The chemical composition of a weld metal determines the resulting solidification mode of stainless steel and the consequent weld metal quality. In this work tungsten inert gas (TIG) welding of EN grade 1.4435 austenitic stainless steel was monitored using laser-induced breakdown spectroscopy (LIBS) for the in situ measurement of chemical composition changes. This research aims to prototype a real-time chemical composition analysis system for welding applications and prove the feasibility of such quality control loop. LIBS was used to investigate in situ the monitoring of metal vaporization during TIG welding. We found Mn vapor formation above the weld pool and subsequent condensation of Mn on the weld metal surface using LIBS. Post-weld line scans were conducted by LIBS on various welds produced with different welding currents. Local changes of Ni and Mn were observed at higher welding currents. The results are in good agreement with the literature and proved that LIBS can be used in situ to inspect the TIG welding process.
Neutron cameras allow visualizing hydrogen distributions with radiographic or tomographic imaging methods in iron (and steel) and many other metals. The necessary contrast between hydrogen and these metals stems from the high difference in the total neutron cross section of both elements. This allows, e.g., the in situ measurement of hydrogen mass flow inside cm thick metal samples with a temporal resolution of at best 10 s using neutron radiography as well as the quantitative measurement of hydrogen accumulations, e.g., at the crack’s inner surfaces in hydrogen embrittled iron samples with neutron tomography. This new quality of the information on a micrometer scale allows new insights for the analysis of hydrogen-assisted damage mechanisms. Further, this method is non-destructive and provides local information in situ and in three dimensions with a spatial resolution of 20 μm - 30 μm. In this contribution, we give a short historical overview of neutron imaging and show examples that demonstrate the spatial and temporal resolution of the neutron radiography and tomography methods in order to visualize and quantify hydrogen accumulations, absorption processes, and diffusion. The examples are taken from the works of researchers dealing with titanium, palladium, zirconium, and iron or steel. More detailed descriptions of the experimental and analytic procedures are given for hydrogen detection using radiography and tomography on iron and steel samples.
The Modified Varestraint Transvarestraint (MVT) test was used to investigate the solidification cracking susceptibility of an unstabilised, a Nb-stabilised and two (Ti + Nb) dual-stabilised ferritic stainless steels. Two different welding speeds of 6 and 3 mm/s using autogenous gas tungsten arc welding were employed. At the welding speed of 6 mm/s, the high-content (Ti + Nb) steel was resistant and the Nb-stabilised steel was marginally susceptible to solidification cracking. At the welding speed of 3 mm/s, the Nb and the high (Ti + Nb) steels were found to be marginally susceptible to solidification cracking while the unstabilised and low-content (Ti + Nb) grades were resistant to solidification cracking. The weld metal microstructures transverse to the welding direction revealed columnar grains in all the samples for both welding speeds. The ferritic stainless steels were generally resistant to solidification cracking, except the Nb-stabilised steel, which was marginally susceptible to solidification cracking.
A laser-induced breakdown spectroscopy (LIBS) system was combined with a bead-on-plate Tungsten Inert Gas (TIG) welding process for the in situ measurement of chemical compositions in austenitic stainless steels during welding.Monitoring the weld pool's chemical composition allows governing the weld pool solidification behavior, and thus enables the reduction of susceptibility to weld defects. Conventional inspection methods for weld seams (e.g. ultrasonic inspection) cannot be performed during the welding process. The analysis system also allows in situ study of the correlation between the occurrence ofweld defects and changes in the chemical composition in theweld pool or in the two-phase regionwhere solid and liquid phase coexist. First experiments showed that both the shielding Ar gas and the welding arc plasma have a significant effect on the selected Cr II, Ni II and MnII characteristicemissions, namely an artificial increase of intensity values via unspecific emission in the spectra.
In situ investigations showed that this artificial intensity increase reached a maximum in presence of weld plume. Moreover, an explicit decay has been observedwith the termination of thewelding plumedue to infrared radiation during sample cooling. Furthermore, LIBS can be used after welding to map element distribution. For austenitic stainless steels,Mnaccumulations on both sides of theweld could be detected between the heat affected zone (HAZ) and the base material.
Gravity has significant effects on alloy solidification, primarily due to thermosolutal convection and solid phase buoyancy. Since 2004, the European Space Agency has been supporting investigation of these effects by promoting in situ X-ray monitoring of the solidification of aluminium alloys on microgravity platforms, on earth, and in periodically varying g conditions. The first microgravity experiment-investigating foaming of liquid metals - was performed on board a sounding rocket, in 2008. In 2012 the first ever X-ray-monitored solidification of a fully dense metallic alloy in space was achieved: the focus was columnar solidification of an Al-Cu alloy. This was followed in 2015 by a similar experiment, investigating equiaxed solidification. Ground reference experiments were completed in all cases. In addition, experiments have been performed on board parabolic flights-where the effects of varying gravity have been studied. We review here the technical and scientific progress to date, and outline future perspectives.
One of the main advantages of metal additive manufacturing (MAM) techniques is their ability to produce components with site-specific microstructural features. Nevertheless, microstructural defects and lack of repeatability are still major concerns in MAM. In this study, a laser powder bed fusion (PBF-LB/M) IN718 material, produced using two different scan length vectors, is investigated using Bragg-edge neutron 2D imaging (BENI) combined with electron backscatter diffraction (EBSD) analysis. BENI is able to detect, on a macroscopic scale, process-induced changes in texture in a large field of view covering the entire sample (20×80 mm2). In addition, high-resolution BENI (HR-BENI), with a pixel size of 12.8 µm, provides a micro-scale examination of the local variations of texture and grain morphology, otherwise undistinguishable using the standard resolution. As such, HR-BENI offers a straightforward and detailed way of screening the integrity of MAM parts at cm-length scales.
The ISO 3690 standard “Determination of hydrogen content in arc weld metal” requires a thermal activation of the diffusible hydrogen in a piece of weld metal for the subsequent ex situ concentration measurement by carrier gas hot extraction CGHE or thermal desorption spectroscopy (TCD). Laser-induced breakdown spectroscopy (LIBS) offers a time and spatially resolved, almost non-destructive, in situ measurement of hydrogen at surfaces without sample preparation. We measured hydrogen in steels, which were charged either electrochemically or by high-pressure hydrogen gas, and compared the results. Further, the feasibility of quantitative hydrogen line scan measurements with LIBS was demonstrated by measuring hydrogen at water jet cut surfaces. The hydrogen concentrations measured with the help of LIBS were compared with CGHE measurements. It was observed that hydrogen can be reliably measured with LIBS for concentrations larger than 2 wt.-ppm. The maximum hydrogen concentration achieved using electrochemical charging was 85.1 ppm. The results show that LIBS is a promising technique for time- and spatially resolved measurements of hydrogen in steels.