The tribological properties of nanostructured surface films formed during dry sliding, for example during
automotive braking, were determined by modelling using the method of movable cellular automata.
Starting from a basic model structure, consisting of magnetite with 13% graphite inclusions, the impact of
additional soft and hard particles of different size and volume fraction was studied systematically. It was
revealed that agglomerates of soft particles decomposed and finally mixed with the oxide in the same
way as single nanoparticles. On the other hand, agglomerates of hard particles mixed with the other
components without decomposing. Whereas increasing the amount of soft components in the third body
lowered the coefficient of friction, the opposite occurred with the hard particles. The boundary conditions
for obtaining smooth sliding conditions with minor fluctuations between friction forces at successive time
steps could be defined. In addition to features of the nanostructure, the applied normal pressure
impacted modelling results. Within the parameter range of smooth sliding behaviour, increasing pressure
induced thicker granular interface layers, which lead to a slight decrease of the coefficient of friction.
Changing the amount of soft or hard particles did not change this pressure dependency but only the
friction level.
This work focuses on surface changes induced by repeated brake applications and tries to provide explanations, how such material modifications might affect friction and wear properties of automotive disc brakes. Surface films were investigated locally by transmission electron microscopy (TEM) after having prepared thin cross-sections with a focused ion beam instrument (FIB). Since the observed friction layers revealed a nanocrystalline structure, modelling with the method of movable cellular automata (MCA) was performed by assuming an array of linked nanometer-sized particles. In spite of complicated material combinations at the pad surface, two very characteristic features were always observed at both the pad and disc surface, namely a steel constituenteither ferritic (pad) or pearlitic (disc), partly covered with patches of nanocrystalline iron oxide, on a zone of severe plastic deformation with fragmented grain structure. When using an automata size of 10 nm, reasonable values for the mean coefficient of friction (COF) were obtained, namely 0.35 and 0.85 for oxide-on-oxide and metal-on-metal contacts, respectively. Immediately after brake application mass-mixing and bond-breaking was observed within a narrow zone at both surfaces.