Polymer surfaces were modified in low-pressure glow discharge plasmas for introduction of monotype functional groups of different type and density. For this purpose three ways are selected, (i) oxygen plasma treatment followed by wet-chemical reduction of O functional groups to OH groups, (ii) plasma bromination for introducing C - Br groups and (iii) coating by deposition of thin plasma (co-) polymerized layers of functional groups-bearing monomers with OH, NH2, COOH, epoxy etc. functionalities. Subsequently, these groups were used as anchoring points for chemical grafting of spacer molecules, oligomers, prepolymers, fluorescent labels, ionic and nucleic acid residues, employing different chemical routes. The yield in monosort functional groups at polymer surfaces ranged from 1014 (process i), 2040 (process ii) and 1831 groups per 100 C atoms (process iii) as measured by XPS after derivatization. The consumption of functional groups amounted to 4090% of all functionalities present at the surface and depended on the dimensions of grafted molecules. For infinitely variably tuning the number of functional groups process iii was performed as copolymerization of a functional group-carrying comonomer with a non-functionalized (chain-extending) comonomer.
Communication: Fire retardant coatings are deposited on polyamide-66 using plasma polymerisation. Chemical composition and thickness of deposits are adjusted varying the plasma treatment based on hexamethydisiloxane mixed with oxygen. The fire retardancy performances are evaluated using a cone calorimeter. The correlation between fire retardancy and thickness as well as chemical composition is discussed.
Polymer surfaces can be finished with functional groups upon exposure to a plasma. Species of the plasma gas are attached at surface carbon atoms, forming functional groups of different composition. To produce a modified polymer surface with a high density and homogeneity of hydroxyl groups only, the oxygen-plasma-formed oxygen functional groups were chemically reduced by diborane and LiAlH4 with yields of 10 to 11 OH groups per 100 carbon atoms in the 3 to 5 nm near-surface layer as detected by X-ray photoelectron spectroscopy (XPS). The identification of hydroxyl groups was performed by means of attenuated total reflectanceFourier transform infrared spectroscopy and XPS.
The retention of chemical structure and functional groups during pulsed plasma polymerization was used for producing adhesion-promoting plasma polymer layers with high concentrations of exclusively one kind of functional groups, such as OH, NH2, or COOH. The maximum content of functional groups was 31 OH using allyl alcohol, 18 NH2 using allylamine, or 24 COOH per 100 C atoms using acrylic acid. To vary the density of functional groups, chemical co-polymerization with ethylene as 'chain-extending' co-monomer, or butadiene as 'chemical crosslinker' was initiated in the pulsed plasma. The composition of these co-polymers was investigated by XPS and IR spectroscopy. The concentrations of functional groups were measured by derivatizing with fluorine-containing reagents and using XPS. A set of plasma parameters was found to be a good compromise between a high number of functional groups and complete insolubility in water, ethanol or THF,which is needed for further chemical processing. Here, these monotype-functionalized surfaces were used in metal-polymer systems as adhesion-promoting interlayers to examine the influence of type and density of functional groups on adhesion. As expected, COOH- and OH-group-terminated interlayers showed maximum peel strengths to evaporated aluminium layers. The adhesion increased linearly with the number of OH groups to a maximum at about 27 OH per 100 C atoms. Higher concentrations of OH groups did not increase the peel strength further.
In contrast to other plasma modification processes of polymer surfaces, the bromination is very selective and shows a high yield in C—Br groups. The most convenient bromination process was found using bromoform, which was thus preferred to elemental bromine, allyl bromide, vinyl bromide or tert-butylbromide. The bromoform process give yields in C—Br up to 40 C—Br or more, with only 2-3% co-introduction of O-functionalities whereas allyl bromide results in yields of about 20 C—Br and more, but in more than 10% oxygen-containing by-products. C—Br groups serve as anchoring points for grafting of molecules, oligomers and pre-polymers of diole or diamine character.
This new functionalization method consists of the deposition of very thin plasma polymer layers (20 to 100 nm) of functional group bearing monomers in pulsed plasma. With allylalcohol, a maximum of 30 OH groups per 100 C atoms was measured with a selectivity of about 90% and a significant stability at long-time exposure to air. Allylamine was used to produce primary amino groups, with a maximum of 18 NH2 groups per 100 C atoms. Side reactions were observed during the storage in air, such as oxidation of the amino groups. Carboxylic groups could be produced using acrylic acid with a maximum concentration of 24 COOH groups per 100 C atoms. The most prominent side reaction was the decarbonylation/ decarboxylation of the acid group during plasma deposition.___TAGSTART___BR___TAGEND___ The variation of the density of functional groups using the pulsed-plasma polymerization of functional-group-bearing monomers was possible by the chemically-initiated radical copolymerization with either a chain-extending monomer, such as ethylene, or a cross linker, such as butadiene, in plasma. The density of functional groups could be adjusted continuously (0 to 30 OH, 0 to 18 NH2 and 0 to 24 COOH groups per 100 C atoms).___TAGSTART___BR___TAGEND___ The successful application of these densely functionalized polymer surfaces for producing biocompatible surfaces and for use in metalpolymer composites is proposed.
Several approaches were investigated to produce monosort functionalized polymer surfaces with a high density and homogeneity of functional groups: (i) Plasma oxidation followed by wet-chemical reduction, (ii) formation of radicals and grafting on of functional group carrying molecules, (iii) plasma bromination followed by (iv) Williamson or Gabriel-like synthesis of spacer molecules, and (v) a pulsed plasma polymerization of functional groups bearing monomers or (vi) their copolymerisation with other comonomers. The formation of hydroxyl (OH), primary amino (NH2), and carboxyl (COOH) groups was studied in detail. The oxygen plasma treatment (i) in a low-pressure non-isothermal glow discharge results in the formation of a wide variety of O functional groups, polymer degradation and crosslinking. Low power densities and short exposure times (0.1 to 2 s) are required to functionalize a surface while preserving the original polymer structure. Carbonate, ester, and aromatic groups are rapidly degraded by an oxygen plasma treatment leading to scissions of polymer backbones and loss in molecular weight. Also the formation of macrocycles and C=C bonds was observed in a region of around 4 nm in depth. The investigated polymers could be classified by their degradation behaviour on exposure to the oxygen plasma.___TAGSTART___BR___TAGEND___ In order to maximize the process selectivity for OH groups, the variety of oxygen functionalities formed by the oxygen plasma was wet-chemically reduced by diborane, vitridetrade (Na complex), and LiAlH4. Typical yields were 9 to 14 OH groups per 100 carbon atoms.___TAGSTART___BR___TAGEND___ Plasma bromination (iii) (40 Br per 100 C atoms) of polymers, followed by grafting of spacer molecules (iv), has been proved to be a highly selective reaction.___TAGSTART___BR___TAGEND___ Another way to produce high densities of monosort functionalities was the pulsed plasma polymerization of functional group bearing monomers such as allylamine, allylalcohol or acrylic acid (v). The retention of chemical structure and functional groups during plasma polymerization was achieved by using low power densities and the pulsed plasma technique. The maximum yields were 30 OH, 18 NH2, and 24 COOH groups per 100 C atoms. To vary the density of functional groups a chemical copolymerization with ''chain-extending'' comonomers such as butadiene and ethylene was initiated in the pulsed plasma (vi). Additionally, the often-observed post-plasma oxidations of such layers initiated by reaction of trapped radicals with oxygen from the air were successfully suppressed by using NO gas as radical quencher.
The retention of chemical structure and functional groups during plasma polymerization was investigated. Usually plasma polymer layers, prepared by a continuous wave radio-frequency plasma, are often chemically irregular in their structure and composition. To minimize these irregularities low wattages and the pulsed plasma technique were applied to avoid fragmentations. The first goal was to produce plasma polymers comprising double or triple bonds as precursors for electrically conducting polymers. Acetylene, ethylene, butadiene and polystyrene were used as monomers and deposited as thin polymer films by pulsed plasmas of low wattages. Styrene polymerization was strongly enhanced in the dark phase (plasma off) of a pulsed r.f. plasma caused by the reactivity of the vinyl-type double bond. This could be confirmed by a verification of a rather high chemical regularity of the film sample. The oxygen content of this film measured by X-ray photoelectron spectrometry (XPS) was in situ 0% and after 24 h exposure to air lower than 1%. Additionally, post-plasma oxidations of trapped radicals with air could be suppressed using NO gas as radical quencher. Such quenched plasma polymer layers were completely stable against oxidation for a number of weeks. During the low-wattage pulse plasma polymerization metal atoms were simultaneously or layer by layer evaporated into the growing layer and in situ measured by XPS. These metal atoms are acting as dopants. Here, Li, K, Mg and Cr were used at different concentrations providing electrical conductivity and magnetic properties for the film.