Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (132)
- Beitrag zu einem Tagungsband (44)
- Beitrag zu einem Sammelband (35)
- Vortrag (29)
- Posterpräsentation (10)
- Buchkapitel (5)
- Monografie (2)
- Sonstiges (1)
Schlagworte
- Plasma polymerization (22)
- Plasma (15)
- NEXAFS (13)
- Plasma modification (9)
- Adhesion (8)
- Surface modification (8)
- Allyl alcohol (7)
- Polymer (7)
- Surface functionalization (7)
- Polystyrene (6)
Eingeladener Vortrag
- nein (29)
1Brominated carbon nanotubes as effective catalysts for petroleum hydrocarbons aerobic oxidation
(2012)
Artificial weathering of LDPE under dry conditions (<10% of relative humidity) by UV radiation was monitored
by dielectric spectroscopy. For an apolar polymer like LDPE, dielectric study yields information
about the change in structure and dynamics of the system. The fluctuations of the polar groups which
are generated as a result of photooxidation such as carbonyl groups can be monitored as characteristic
relaxation processes like the αc or β mode. The dielectric loss characterized by typical dielectric parameters
like the activation energy and dielectric strength are strongly dependent upon changes induced
by photooxidation in the amorphous and crystalline domains. This paper discusses in detail how the foil
reached its mechanical disintegration. It was found that initial stages of weathering induce chain scission
and/or crosslinking in the amorphous domains of the polymer and the motional processes in the crystalline
regions are not affected. After this induction period, an increase in the degree of crystallization was
observed by employing differential calorimetry. The increasing crystallinity is considered as one of the
reasons for embrittlement which finally leads to the complete loss of the structural integrity.
A new concept for molecular interface design in metal-polymer systems is presented. The main features of this concept are the replacement of weak physical interactions by strong covalent bonds, the flexibilization of the interface for compensating different thermal expansions of materials by using long-chain flexible and covalently bonded spacers between the metal and the polymer as well as its design as a moisture-repellent structure for hindering diffusion of water molecules into the interface and hydrolysis of chemical bonds.
For this purpose, the main task was to develop plasmachemical and chemical techniques for equipping polymer surfaces with monotype functional groups of adjustable concentration. The establishing of monotype functional groups allows grafting the functional groups by spacer molecules by applying usual wet-chemical reactions. Four processes were favoured for production of monotype functional groups by highly selective reactions: the plasma bromination, the plasma deposition of plasma polymers, the post-plasma chemical reduction of O-functionalities to OH-groups, and the chemical replacement of bromine groups by NH2-groups. The grafting of flexible organic molecules as spacers between the metal layer and polymer improved the peel strength of the metal. To obtain maximal peel strength of aluminium coatings to polypropylene films and occurrence of cohesive failure in the polypropylene substrate, about 27 OH groups per 100 C-atoms or 6 COOH groups per 100 C-atoms were needed. Introducing C6-11-aliphatic spacers 1 OH or COOH group per 100 C-atoms contributed about 60% of the maximal peel strength of the Al-PP system, i.e. 2 or 3 spacer molecules per 100 C-atoms were sufficient for maximal peel strength.
ToF-SIMS has been used to study the surface functionalization of polypropylene and polyethylene samples by exposure to low-pressure ammonia plasma. Static secondary ion mass spectrometry is an appropriate tool to determine hydrogen isotopes as elements and in fragment ions with high sensitivity and selectivity. Specifically the exchange of hydrogen isotopes and the incorporation of N-containing moieties in the near-surface layer of the polyolefins have been studied in ND3 plasma experiments with conventional polypropylene (h-PP) and polyethylene (h-PE) and NH3 plasma experiments with deuterated polyethylene (d-PE). Considering the exchange of hydrogen between the plasma and the polymer surface studied by using deuterated ammonia and polyolefin samples the conclusion has been derived that polypropylene with its side chain methyl groups is more susceptible to hydrogen exchange reactions. For ND3 plasma treatment of polyethylene and polypropylene similar N-containing fragments were obtained and the measured semi-quantitative ToF-SIMS N-uptake data are rather similar. The observation of a wide range of characteristic mixed CkNlHmDn+ secondary fragment ions suggests complex and manifold reaction pathways at the polymer–plasma interface besides simple grafting of –ND2 or –NH2 moieties formed by ammonia fragmentation in the plasma. Finally, indications of an isotopic effect for hydrogen isotopes in the plasma process have been observed by comparison of ND3/h-PE results with those of NH3/d-PE.
The peel strength of aluminium to polypropylene and poly(tetrafluoroethylene) was determined in dependence on the type and the concentration of functional groups on the polymer surface. For this purpose the polymer surface was equipped with monotype functional groups. The first method to produce monotype functionalized surfaces was an introduction of O functional groups using an oxygen plasma treatment and converting these groups to OH groups applying a wet chemical reduction. In result of this two-step treatment the hydroxyl group concentration at the polymer surface could be increased from 34 to 1014 OH groups/100 C atoms. The second method consists in the deposition of a 150 nm adhesion-promoting layer of plasmapolymers or copolymers onto the polymer surface using the pulsed plasma technique. For that purpose functional groups carrying monomers as allyl alcohol, allylamine and acrylic acid were used. Applying the plasma-initiated copolymerization and using neutral monomers like ethylene or butadiene the concentration of the functional groups was varied.
A correlation of peel strength with the ability of forming chemical interactions between Al atoms and functional groups was found: COOH > OH >> NH2 > H(CH2CH2).
Melamine and melamine resins are widely used as fire retardants for polymer materials used in pharmaceutical, plastic, textile, rubber, and construction industry. Melamine-based flame retardants act by blowing off intumescent layers, char formation, and emission of quenching ammonia gas and diluent molecular nitrogen. Special advantages are: low cost, low smoke density and toxicity, low corrosive activity, safe handling, and environmental friendliness. Methylated poly(melamine-co-formaldehyde) (mPMF) was used as thick (≥40 µm) fire-retardant coating for plasma pretreated polymers. A combined low-pressure plasma pretreatment consisting of oxygen plasma exposure followed by deposition of thin poly(allylamine) (ppAAm) and poly(allyl alcohol) (ppAAl) plasma polymers as adhesion promoters have improved the adhesion of thick mPMF coatings strongly. Chemical structure and composition of deposited polymer films were characterized by infrared-attenuated total reflectance and X-ray photoelectron spectroscopy (XPS). After peeling, the peeled layer surfaces were also investigated for identification of the locus of failure and their topography using optical microscopy and XPS. Often the adhesion promotion was so efficient that the peeling of coating was not possible. Thermal properties of plasma polymers and dip-coating films were analyzed by thermogravimetric analysis. Significant improvement of fire-retardant properties of coated polymers was confirmed by flame tests.