The aim of this work was to study the interaction between high-density polyethylene (HDPE) grades as material for dangerous goods packagings and biofuels such as E85 and biodiesel. Jerricans made of two polyethylene (PE) grades were filled with these fuels and exposed to temperatures of 20°C and 40°C for 1 year. Tensile properties (tensile strength, breaking elongation and elasticity modulus) and melt flow rate (MFR) were determined once a month, and Fourier transform infrared (FTIR) spectroscopy was used to evaluate changes in the chemical structure.
Measurements of the MFR and tensile properties of the PE grades after 1 year of exposure to E85 showed only a slightly damaging influence. An increase in the peak of 1585 cm-1 (C=C) stretching vibrations is visible in the FTIR spectra after the immersion tests with E85. Therefore, packagings made of HDPE grades are suitable for the transport of E85.
An increase in the MFR with immersion time of the grades in biodiesel was measured, in particular, after 1 year of exposure. The elasticity modulus of the PE grades was reduced with immersion time. The FTIR spectra showed a broadening of the CO peak of 1740 cm-1 and the appearance of the hydroxyl group at 3500 cm-1. Both results are explained by secondary degradation products of the PE decomposition process caused by increasing unsaturated fatty acid content in the biodiesel. In light of the above mentioned, it was concluded that HDPE grades are not suitable as packaging materials for the transport of biodiesel.
The aim of this work was to study the interaction between high density polyethylene (HDPE) grades as material for dangeraus goods packagings and biofuels such as E10 (fuel with 10% ethanol), E85 (fuel with 85% ethanol), biodiesei and 810 (heating oil with 10% biodiesel). Jerricans made of two polyethylene grades were filled with these fuels and exposed to temperatures of 20 oc and 40 oc for more than one year. Tensile properlies (tensile strength, breaking elongation and elasticity modulus) and Melt Flow Rate (MFR) were determined, and Fourier Transform Infrared Spectroscopy (FTIR) was used to evaluate changes in the chemical structure.
Measurements of the MFR and tensile properlies of the polyethylene grades after exposure to E1 0, E85 and 810 showed only a slightly damaging influence. A n increase in the peak of 1585 cm·1 for the (C=C) stretching vibrations was visible in the FTIR spectra after immersion tests with E85. A n increase in the MFR with the immersion time of the grades in biodiesei was measured - in parlicular, after one year of exposure. The elasticity modulus of the polyethylene grades was reduced with the immersion time too. The FTIR spectra showed a broadening of the C=O peak of 1740 cm·1 and the appearance of the hydroxyl group at 3500 cm·1.