Hydrogen embrittlement (HE) is a widely known phenomenon and under investigation already for more than a century. This phenomenon, though thoroughly studied, is not yet completely understood, and so far, there are several suggested mechanisms that try to explain the occurrence of HE. One important factor of understanding the HE phenomenon and predicting hydrogen-assisted failure is the descent knowledge about the hydrogen transport behaviour in the material. Neutron radiography is a proven method for tracking hydrogen diffusion and it was applied successfully in various research studies. In the presented study, we examined the hydrogen effusion behaviour in duplex stainless steel by means of neutron radiography and calculated the effective diffusion coefficient from the obtained transmission images.
In recent years, the optimization of the imaging stations at research reactors and especially the further development of the neutron detectors allowed the measurement of hydrogen distributions with increasing spatial and temporal resolution at lower detection limits at the same time. Hydrogen has compared to iron a high total neutron cross section, which allows with basic radiographic methods the visualization of hydrogen in two and three dimensions inside the microstructure of components. This enables the in situ measuring of hydrogen mass flows inside cm thick steel samples with a temporal resolution of 20 s as well as the quantitative measurement of hydrogen accumulations at the crack’s inner surfaces in hydrogen embrittled iron samples. For the first time, we detected directly gaseous hydrogen in the crack cavities and we could measure the gas pressure. This new quality of the information on a micrometer scale allows new insights for the analysis of damage mechanisms, e.g. of hydrogen embrittlement. Further, this method is non-destructive and provides local information in situ and in three dimensions with a spatial resolution of 20-30 µm, which is not accessible with common methods as e.g. thermal desorption spectroscopy.
In this contribution, we show examples that demonstrate the spatial and temporal resolution of the neutron radiography and tomography method in order to visualize and quantify hydrogen accumulations at cracks. The measurements were performed at the research reactor BER II of HZB in Berlin and at the FRM II reactor of the neutron source Heinz Maier-Leibnitz in Garching.
Cold neutrons are predominantly scattered at hydrogen when penetrating hydrogen-charged samples, resulting in a high image contrast between hydrogen and e.g. iron. The used radiographic set-ups consist of a neutron source, state-of-the-art scintillator screens and digital cameras. This allows monitoring diffusive hydrogen fluxes two-dimensionally with 20s temporal resolution. Such hydrogen fluxes can be quantified by using standards with known hydrogen content and similar sample thickness.
Neutron tomography generates three-dimensional models of the hydrogen distribution in steel. Such models gain new insight for damage analysis by showing the hydrogen accumulations around cracks and by enabling the hydrogen gas pressure estimation inside cracks.
The capabilities and limitations, as well as perspectives of this method will be discussed and illustrated with help of selected examples.
We investigated the hydrogen distribution spatially and temporally in technical iron at room temperature. Samples were charged electrochemically and subsequently analysed by means of neutron radiography and tomography. The radiographic images allowed for a time-resolved analysis of hydrogen fluxes. The three-dimensional distribution of hydrogen measured by neutron tomography delivered valuable information for the damage analysis of hydrogen-induced cracks. For the first time hydrogen concentration gradients inside the material could be detect directly together with the cracks. The neutron radiography and tomography results were gained at the Research Reactor BER II of the HZB in Berlin.
We investigated hydrogen embrittlement and blistering in electrochemically hydrogen-charged technical iron samples at room temperature. Hydrogen-stimulated cracks and blisters and the corresponding hydrogen distributions were observed by neutron tomography. Cold neutrons were provided by the research reactor BER II to picture the sample with a spatial resolution in the reconstructed three-dimensional model of ~25 µm. We made the unique observation that cracks were filled with molecular hydrogen and that cracks were surrounded by a 50 µm wide zone with a high hydrogen concentration. The zone contains up to ten times more hydrogen than the bulk material. The hydrogen enriched zone can be ascribed to a region of increased local defect density. Hydrogen also accumulated at the sample surface having the highest concentration at blistered areas. The surfaces of the brittle fractured cracks showed micropores visualized by scanning electron microscopy. The micropores were located at grain boundaries and were surrounded by stress fields detected by electron backscattered diffraction. The cracks clearly originated from the micropores.
While the problem of the identification of mechanisms of hydrogen assisted damage has and is being thoroughly studied, the quantitative analysis of such damage still lacks suitable tools. In fact, while, for instance, electron microscopy yields excellent characterization, the quantitative analysis of damage requires at the same time large field-of-views and high spatial resolution. Synchrotron X-ray refraction techniques do possess both features. In this work, we show how synchrotron X-ray refraction computed tomography (SXRCT) can quantify damage induced by hydrogen embrittlement in a lean duplex steel, yielding results that overperform even those achievable by synchrotron X-ray absorption computed tomography. As already reported in literature, but this time using a non-destructive technique, we show that the hydrogen charge does not penetrate to the center of tensile specimens. By the comparison between virgin and hydrogen-charged specimens, we deduce that cracks in the specimen bulk are due to the rolling process rather than hydrogen-assisted. We show that (micro)cracks propagate from the surface of tensile specimens to the interior with increasing applied strain, and we deduce that a significant crack propagation can only be observed short before rupture.
Neutron imaging is a valuable tool for measuring hydrogen distributions qualitatively and quantitatively in metals. Time-resolved neutron radiography allows to measure hydrogen mass flow inside cm thick steel samples with ~10 s temporal resolution. Hydrogen accumulations around cracks in embrittled iron samples can be visualized three-dimensionally by neutron tomography. This quality of information allows new insights for the analysis of damage mechanisms on a micrometer scale, e.g. of hydrogen blistering. Even the gas pressure of molecular hydrogen in crack cavities has been measured from tomographic reconstructions to be in the range of 5 MPa to 15 MPa for technical iron. Further, this method is non-destructive and provides local information in situ and in all three dimensions with a spatial resolution of 20 - 30 µm. The combination with other methods gives a new quality of information, e.g. of the hydrogen allocation on fractured surfaces.