- Calcium-carbonate (1)
- Catalysis (1)
- Core-shell (1)
- Crystal-growth (1)
- Fluorapatite-gelatin nanocomposites (1)
- Mechanochemistry (1)
- Nano particles (1)
- Nanoparticle synthesis (1)
- Nanoparticles (1)
- Nickel nanoparticles (1)
Organisationseinheit der BAM
A facile and efficient methodology is described for the solvothermal synthesis of size-tunable, stable, and uniform NiCu core–shell nanoparticles (NPs) for application in catalysis. The diameter of the NPs is tuned in a range from 6 nm to 30 nm and to adjust the Ni:Cu ratio from 30:1 to 1:1. Furthermore, the influence of different reaction parameters on the final NPs is studied. The NPs are structurally characterized by a method combination of transmission electron microscopy, anomalous small-angle X-ray scattering, X-ray absorption fine structure, and X-ray photoelectron spectroscopy. Using these analytical methods, it is possible to elucidate a core–shell–shell structure of all particles and their chemical composition. In all cases, a depletion from the core to the shell is observed, with the core consisting of NiCu alloy, surrounded by an inner Ni-rich shell and an outer NiO shell. The SiO2-supported NiCu core–shell NPs show pronounced selectivity of >99% for CO in the catalytic reduction of CO2 to CO using hydrogen as reactant (reverse water–gas shift reaction) independent of size and Ni:Cu ratio.
The transformation of amorphous precursors into crystalline solids and the associated mechanisms are still poorly understood. We illuminate the formation and reactivity of an amorphous cobalt phosphate hydrate precursor and the role of water for its crystallization process. Amorphous cobalt phosphate hydrate nanoparticles (ACP) with diameters of ∼20 nm were prepared in the absence of additives from aqueous solutions at low concentrations and with short reaction times. To avoid the kinetically controlled transformation of metastable ACP into crystalline Co₃(PO₄)₂ × 8H₂O (CPO) its separation must be fast. The crystallinity of ACP could be controlled through the temperature during precipitation. A second amorphous phase (HT-ACP) containing less water and anhydrous Co₃(PO₄)₂ was formed at higher temperature by the release of coordinating water. ACP contains approximately five molecules of structural water per formula unit as determined by thermal analysis (TGA) and quantitative IR spectroscopy. The Co²+ coordination in ACP is tetrahedral, as shown by XANES/EXAFS spectroscopy, but octahedral in crystalline CPO. ACP is stable in the absence of water even at 500 °C. In the wet state, the transformation of ACP to CPO is triggered by the diffusion and incorporation of water into the structure. Quantitative in situ IR analysis allowed monitoring the crystallization kinetics of ACP in the presence of water.
The reaction of iron chlorides with an alkaline reagent is one of the most prominent methods for the synthesis of iron oxide nanoparticles. We studied the particle formation mechanism using triethanolamine as reactant and stabilizing agent. In situ fast-X-ray absorption near edge spectroscopy and small-angle X-ray scattering provide information on the oxidation state and the structural information at the same time. In situ data were complemented by ex situ transmission electron microscopy, wide-angle X-ray scattering and Raman analysis of the formed nanoparticles. The formation of maghemite nanoparticles (γ-Fe2O3) from ferric and ferrous chloride was investigated. Prior to the formation of these nanoparticles, the formation and conversion of intermediate phases (akaganeite, iron(II, III) hydroxides) was observed which undergoes a morphological and structural collapse. The thus formed small magnetite nanoparticles (Fe3O4) grow further and convert to maghemite with increasing reaction time.
Nickel nanoparticles are an active research area due to their multiple applications as catalysts in different processes. A variety of preparation techniques have been reported for the synthesis of these nanoparticles, including solvothermal, microwave-assisted, and emulsion techniques. The well-studied solvothermal oleylamine synthesis route comes with the drawback of needing standard air-free techniques and often space-consuming glassware. Here, we present a facile and straightforward synthesis method for size-controlled highly monodisperse nickel nanoparticles avoiding the use of, e.g., Schlenk techniques and space-consuming labware. The nanoparticles produced by this novel synthetic route were investigated using small-angle X-ray scattering, transmission electron microscopy, X-ray diffraction, and X-ray spectroscopy. The nanoparticles were in a size range of 4–16 nm, show high sphericity, no oxidation, and no agglomeration after synthesis.
Current time-resolved in situ approaches limit the scope of mechanochemical investigations possible. Here we develop a new, general approach to simultaneously follow the evolution of bulk atomic and electronic structure during a mechanochemical synthesis. This is achieved by coupling two complementary synchrotron-based X-ray methods: X-ray absorption spectroscopy (XAS) and X-ray diffraction. We apply this method to investigate the bottom-up mechanosynthesis of technologically important Au micro and nanoparticles in the presence of three different reducing agents, hydroquinone, sodium citrate, and NaBH4. Moreover, we show how XAS offers new insight into the early stage generation of growth species (e.g. monomers and clusters), which lead to the subsequent formation of nanoparticles. These processes are beyond the detection capabilities of diffraction methods. This combined X-ray approach paves the way to new directions in mechanochemical research of advanced electronic materials.