In the paper the method of discrete modeling (movable cellular automata method) and combined discrete-continuous description of the simulated medium are used to analyze processes occurring in the local contact of the automotive brake system. The characteristic size of the considered region is 1.5 ?m. The following contact situation is simulated: steel fiber coated by an iron oxide film as the brake pad and pearlitic steel also coated by an iron oxide layer as the disc. On the assumption of oxide layer wearing we simulate the iron oxide - iron oxide, iron oxide - metal and metal - metal contacts.
The calculation results for the friction coefficient for various contact situations give quite adequate values. For example, for the oxide - oxide system the calculated coefficient is approximately equal to 0.4, while for the metal - metal contact the obtained value varies from 0.7 to 0.9. Analysis of a set of the obtained results allows concluding that oxide is formed more rapidly than the sliding layer, which in turn makes the friction coefficient value stabilized.
The sliding behaviors of two simplified tribofilms with amorphous structure consisting either of SiO₂ molecules or C atoms were simulated by molecular dynamics modeling. The objective was to identify mechanisms explaining the experimentally observed lubricating properties of the two amorphous films. The impacts of layer thickness, normal pressure, temperature and different substrate materials were studied systematically, while the sliding velocity was kept constant at 30 m/s. While the layer thickness was not critical, all the other parameters showed special effects under certain conditions. Normal pressure impeded void formation and could even eliminate voids if applied at high temperature. Stick-slip sliding was changed to smooth sliding at high temperature due to void healing. Considering the carbon film, high friction forces and shearing of the entire film was observed with diamond substrates, whereas interface sliding at low friction forces and an amorphous layer of iron mixed with carbon was observed if the supporting substrates consisted of α-Fe. Both films show a decrease of friction forces and smooth sliding behavior at elevated temperature, corresponding well to the tribological behavior of and advanced nanocomposite sliding against a steel disc under severe stressing conditions when high flash temperatures can be expected.