Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (104)
- Beitrag zu einem Tagungsband (34)
- Zeitschriftenartikel (24)
- Forschungsbericht (11)
- Sonstiges (6)
- Posterpräsentation (5)
- Beitrag zu einem Sammelband (3)
- Handbuch (3)
Schlagworte
- Korrosion (107)
- Corrosion (60)
- Potentialfeldmessung (56)
- Betonstahl (18)
- Concrete (15)
- Spannungsrisskorrosion (14)
- Spannstahl (12)
- Wasserstoff (10)
- Potential mapping (8)
- Reinforcement (8)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (104)
Large scale reinforced concrete test specimen for potential mapping under practical conditions
(2017)
Electrochemical potential mapping according to guideline B3 of DGZfP (German Society for Non-Destructive Testing) is a recognized technique for the localization of corroding reinforcing steels. In reinforced concrete structures the measured potentials are not necessarily directly linked to the corrosion likelihood of the reinforcing steel. The measured values may be significantly affected, different from e.g. stress measurement, by different influences on the potential formation at the phase boundary metal/concrete itself as well as the acquisition procedure. Due to the complexity of influencing factors there is a risk that the results are misinterpreted. To investigate these influencing factors under practical conditions it requires a specimen with similar damage patterns, dimensions and more factors e.g. metallic mounting parts. Recently the BAM realized such a large scale test specimen for this purpose.
n der Regel ist die korrosive Beanspruchung der Bewehrung von Stahlbetonbauwerken der lebensdauerbestimmende Faktor eines Bauwerkes. Für die Instandsetzung eines Bauwerkes ist es somit entscheidend im Vorfeld ein Messverfahren zu verwenden das aktive Korrosion detektieren kann, um somit den Umfang von Instandsetzungsmaßnahmen zielgerichtet planen zu können.
The development of alkali‐activated materials (AAMs) as an alternative to Portland cement (PC) has seen significant progress in the past decades. However, there still remains significant uncertainty regarding their long term performance when used in steel‐reinforced structures. The durability of AAMs in such applications depends strongly on the corrosion behaviour of the embedded steel reinforcement, and the experimental data in the literature are limited and in some cases inconsistent. This letter elucidates the role of the chemistry of AAMs on the mechanisms governing passivation and chloride‐induced corrosion of the steel reinforcement, to bring a better understanding of the durability of AAM structures exposed to chloride. The corrosion of the steel reinforcement in AAMs differs significantly from observations in PC; the onset of pitting (or the chloride ‘threshold’ value) depends strongly on the alkalinity, and the redox environment, of these binders. Classifications or standards used to assess the severity of steel corrosion in PC appear not to be directly applicable to AAMs due to important differences in pore solution chemistry and phase assemblage.
Electrochemical half-cell potential measurements for the detection of reinforcement corrosion
(2014)
This specification describes the application of electrochemical half‐cell potential measurements (frequently also called potential mapping) for the detection of reinforcement corrosion in reinforced concrete structures. Areas of corroding reinforcement steel can be located in a nondestructive manner by means of this procedure. Half‐cell potential measurements are used in order to detect chloride‐induced corrosion. However, it is not recommended in order to assess the risk of carbonation‐induced corrosion. For this purpose the determination of the carbonation depth and the concrete cover appear to be more appropriate.
The content of this specification exclusively refers to the application of mobile, local variable reference electrodes, which are only placed on the concrete surface while measuring. The technique distinguishes itself thereby from the range of corrosion monitoring systems with stationary installed reference electrodes and sensor systems, respectively, whereby it is possible to continuously track measurements within the area of the installed electrodes. However, these methods are not dealt with in this specification.
Durch das alkalische Porenwassermilieu ist Stahl im Beton vor Korrosion geschützt. Unter ungünstigen Umgebungsbedingungen (Karbonatisierung, Chlorideintrag) kann die passive Deckschicht auf der Stahloberfläche zerstört werden. Im weiteren Verlauf können sich korrosionsbedingte Folgeschäden, wie Risse und Abplatzungen am Bauwerk ergeben. Um notwendige Sanierungsmaßnahmen sind frühzeitige und weitgehend zerstörungsfrei ermittelte Informationen über das aktuelle Korrosionsverhalten der Stahlbewehrung von großer Bedeutung. Die Potentialfeldmessung ist ein etabliertes und weit verbreitetes Verfahren zur Beurteilung des Korrosionszustandes der Bewehrung in Stahlbetonbauwerken. Mit Hilfe dieses Verfahrens können Bereiche aktiv korrodierender Bewehrung zerstörungsfrei lokalisiert werden. In der Regel kommt diese Messmethode bei der Detektion chloridinduzierter Korrosion zum Einsatz.
Das Merkblatt B3 „Elektrochemische Potentialmessungen zur Detektion von Bewehrungsstahlkorrosion“ ist im Jahr 2014 in der dritten überarbeiteten Fassung erschienen. Die erste Ausgabe des Merkblattes stammte aus dem Jahr 1990. Seitdem hat sich die Potentialfeldmessung von einer Messaufgabe für Korrosionsexperten zu einer Standard-Prüfaufgabe bei der Instandsetzung von (Verkehrs-)Bauwerken und der Ausführung von KKS-Systemen entwickelt. Dieser Entwicklung trägt die Überarbeitung des Merkblatts Rechnung: Während in früheren Fassungen die Verfahrensbeschreibung im Vordergrund stand, rückten bei den Überarbeitungen sukzessiv Maßnahmen zur Sicherstellung einer einheitlichen Qualität bei der Durchführung und Auswertung der Messungen in den Vordergrund. Dieser Trend setzt sich auch in der Merkblatt-Fassung von 2014 fort. So wurde die Durchführung der Messungen gegenüber der Vorgängerversion weiter spezifiziert. Zusätzlich wurden erstmals Vorgaben zur grafischen Darstellung der Messergebnisse aufgenommen und zur statistischen Analyse von Potentialfeldmessdaten, wie sie im europäischen Ausland z.T. üblich ist, kritisch Stellung genommen. Eine weitere wesentliche Ergänzung des Merkblatts sind die Hinweise zur Ausschreibung, die in der Fassung von 2014 erstmals aufgenommen wurden und dazu beitragen sollen, bis dato häufige Missverständnisse bei der Definition der Messaufgabe und der Abgrenzung zwischen Grundleistungen und zusätzlichen Leistungen zukünftig zu vermeiden und so eine bessere Vergleichbarkeit von Angeboten und höhere Kostensicherheit für beide Seiten sicherzustellen.
Ein wesentliches Element bei der Qualitätssicherung ist die Qualifikation des Prüfpersonals. Entsprechende Fortbildungsprogramme werden von der Bundesanstalt für Materialprüfung bereits seit mehreren Jahren angeboten und sind ab 2016 auch von anderen Ausrichtern geplant. Auf diese Angebote wird in dem Merkblatt explizit hingewiesen. Eine verpflichtende Teilnahme an einer Fortbildung im Sinne einer Zertifizierung ist in dieser Fassung des Merkblatts nicht vorgesehen, soll jedoch in zukünftige Merkblatt-Fassungen aufgenommen werden.
Elektrochemische Messungen
(2017)