MSL compatible isothermal furnace insert for high temperature shear-cell diffusion experiments
(2011)
For long-time diffusion experiments shear-cell techniques offer more favourable terms than the traditional long capillary techniques. Here, we present a further developed shear-cell that enables the measurement of diffusion coefficients up to temperatures of 1600 °C. Hence, diffusion experiments can be carried out at temperatures not accessible until now by conventional capillary or shear-cell techniques. The modified shear-cell, which can contain up to six samples of a total length of 90mm and a diameter of 1.5 mm, is built of 30 shear discs of 3mm thickness each. It is operated in an isothermal furnace insert which can be accommodated in the Materials Science Laboratory of the International Space Station. This provides the opportunity that the shear-cell can be applied to microgravity and to ground-based experiments, respectively. The heater insert with an overall length of 518mm and a diameter of 210mm consists of four heating zones with a total power of 3.5 kW. Temperature homogeneity along the graphite sample compartment is better than 2K at 1600°C. Details of the new design are discussed and results of first successfully performed heating and shearing cycles are presented.
The sintering of bioactive glasses allows for the preparation of complex structures, such as three‐dimensional porous scaffolds. Such 3D constructs are particularly interesting for clinical applications of bioactive glasses in bone regeneration, as the scaffolds can act as a guide for in‐growing bone cells, allowing for good Integration with existing and newly formed tissue while the scaffold slowly degrades. Owing to the pronounced tendency of many bioactive glasses to crystallize upon heat treatment, 3D scaffolds have not been much exploited commercially. Here, we investigate the influence of crystallization on the sintering behavior of several bioactive glasses. In a series of mixed‐alkali glasses an increased CaO/alkali metal oxide Ratio improved sintering compared to Bioglass 45S5, where dense sintering was inhibited.
Addition of small amounts of calcium fluoride helped to keep melting and sintering temperatures low. Unlike glass 13‐93, these new glasses crystallized during sintering but this did not prevent densification. Variation in bioactive glass particle size allowed for fine‐tuning the microporosity resulting from the sintering process.