First results of an inter-laboratory comparison (27 participants in Europe, Japan and USA) of XPS data obtained with non-conducting samples are presented. Binding energies of Al 2s for alumina, N 1s and imide C 1s for Kapton and Sr 3p3/2 for a strontium titanate film on glass were obtained after static charge referencing with the help of 15 nm gold particles deposited at the surface of the test samples. For the alumina sample C 1s static charge referenced data are also presented. Repeat standard deviations (sr), between standard deviations (sb), reproducibility standard deviations (sR) and total means are evaluated from the experimental data. It can be stated that although the repeat standard deviation is as small as 0.05 eV in the best case, the standard deviation characterizing the reproducibility of the method is obviously not better than 0.15 eV in the best case at the present time. The knowledge of these standard deviations is important for metrology, validations of analytical procedures relying on qualitative photoelectron spectroscopy and XPS databanking.
Overlayers of SiO2 (nominally 4, 6 and 8 nm thick) on silicon, prepared by thermal oxidation, were investigated using x-ray photoelectron spectroscopy (XPS). The thickness of these overlayers was obtained from a measurement of the photoelectron intensities originating from the substrate and the oxide overlayer by applying an appropriate quantitative model. The uncertainty budget of that thickness measurement method is given. The relative combined standard uncertainty of the method was found to be 15%. The effective attenuation lengths or the corresponding electron inelastic mean free paths are of considerable importance for both the estimated values of overlayer thickness and combined standard uncertainties. The XPS results were compared with ellipsometry data.
Organic thin films with defined chemical structures and physical properties are required for various applications. Plasma polymerization is of technological interest, since the deposition of plasma polymers is possible on any material of any shape in the desired thickness. We report on the TOF-SIMS (TOF: time-of-flight) and XPS investigations of pulse plasma poly(acetylene) and alkali metal doped pulse plasma poly(acetylene) films. The combination of TOF-SIMS and XPS supplies detailed information on the surface chemistry of these films. Application of both methods provides the possibility for cross-checking certain results. Moreover the different sensitivities of the methods can be utilized. According to the TOF-SIMS and XPS data it can be concluded that the interaction of alkali metals with plasma poly(acetylene) results in electrovalent bonds of the type Me?+C?- between carbon and metal. Furthermore carbonoxygenmetal interactions were observed. These interactions are of the type C=O?-cdots, three dots, centeredMe?+ and/or CO?-Me?+.
Recently, time-of-flight secondary ion mass spectrometry (ToF-SIMS) and X-ray photoelectron spectroscopy (XPS) instrumentation has been used to address areas of interest within micro-fluidic devices providing full access to the surface chemistry established at the bottom of micro-channels therein. After careful calibration, information on surface chemistry as obtained by ToF-SIMS or XPS can be interpreted in terms of wettability expressed as contact angles which are then characteristic for the inner walls of micro-channels. Standard contact angle measurement is not applicable in micro-channels. The approach has been demonstrated to be successful with two different micro-fluidic devices hot embossed into high-end quality poly(methyl methacrylate) (PMMA) or Polycarbonate wafers. A pre-selected surface chemistry at micro-channel walls can be established by plasma technologies but ageing and rinsing effects have to be under control. A combination of ToF-SIMS, XPS and contact angle measurement techniques has been demonstrated to provide the required information. Finally, it is shown by ToF-SIMS and XPS analysis that in the production of micro-fluidic parts during practical processing using hot embossing technologies, material originating from cover foils will reside on the polymer wafer's surface. Moreover, residues of releasing agents as silicone oil used during processing can be detected by ToF-SIMS. Both cover foil residues and silicones are issues of trouble shooting in micro-fluidics because they will change contact angles efficiently.
Microarrays are a versatile platform for diagnostics and high-throughput analysis. Carbohydrate microarrays are valuable tools to investigate interactions with other molecules since many glycans are involved in fundamental biological processes. A combined X-ray photoelectron spectroscopy (XPS) and time-of-flight secondary ion mass spectrometry (ToF-SIMS) surface analysis was used to investigate the basic steps in the production of carbohydrate microarrays. The preparation included coupling of a thiol-terminated mannoside to maleimide-functionalized glass surfaces derived from γ-aminopropyl silane (GAPS) slides. XPS results clearly demonstrate successful chemical modification in each fabrication step, and ToF-SIMS imaging revealed immobilized carbohydrates in the spotted regions of the final microarray.
Self-assembled monolayers of aromatic omega-aminothiols on gold: surface chemistry and reactivity
(2010)
Amino-terminated self-assembled monolayers on gold substrates were studied by X-ray photoelectron spectroscopy (XPS), near-edge X-ray absorption fine structure (NEXAFS) measurements, and atomic force microscopy (AFM). Two different ω-amino-4,4'-terphenyl substituted alkanethiols of the general structure H2N-(C6H4)3-(CH2)n-SH (ATPn) were used: 2-(4''-amino-1,1':4',1''-terphenyl-4-yl)ethane-1-thiol (n = 2, ATP2) and 3-(4''-amino-1,1':4',1''-terphenyl-4-yl)propane-1-thiol (n = 3, ATP3). Moreover, the addressability of amino groups within the films was investigated by chemical derivatization of ATPn SAMs with 3,5-bis(trifluoromethyl)phenyl isothiocyanate (ITC) forming fluorinated thiourea ATPn-F films. Evaluation of high-resolution C 1s and N 1s XPS data revealed successful derivatization of at least 50% of surface amino species. Furthermore, it could be demonstrated by angle-resolved NEXAFS spectroscopy that chemical derivatization with ITC has no noticeable influence on the preferential upright orientation of the molecules in the SAMs.
Results of an interlaboratory comparison of XPS data obtained with stainless steel are presented. Only one photoelectron spectrometer model was used. The stainless-steel sample surfaces were analysed in different states by XPS: as received, after sputtering to I(C 1s)/I(Fe 2p3/2) 0.025 and after removing a chromium-enriched oxide layer following a certain protocol. The Fe, Cr and Ni elemental concentrations were evaluated from the respective XPS data submitted by the participants of the interlaboratory test experiment. Total means, repeat standard deviations (sr) and reproducibility standard deviations (sR) are presented. The best reproducibility standard deviations were obtained for the XPS analysis after removal of a chromium-enriched oxide layer and quantification of the XPS intensities without taking the contamination elements of carbon and oxygen into account. The absolute reproducibility standard deviation of the elemental concentrations in that case is as small as 1.1-1.5 at.%. This gives 2%, 6% and 16% for the relative reproducibility standard deviation of the concentrations of iron, chromium and nickel, respectively. The total means of the iron, chromium and nickel concentrations finally obtained agree within 2sR with bulk values determined by wavelength-dispersive x-ray fluorescence spectroscopy. Comparison to an earlier interlaboratory test experiment shows that using only one model of photoelectron spectrometer reduces the reproducibility standard deviations efficiently. Copyright © 2002 John Wiley & Sons, Ltd.
A combined XPS, NEXAFS, and ToF-SIMS chemical surface characterization of carbohydrate-functionalized gold and glass surfaces is presented. Spot shape and chemical composition across a spot surface are provided by surface-sensitive methods as ToF-SIMS and XPS, used in their imaging modes. Moreover, the feasibility of this multimethod approach to control relevant production steps of a carbohydrate microarray prototype is demonstrated.