A case study on the TEM analysis of the size and shape distribution of TiO2 bipyramidal nanoparticles prepared on TEM grids was included in the recently published ISO standard ISO 21363. It was agreed to organize at a later stage a second inter-lab comparison with the nanoparticles distributed to the participants as a liquid suspension. Protocols for uniform nanoparticle deposition on suited supports developed and optimized within the EMPIR nPSize project are also prepared to be distributed. For this, we have chosen the VAMAS platform (www.vamas.org) which offers an excellent international infrastructure of laboratories with high competence in nanoparticle measurement. The VAMAS technical working area dedicated to nanoparticle measurement is TWA 34 ‘Nanoparticle populations’. For this type of nanoparticles, the size and shape distributions are the primary parameters to be reported. Due to the good deposition protocols developed, an automated image analysis is enabled (in contrast to the manual analysis of irregular TiO2 nanoparticles.
In parallel with the TiO2 nanoparticle exercise, two spherical SiO2 nanoparticle samples with bi-modal size distributions (nominal relative number concentrations of 1:1 and 10:1) are prepared for a second VAMAS inter-lab comparison. Here, the nanoparticle concentration is the primary parameter to be measured. For the imaging methods it is targeted to measure the relative nanoparticle concentrations of the two modes. For the absolute nanoparticle concentration to be measured by imaging methods it is necessary to control the volume of the liquid suspension deposited on the substrate and to obtain such a homogeneous nanoparticle deposition on the substrate which allows to count (or extrapolate) all the deposited particles.
In this paper one refined approach is applied to determine the exact orientation of bipyramidal TiO2 nanoparticles prepared with good dispersion as almost isolated particles on a carbon TEM grid. The advantages of the recently developed high-throughput Transmission Kikuchi Diffraction (TKD) are used to identify quickly and reliably the geometrical orientation of the crystalline TiO2 nanoparticle bipyramids (anatase) on a statistically relevant number of particles.
The characteristics of TiO2 coatings can greatly influence their final performance in large-scale applications. In the present study self-assembly of TiO2 nanoparticles (NPs) in multiple layers was selected as a deposition procedure on various substrates. For this, the main prerequisite constitutes the surface modification of both NPs and substrate with e.g. silane coupling agents. A set of functionalized TiO2 NPs has been produced by reaction with either (3- aminopropyl)triethoxysilane (APTES) or (3-aminopropyl)phosphonic acid (APPA) to functionalize the NP surface with free amino-groups. Then, the complementary functionalized NP set can be obtained from an aliquot of the first one, through the conversion of free surface amino-groups to aldehydes by reaction with glutaraldehyde (GA). Several types of TiO2 NPs differing in size, shape and specific surface area have been functionalized. FTIR, TGA, SEM/EDS, XPS, Auger electron spectroscopy (AES) and ToF-SIMS analyses have been carried out to evaluate the degree of functionalization, all the analytical methods employed demonstrating successful functionalization of TiO2 NP surface with APTES or APPA and GA.
Hydrothermal synthesis of anatase TiO2 nanosheets with a high fraction of exposed {001} facets and related high photocatalytic activity - as an alternative to bipyramidal anatase TiO2 nanoparticles mainly exposing the {101} facets. The scope of the material preparation work is the thermal reduction of residual fluorides from HF (capping agent) induced during the synthesis of TiO2 nanosheets by calcination at 873K. The analytical task consists of detection and localization of fluorine present at the surface and/or in the bulk of TiO2 nanosheets before and after calcination by SEM/EDX, Auger electron spectroscopy and ToF-SIMS.
In the present paper we show an approach of measuring large numbers of nanoparticles in a single scan TKD. TiO2 anatase nanoparticles (NP) of bipyramidal shape were deposited on standard carbon grid used for TEM. The procedure used promoted formation of NP ‘monolayer’ islands with uniform distribution of NPs on the carbon surface which allowed mapping of large number of nanoparticles in the single island.
Collection of whole map covering ~2800 nanoparticles took nearly 20 minutes. Inverse pole figure color coded map indicates that the NPs are either lying on a {101} facet (within 10° range around perfect {101} parallel to the carbon surface orientation) on the carbon film or are lying on a {100} facet (within 10° range around the perfect {100} parallel to the carbon surface orientation). Very unlikely was the NP orientation standing on a {001} face. The NPs size distribution described as equivalent circle diameter (ECD) has been also evaluated and the mean NP ECD was 59 nm with standard deviation of 15 nm, i.e. in good agreement with electron microscopy or AFM results.
This study shows high potential of the technique for crystalline NPs analysis with respect to geometrical orientation of the particles on the substrate. With known orientation, the 3D dimensional characterisation of such non-spherical NPs becomes possible from 2D projection electron micrographs. Moreover, the NP size distribution can be easily extracted. Superior accuracies down to 1-2 nm are achievable. The approach is applicable also on thin lamellae extracted from particulate (or mesoporous) layers.