Corrosion of steel reinforcement in concrete exposed to chloride containing environments is a serious problem in civil engineering practice. Electrochemical methods, e.g., potential mapping, provide information whether the steel reinforcement is still passive or depassivation has been initiated. By applying such techniques no information on the type of corrosion, its extent and distribution of corrosion products is available. Particular the corrosion progress is a significant problem. Especially in the case of macrocell corrosion in reinforced concrete structures, the development at the anode cannot be separated into corrosion damage resulting from macrocell corrosion or self-corrosion. Until now also in laboratory tests it is impossible to collect such information without destroying specimens after electrochemical testing was performed. To overcome this problem it was tried to study the steel surface within the mortar specimens by X-ray tomography (CT). Within the scope of these investigations it could be shown, that X-ray tomography is suitable to make corrosion pits and their development visible which are embedded in a mortar with a cover thickness of about 35 mm. In this publication the time-dependent corrosion damage of reinforced steel is documented by X-ray tomography.
By means of synchrotron X-ray computed tomography, model composites consisting of silica and styrenebutadiene rubber were studied with a very high spatial resolution. By our analysis technique we were able to determine the nano- and micro dispersion from the experimental results by our numerical analysis. These results are discussed with respect to crucial advantages of the generically 3-dimensional tomography technique as compared to 2-dimensional methods. Our quantitative analysis of the 3d images demonstrates that in the case of our model composites the filler dispersion is good, independent on the filler concentration. Our new 3-dimensional results evidence that considering only 2-d pictures may lead to ambiguities that can lead to wrong conclusions.
We present a modified aluminium casting which is especially suited as test piece for measuring casting defects and the geometry by means of cone-beam micro-focus X-ray systems, and which may become a reference standard for dimensional measurements and defect detection.
To obtain a test piece with inner geometries measured by tactile means, we divided a small aluminium cylinder head into four pieces in such a way that most inner surfaces can be reached with a tactile probe. Reference geometries (spheres and cylinders) were applied to define a coordinate system for aligning the measurements in the disassembled and re-assembled state. The four pieces were re-assembled after the tactile measurement.
The test piece also contains casting defects. In order to be able to use the assembled cylinder head as reference sample for defect detection, measurements with higher spatial resolution and better signal-to-noise ratio were performed on the single parts. For improving the reliability of the reference measurements, CT measurements of each part were carried out in three different orientations, and the individual defect detections were combined to obtain a reference data set with a high probability of defect detection and a low rate of erroneous detections.
A new method for comparing the defect detection in a CT measurement to a reference data set is demonstrated, which provides individual information on every detected flaw.
We discuss the results of measurements in the assembled state with respect to the reference data for flaw detection.