Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (30)
- Vortrag (25)
- Beitrag zu einem Tagungsband (8)
- Posterpräsentation (3)
- Buchkapitel (2)
- Beitrag zu einem Sammelband (1)
- Sonstiges (1)
- Forschungsbericht (1)
Schlagworte
- Neutron radiography (15)
- Hydrogen (10)
- Neutron imaging (10)
- Diffusion (8)
- LIBS (8)
- Hydrogen embrittlement (7)
- Welding (7)
- In situ measurement (6)
- Neutron tomography (6)
- Hydrogen diffusion (5)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (25)
We report about diffusion measurements and molecular dynamic simulations
in Al-Ni and Al-Cu melts. Capillary methods were used to measure Ni and
Cu self diffusion and to measure interdiffusion. The combination of the
capillary set-up with X-ray radiography allowed in-situ detecting of
convective contributions to the interdiffusion transport by tracking the
time dependence of diffusion. Thus, the determination of the
interdiffusion coefficient can
be restricted to convection-free experiment times resulting in an
increased accuracy of the measured interdiffusion coefficient.
Additionally, quasielastic neutron scattering was used to measure
convection-free Ni and Cu self diffusion. Molecular dynamics simulations
were used to determine all diffusion coefficients and the thermodynamic
factor. The comparison between experiment and simulation shows an
excellent agreement of the interdiffusion coefficients as a function of
temperature. It was found that interdiffusion is enhanced by
thermodynamic forces with a maximum around the stoichiometric composition.
In recent years, the optimization of the imaging stations at research reactors and especially the further development of the neutron detectors allowed the measurement of hydrogen distributions with increasing spatial and temporal resolution at lower detection limits at the same time. Hydrogen has compared to iron a high total neutron cross section, which allows with basic radiographic methods the visualization of hydrogen in two and three dimensions inside the microstructure of components. This enables the in situ measuring of hydrogen mass flows inside cm thick steel samples with a temporal resolution of 20 s as well as the quantitative measurement of hydrogen accumulations at the crack’s inner surfaces in hydrogen embrittled iron samples. For the first time, we detected directly gaseous hydrogen in the crack cavities and we could measure the gas pressure. This new quality of the information on a micrometer scale allows new insights for the analysis of damage mechanisms, e.g. of hydrogen embrittlement. Further, this method is non-destructive and provides local information in situ and in three dimensions with a spatial resolution of 20-30 µm, which is not accessible with common methods as e.g. thermal desorption spectroscopy.
In this contribution, we show examples that demonstrate the spatial and temporal resolution of the neutron radiography and tomography method in order to visualize and quantify hydrogen accumulations at cracks. The measurements were performed at the research reactor BER II of HZB in Berlin and at the FRM II reactor of the neutron source Heinz Maier-Leibnitz in Garching.
Fast digital radiography was used to observe the crack development during single pass bead-on-plate gas tungsten arc welding with a minifocus X-ray source and a digital detector array with 75-micrometer pixel size. The sample material were 5 mm thick AlMgSi plates. An acquisition rate of 12 frames per second and an exposure time of 40 ms per frame were used for real-time observation of the hot crack propagation during welding. The basic spatial resolution of the images is about 80 µm. A 3D laminographic reconstruction of the acquired 2D radiographic images gives access to the volumetric extent of the cracks in the welded sample. The parallel use of a high-speed camera during welding allows the real-time inspection of surface cracks. The development of surface cracks was compared with the crack’s distribution in the sample volume and these results were correlated to the used welding parameters.
Cold neutrons are predominantly scattered at hydrogen when penetrating hydrogen-charged samples, resulting in a high image contrast between hydrogen and e.g. iron. The used radiographic set-ups consist of a neutron source, state-of-the-art scintillator screens and digital cameras. This allows monitoring diffusive hydrogen fluxes two-dimensionally with 20s temporal resolution. Such hydrogen fluxes can be quantified by using standards with known hydrogen content and similar sample thickness.
Neutron tomography generates three-dimensional models of the hydrogen distribution in steel. Such models gain new insight for damage analysis by showing the hydrogen accumulations around cracks and by enabling the hydrogen gas pressure estimation inside cracks.
The capabilities and limitations, as well as perspectives of this method will be discussed and illustrated with help of selected examples.
Die dehnungsinduzierte Martensitbildung wurde mittels Röntgen-Diffraktion und -Radiographie mit dem EDDI-Instrument am BESSY II in supermartensitischem Stahl mit Anlassaustenit untersucht. Die Bildung wird durch Wasserstoff im Gefüge unterdrückt. Die Duktilität von wasserstofffreiem SMSS korreliert mit dem Anteil an dehnungs-induziertem Martensit
Neutron imaging is a valuable tool for measuring hydrogen distributions qualitatively and quantitatively in metals. Time-resolved neutron radiography allows to measure hydrogen mass flow inside cm thick steel samples with ~10 s temporal resolution. Hydrogen accumulations around cracks in embrittled iron samples can be visualized three-dimensionally by neutron tomography. This quality of information allows new insights for the analysis of damage mechanisms on a micrometer scale, e.g. of hydrogen blistering. Even the gas pressure of molecular hydrogen in crack cavities has been measured from tomographic reconstructions to be in the range of 5 MPa to 15 MPa for technical iron. Further, this method is non-destructive and provides local information in situ and in all three dimensions with a spatial resolution of 20 - 30 µm. The combination with other methods gives a new quality of information, e.g. of the hydrogen allocation on fractured surfaces.
A long list of criteria determining the hot cracking susceptibility already exists. A main influence on solidification cracking can result from the design of the welded construction, i.e. from the influence of external loads. Using the Controlled Tensile Weldability (CTW) test, an external load hot cracking test, the influence of constant pre-load and different extension rates on the solidification cracking behavior of GTA (Gas Tungsten Arc) welds in an austenitic (AISI 309) and a ferritic (AISI 441) steel were investigated. Compared to specimens welded allowing free shrinkage and welded with an applied constant tensile pre-load, the specimens welded during the application of increasing tensile load show solidification cracks. In the weld seams, a characteristic angle α between the predominantly columnar grains and the fusion line can be observed. Specimens showing solidification cracks show a significantly larger angle α compared to the crack-free specimens. Based on these observations, the characteristic angle α is proposed as a new hot cracking criterion.
Neutron Bragg-edge imaging was applied for the visualization of a γ-Austenite to α'-martensite phase transformation. In the present study, a super martensitic
stainless steel sample was heated until complete austenitization and was subsequently cooled down to room temperature. The martensitic phase Transformation started at Ms = 190 °C. Using a monochromatic neutron beam with λ = 0.390 nm, the transmitted intensity was significantly reduced during cooling below Ms, since the emerging martensitic phase has a higher attenuation coefficient than the austenitic phase at this wavelength. The phase Transformation process was visualized by filming the transmission images from a scintillator screen with a CCD camera with a temporal resolution of 30 s and a spatial
resolution of 100 µm.
Hydrogen embrittlement (HE) is a widely known phenomenon and under investigation already for more than a century. This phenomenon, though thoroughly studied, is not yet completely understood, and so far, there are several suggested mechanisms that try to explain the occurrence of HE. One important factor of understanding the HE phenomenon and predicting hydrogen-assisted failure is the descent knowledge about the hydrogen transport behaviour in the material. Neutron radiography is a proven method for tracking hydrogen diffusion and it was applied successfully in various research studies. In the presented study, we examined the hydrogen effusion behaviour in duplex stainless steel by means of neutron radiography and calculated the effective diffusion coefficient from the obtained transmission images.
Gravity has significant effects on alloy solidification, primarily due to thermosolutal convection and solid phase buoyancy. Since 2004, the European Space Agency has been supporting investigation of these effects by promoting in situ X-ray monitoring of the solidification of aluminium alloys on microgravity platforms, on earth, and in periodically varying g conditions. The first microgravity experiment-investigating foaming of liquid metals - was performed on board a sounding rocket, in 2008. In 2012 the first ever X-ray-monitored solidification of a fully dense metallic alloy in space was achieved: the focus was columnar solidification of an Al-Cu alloy. This was followed in 2015 by a similar experiment, investigating equiaxed solidification. Ground reference experiments were completed in all cases. In addition, experiments have been performed on board parabolic flights-where the effects of varying gravity have been studied. We review here the technical and scientific progress to date, and outline future perspectives.
In situ crack detection in the mushy zone and the solid weld of a gas tungsten arc (GTA) weld using X-ray imaging during welding is a new research area for NDT inspection. Usually, NDT flaw detection is done after the complete solidification of the weld seam. In this paper, we present the use of real-time radiography with a minifocus X-ray source (YXLON X-ray tube Y.TU 225-D04) and a 75μm pixel size digital detector array (Dexela 1512) for the acquisition of 2D radiographic images by a sequence of exposures with time intervals of 80 ms for hot crack detection during single pass bead-on-plate GTA welding of 3 mm thick plates of aluminium alloy AlMgSi (6060). An analysis of the crack distribution in the weld sample is conducted from the acquired 2D radiographs and its corresponding 3D volumetric reconstruction achieved by linear coplanar digital laminography.
This in situ approach opens new possibilities in the field of hot crack research by having the direct information of both the crack initiation and growth and its correlation to the welding parameters.
The purpose of the present study is to show the feasibility of examining hydrogen desorption in technical iron samples using neutron radiography at the ANTARES facility of the FRM II research reactor, Technische Universität München. It has been shown that this method is appropriate for in situ determination of hydrogen Desorption for concentrations as low as 20 ppmH. Experiments were carried out in the temperature range from room temperature up to 260 °C. Measurement was based on direct comparison between electrochemically hydrogen-loaded iron samples and hydrogen-free reference samples at the same temperature.
This enables the determination of hydrogen concentration as a function of time and temperature. Ex situ carrier gas hot extraction experiments using the same temperature–time profiles as the neutron radiography experiments have been used to calibrate the greyscale values of the radiographs to defined hydrogen concentrations. It can be stated that hydrogen desorption correlates with sample temperature.
The purpose of the present study was to show the feasibility of measuring hydrogen effusion in austenitic stainless steel (1.4301) using neutron radiography at the facility ANTARES of the research reactor FRM II of the Technische Universität München. This method is appropriate to measure in-situ hydrogen effusion for hydrogen concentrations as small as 20 ppmH. Experiments were carried out in the temperature range from room temperature up to 533 K. The measurement principle is based on the parallel comparison of electrochemically hydrogen charged specimen with hydrogen-free reference specimen at the same temperature. This allows the determination of the hydrogen concentration in the specimens as a function of time and temperature. Separate hot carrier gas extraction experiments using the same temperature–time profiles as the radiography experiments have been used to calibrate the grey values of the neutron transmission images into hydrogen concentrations. It can be stated that the hydrogen effusion correlates with the specimen temperature.