NEXAFS analysis of a plasma treated, partially crystalline poly(ehtylene terephtalate) surface
(1996)
Plasma-deposited polymer films were prepared from organic molecules and investigated using near edge X-ray absorption fine structure (NEXAFS) and X-ray photoelectron spectroscopy (XPS) for aging effects after exposure to air. Results from the investigation of homopolymers are summarized. Primarily the effect of the deposition parameters duty cycle and power are dealt with. The effect of the deposition parameter pressure is briefly discussed. An example to show the effect of feed gas composition on the aging of plasma polymerized ethylene/allyl alcohol and styrene/allyl alcohol copolymer is also given. In general, change in content of unsaturated or aromatic species, change in concentration of monomer functionality, and change in the oxygen content was observed in the plasma polymerized films on aging.
XPS and NEXAFS spectroscopy were used for the chemical characterization of pulsed plasma-deposited ethylene films before and after exposure to ambient air. The influence of external plasma parameters on the spectroscopic results was investigated. Information on the chemical character of the plasma-polymerized films, such as the regularity of the primary structure, the amount of long-living radicals, and branching or cross-linking or both was derived from this data. Irregularity and radical concentration for post-plasma reactions of the plasma-deposited films increased with the duty cycle or power. A decreased level of monomer fragmentation and, consequently, an increase in regularity is partially concluded from the experimental data when the monomer pressure is increased. The concentration of surface radicals available for post-plasma reactions also increased with monomer pressure. The correlation found between the degree of the post-plasma oxygen incorporation and the variation of the various external parameters agreed with earlier ToF-SSIMS findings.
Chemical properties of plasma-polymerized styrene films can be effectively controlled by the appropriate choice of external plasma parameters, such as duty cycle, power and monomer pressure. Chemical properties here are the regularity of the primary structure, the amount of long living radicals and branching or cross-linking or both in plasma polymerized styrene films, which can be indirectly monitored by X-ray photoelectron spectroscopy (XPS) and near edge X-ray absorption fine structure (NEXAFS) spectroscopy. Principally, XPS and NEXAFS spectra of plasma-polymerized styrene show all the spectroscopic fingerprints characteristic of atactic polystyrene indicating an inherent similarity of the respective primary chemical structures. There is an increase in irregularity and radical concentration for the plasma deposited films with increasing duty cycle or power. With an increase in monomer pressure, a decreased level of monomer fragmentation and, consequently, an increase in regularity must be concluded from the experimental data. The applied power regulates the fragmentation of the monomers as monitored by spectroscopic signals correlated to the aromatic rings. A trend in the extent of the post-plasma oxygen incorporation according to the variation of the various external plasma parameters was deduced, which agrees with earlier ToF-SIMS findings
Selected FTIR, XPS and NEXAFS spectroscopy results obtained with films deposited with different plasma polymerization processes and different monomers (styrene, acetylene, ethylene and butadiene) are presented. In detail FTIR spectra, XPS surveys, XPS valence bands and core level signals including shake-up features as well as carbon K-edge absorption spectra are qualitatively and, in some cases, semi-quantitatively considered. Information on the film formation, the chemistry of the films and the film stability against air exposure are derived from spectroscopic features. With styrene chemically rather well defined plasma polymer layers can be formed with rather high deposition rates applying a pulse plasma process. Using ethylene, acetylene or butadiene as a monomer in the plasma deposition process the deposition rates are smaller. Using these monomers plasma polymer films can be obtained with a primary chemical structure which is similar to each other but more or less different from those of the respective conventional polymers. The main difference between these samples is their individual concentration of unsaturated carbon species. Finally, a technologically relevant example, i.e. a plasma deposited polymer barrier layer deposited on the inner wall of a poly(ethylene) vessel is briefly considered.
Plasma polymerised films of acrylic acid, allyl alcohol and allyl amine were prepared and studied by XPS (X-ray photoelectron spectroscopy) and XAS (X-ray absorption spectroscopy). The influence of external plasma parameters on certain chemical aspects of the films was investigated. The use of XPS and NEXAFS (near edge X-ray absorption fine structure) as complimentary tools in the surface characterisation of thin films has been highlighted. Certain chemical aspects of the plasma polymerised films such as presence of ROCdouble bond; length as m-dashO in the case of plasma polymerised acrylic acid films, presence of RCdouble bond; length as m-dashO and RCOR bonds in case of plasma polymerised allyl alcohol films and presence of RCdouble bond; length as m-dashN and C?N in case of plasma polymerised allyl amine films were studied. The concentration of ROCdouble bond; length as m-dashO species was found to decrease with increase in r.f. duty cycle in the case of plasma polymerised acrylic acid films. In case of plasma polymerised allyl alcohol films there is a decrease in the concentration of RCdouble bond; length as m-dashO species and increase in the concentration of RCOR species at higher pressures, while in the case of plasma polymerised allyl amine films the concentration of RCdouble bond; length as m-dashN and C?N increases at higher powers, with an increase in C?N more pronounced at higher powers.
Br bonding on plasma brominated graphite surfaces has been studied by using Near Edge X-ray Absorption Fine Structure (NEXAFS) and X-ray Photoelectron Spectroscopy (XPS). Br2 and bromoform were used as plasma gases in an r.f. cw low pressure plasma process. Kr plasma had been used to study separately the physical and chemical plasma etching effects. At early steps of plasma bromination which lead to only small XPS Br surface concentration values a quick decay of aromaticity has been observed. At low Br surface concentration radical or even electrophilic addition of bromine onto sp2 carbon atoms is discussed as the dominating reaction pathway. At higher Br surface concentrations the inherent formation of sp3 defects in the graphene network by chemical etching processes promotes nucleophilic substitution of bromine at sp3 carbons as a competing reaction pathway. Both reaction pathways lead to CBr species characterized by the same Br 3d XPS binding energy. However more than one Br 3d component in XP spectra has been found at lower Br2 plasma induced Br surface concentrations and complexation of bromine at HOPG is assumed as a third way of interaction with Br2 plasma.
Plasma deposited styrene/allyl alcohol and ethylene/allyl alcohol copolymer films were prepared and characterized using XPS, NEXAFS and ToF-SIMS. The relative partial flow rates of the co-monomers are used as deposition process parameters to vary and all other process parameters were constrained to conditions optimized for retention of functional groups. By doing this it is possible to control certain chemical properties of the copolymer films such as unsaturation, oxygen and hydroxyl group relative surface contents. The aging behavior of the plasma copolymer films on air was studied, too. Non-linear variations of relative oxygen contents, contents of C—OR species and contents of carbonyl species are obtained vs. variation of feed gas composition for both monomer combinations. The chemical character of the plasma copolymer films varies between the limits given by the respective plasma homopolymers. The observed non-linear correlations are discussed in terms of approaches developed for classic radical copolymerization. The aging behavior of the different plasma copolymers films depends on the feed gas composition. Principally these aging phenomena known from plasma polymer aging studies of that respective monomer which dominates the character of the plasma copolymer are observed.