L P M 1 rutile fluxcored wire designed specifically for welding in position, a T 19 9 L R M (C) 3 rutile flux-cored wire suitable for welding in the flat position, a T 19 9 L M M 1 metal-powder flux-cored wire as well as a G 19 9 L Si solid wire.
The roles of microalloying niobium, titanium and vanadium for controlling austenite grain growth, microstructure evolution and hardness were investigated at different simulated heat affected zones (HAZ) for high strength low alloy (HSLA) S690QL steel. High resolution FEG-SEM has been used to characterize fine bainitic ferrite, martensite and nanosized second phases at simulated coarse and fine grain HAZs. It was found that for Ti bearing steel (Ti/N ratio is 2) austenite grain had the slowest growth rate due to the presence of most stable TiN. The fine cuboidal particles promoted intragranular acicular ferrite (IGF) formation. Nb bearing steel exhibited relatively weaker grain growth retardation compared with titanium bearing steels and a mixed microstructure of bainite and martensite was present for all simulated HAZs. IGF existed at coarse grain HAZ of Ti+V bearing steel but it was totally replaced by bainite at fine grain HAZs. Hardness result was closely related to the morphology of bainitic ferrite, intragranular ferrite and second phases within ferrite. The microstructure and hardness results of different simulated HAZs were in good agreement with welded experimental results.
This article presents the latest results of an ongoing national research project on improved models for the prediction of welding residual stresses of thick-plated welded I-girders. The experimental program is presented and the importance of different influencing factors on the residual stresses is discussed in detail. All results are compared for mild (S355J2+N) and high strength (S690QL) steel. Finally, conclusions for further works are drawn.
This article addresses the imperfections caused by the weld assembly in I-shape sections made of two structural steel grades. Load influencing imperfections are assumed as deviations from the ideal shape (e.g. bending distortion) and longitudinal residual stresses. The quality of a numerically aided design of components exposed to either compression and/or bending is significantly affected, depending on these parameters. The Eurocode (EC3) provides robust simplified models. As a result, the Ultimate Limit State (ULS) is approached on a conservative basis. The following investigations are aimed at providing further guidance on these values in component-like specimens. The long term goal is an improved understanding of the load-bearing capacity of such sections. As a first step in this process, the experimental and corresponding numerical studies are presented.
To better understand the mechanism of hydrogen assisted cracking (HAC), it is important to investigate the 3D structure of the cracks non-destructively. Since, cracks introduced by HAC are usually very small, conventional x-ray imaging methods often lack the required spatial resolution.
However, the detection of those cracks can be enhanced by taking advantage of refraction at interfaces within the sample.
To image this refractive deflection we employ analyser based imaging (ABI). In this work we aim at proving the enhanced crack detection of ABI by investigating an alluminum alloy weld.
Low Transformation Temperature (LTT) alloys are high alloyed filler materials, which exhibit a martensitic phase transformation at comparatively low temperatures in order to prevent high tensile residual stresses. A number of publications have already shown that even compressive residual stresses can be observed when using LTT filler materials. Up to know it is not clear in which way this it applicable to multi-run welding exhibiting high shrinkage restraint and complex heat input. In this study the potential for stress reduction during welding of LTT alloys was studied by numerical simulation. This allows for evaluation of the stress development in every single weid run. Additionally, the impact of the structural stiffness was incorporated by modelling a special sample geometry exhibiting a high intensity of restraint. The results show that the stress formation in weid longitudinal direction is determined by the phase transformation as high compressive residual stresses were found here independent from the weid run. On the other hand the transformation induced stresses in weid transverse direction are superimposed by tensile stresses originated from shrinkage restraint. With increasing number of runs the tensile residual stress level is raised. The results were confirmed by residual stress measurements using diffraction methods.
High-strength low-alloyed (HSLA) steels with yield strength ≥ 690 MPa have increasing importance in steel construction and civil engineering. However, weld processing of those steels is a major challenge. The susceptibility for degradation of mechanical properties of weld joints significantly increases in presence of hydrogen and can result in hydrogen assisted cracking (HAC). Generally, risk for HAC increases with increasing yield strength of HSLA steels. To minimize the incidence of HAC, it is essential to gain knowledge about both the (1) absorbed hydrogen amount and its distribution in the weld seam and (2) options to lower
the amount of introduced hydrogen. Existing standards recommend heat treatment procedures (interpass temperature or post weld heat treatment) to reduce the diffusible hydrogen concentration in weldments. In this context, different weld seam geometries should be considered. For HSLA steel fabrication weld processing with seam opening angles of 45° to 60° is typical. Modern weld technologies allow welding with seam opening angles of 30° - reduced welding time and costs. In the present study, the hydrogen distribution in multi-layer welds of a 960 MPa HSLA steel was analysed. Influence of different seam opening angles as well as heat input, interpass temperature and post weld heat treatments were investigated. The welded samples were quenched in ice water immediately after welding and subsequently stored in liquid nitrogen. After defined warming up, small specimens were machined from the weld seam by water jet cutting. The diffusible hydrogen concentration was measured by carrier gas hot extraction with coupled mass spectrometer. The results showed, that low heat input and post weld heat treatment procedures can lower hydrogen concentrations in welds. Furthermore, a gradient of the hydrogen concentration was
identified with increasing weld pool depth. By varying the seam opening angles different hydrogen concentrations were
measured.