Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (19)
- Vortrag (4)
- Posterpräsentation (4)
- Beitrag zu einem Sammelband (2)
Schlagworte
- Glass (5)
- Water content (4)
- Water speciation (4)
- Borosilicate glass (3)
- Internal friction (3)
- NMR spectroscopy (3)
- Viscosity (3)
- Water-bearing glasses (3)
- Fatigue (2)
- Glass structure (2)
Organisationseinheit der BAM
- 5 Werkstofftechnik (12)
- 5.6 Glas (12)
Eingeladener Vortrag
- nein (4)
The effect of structural water on density, elastic constants and microhardness of water-bearing soda-lime-silica glasses of up to 21.5 mol% total water is studied. It is found that the Poisson ratio and the water content are positively correlated, while density and the elastic moduli decrease with increasing water content. Vickers hardness decreases by approximately 27% from the dry to the most hydrous glass. For water fractions <3 mol%, the dependencies are non-linear reflecting the non-linear change in the concentrations of OH and H2O molecules dissolved, whereas for water fractions >3 mol% linear dependencies are found. To distinguish the effect of structural water and environmental water, indentations were performed in toluene, nitrogen gas and air. Timedependent softening was evident for testing dry glasses in humid atmospheres as well as for tests of hydrous glasses in dry atmospheres. This indicates that the response times of dissolved water species are effectively equal in both scenarios.
Borosilicate glasses (16Na2O–10B2O3–74SiO2, NBS) with water contents up to 22 mol% H2O were prepared to study the effect of water on structural relaxation using DTA, viscometry and internal friction measurements. The results show that the glass transition temperature Tg of DTA and the isokom temperature T12, of viscometry are in excellent agreement, confirming the equivalence of enthalpy and viscous relaxation for NBS glass. Combining Tg data with water speciation data demonstrates that OH groups are mainly responsible for the decrease of Tg with increasing hydration, while molecular water plays only a minor role. Internal friction spectra at 7.125 Hz confirm the decisive influence of water on mechanical relaxation. The temperature range of α-relaxation (glass transition) strongly decreases while two β-relaxation peaks (sub-Tg) progressively appear with increasing water content. A high temperature β-relaxation peak, attributed to the presence of OH groups, shifts from 670 to 450 K as total water content increases from 0.01 to 5 wt%. A low temperature β-relaxation peak, attributed to molecular water, appears at 380 K and 330 K in glasses containing 3 and 5 wt% H2O, respectively. These findings suggest that relaxation mechanism of different hydrous species at low temperature may contribute to fatigue of stressed glasses.
Borosilicate glass has a wide range of technical applications due to its high chemical durability and thermal-shock resistivity. Here the effect of H2O on 16 Na2O, 10 B2O3,74 SiO2 glass is studied over a wide range of water contents from 0 to 8 wt.%. MIR spectra give evidence for the coexistence of strongly and weakly H-bonded hydrous species. Evaluation of NIR bands at 5200 cm-1 (molecular H2O), 4700 cm-1 (B-OH), and 4500 cm-1 (Si-OH) reveal that OH groups dominate up to ~6 wt.% H2O, with B-OH/Si-OH of ≈ 0.8. The incorporation of low amounts of H2O has strong impact on structure. NMR spectra of nominally dry glasses indicate a significant fraction (12 %) of 3-coordinated boron, but almost all boron is 4-coordinated after addition of 3 wt.% H2O. Raman spectra show that hydration results preferentially in transformation of Q4 to Q2 while Q3 remain unchanged, probably stabilized by bonding to BO4 tetrahedra. Viscosity measurements and differential thermal analysis give consistent results, confirming strong decrease of the glass transition temperature with addition of water from 849 K (dry) to 540 K (5 wt% H2O). An additional relaxation mechanism in hydrous glasses is inferred from dynamic mechanical analysis and is assigned to cooperative processes involving hydrous species. It is postulated that this relaxation mechanism plays an important role in crack growth kinetics.
Borosilicate glass has a wide range of technical applications due to its high chemical durability and thermal-shock resistivity. Here the effect of H2O on 16 Na2O, 10 B2O3,74 SiO2 glass is studied over a wide range of water contents from 0 to 8 wt.%. MIR spectra give evidence for the coexistence of strongly and weakly H-bonded hydrous species. Evaluation of NIR bands at 5200 cm-1 (molecular H2O), 4700 cm-1 (B-OH), and 4500 cm-1 (Si-OH) reveal that OH groups dominate up to ~6 wt.% H2O, with B-OH/Si-OH of ≈ 0.8. The incorporation of low amounts of H2O has strong impact on structure. NMR spectra of nominally dry glasses indicate a significant fraction (12 %) of 3-coordinated boron, but almost all boron is 4-coordinated after addition of 3 wt.% H2O. Raman spectra show that hydration results preferentially in transformation of Q4 to Q2 while Q3 remain unchanged, probably stabilized by bonding to BO4 tetrahedra. Viscosity measurements and differential thermal analysis give consistent results, confirming strong decrease of the glass transition temperature with addition of water from 849 K (dry) to 540 K (5 wt% H2O). An additional relaxation mechanism in hydrous glasses is inferred from dynamic mechanical analysis and is assigned to cooperative processes involving hydrous species. It is postulated that this relaxation mechanism plays an important role in crack growth kinetics.
The structural properties of a borosilicate glass with nominal 16 mol% Na2O, 10 mol% B2O3 and 74mol% SiO2 and water contents between 0 and 8wt% H2O (0–22 mol% H2O)were investigated with IR, Raman and 11BMAS NMR spectroscopy. In addition to the pronounced OH stretching vibration band of weakly H-bonded species at 3580 cm−1 the MIR spectra show a triplet at 2900, 2350 and 1750 cm−1, similar as observed in water-bearing silicate glasses. These bands are assigned to OH groups and water molecules which are strongly H-bonded, to non-bridging oxygen. Water species contents determined from absorption bands in the NIR at 5200 cm−1 (molecular H2O), 4700 cm−1 (B\\OH), and 4500 cm−1 (Si\\OH) indicate that hydroxyl groups dominate up to ~6 wt% total H2O. Based on the absorption coefficients known from literature for silicate and borate glasses the B\\OH/Si\\OH ratio is estimated to be ≈0.8.
As indicated by density, Raman and NMR data the incorporation ofwater has strong structural impacts in particular at low water contents up to 3 wt% H2O. While the nominally dry glasses still contain a significant fraction (12%) of three-fold coordinated boron, almost all boron is four-fold coordinated in hydrous glasses. The increase of band components in the Raman spectra near 900 cm−1 relative to the region N 1050 cm−1 gives evidence for depolymerization of the network upon hydration. Fitting of the spectra with Gaussians implies that silica tetrahedra with two non-bridging oxygen (Q2) are preferentially formed by reactionwithwater on expense of tetrahedra linked to four tetrahedra (Q4).
In the present study we have investigated whether the effect of water on properties of borate glasses resembles that of alkali oxide. Soda-lime-borate glasses with nominal compositions of x Na2O, 10 CaO, (90-x) B2O3 (x = 5, 15 and 25 mol%) were doped with up to 8 wt.% H2O by processing glass powder + distilled water in platinum capsules in an internally heated gas pressure vessel at 1523 K and 500 MPa. The water content of hydrous glasses was determined by Karl-Fischer titration and near-infrared spectroscopy. The glass transition temperature T-g. was derived from DTA and micropenetration experiments for which the effect of water loss at the surface of the hydrous glasses was studied. Heating glass samples at 10 K min(-1) in the DTA resulted in T-g values which are close to T-12 isokom temperatures confirming the equivalence of enthalpy relaxation and viscous relaxation for borate glasses. For all three glass series it is shown that T-g strongly decreases whereas the liquid fragility strongly increases upon the addition of water. These findings reveal that H2O primarily causes breaking of B-O-B bonds rather than supporting 4-fold coordinated boron as it is well-known for alkali oxides in this concentration range. (C) 2015 Elsevier B.V. All rights reserved.
As subcritical crack growth (SCCG) can reduce tensile strength of glasses by many orders of magnitude, the potential for improvement of fatigue behaviour is most intriguing in developing ultra-strong glasses. An essential bottleneck is the basic understanding of the numerous interplaying pressure-, temperature- and water-affected relaxation phenomena at the crack tip and related toughening strategies. Therefore, the present project aims to advance the basic understanding of structural relaxation effects and local properties caused by increased water concentration and tensile stresses at the crack tip as they are a key for structural toughening designs to develop SCCG-free glasses and glass surfaces.
Our first studies give clear evidence that glass structure and dynamics is strongly modified upon hydration of glasses. These changes are highly related to the nature of network formers but are affected as well by the counter ions (network modifier). Results of the 1st project part suggest that structural relaxation below glass transition temperature, i.e. overlapping of short-range (beta) and long-range (alpha) interactions can contribute to SCCG in water-free environments and that structurally dissolved water in the glasses can have decisive impact on this effect.
In the 2nd project stage specific glasses compositions will be investigated to gain an improved understanding on the relation of sub-Tg relaxation and inert SCCG as well as to shed light to the related effects of dissolved water and its speciation. These glasses cover a broader range of different glass topologies and binding partners, whereby the coupling of alpha and beta relaxations is varied systematically by alkali-, alkaline earth ions and water species concentrations. Preparation of hydrous glasses (up to 8 wt% water) will be performed by high pressure syntheses. Structure will be resolved by NMR, Raman and IR spectroscopy while structural relaxation is accessed in the temperature and frequency domain using dynamic mechanical spectroscopy and ultrasonic damping. We will focus on measurements of inert SCCG (region III) conducting experiments in vacuum and dry gas atmospheres using indentation techniques and stressing of glass specimens in DCB geometry.
Experimental data on SCCG will be provided to SPP groups, which deals with fatigue in metallic glasses and vice versa we will test theoretical predictions of ab-initio simulations of partner within SPP 1594 in order to quantify the effect of water on the crack tip. In summa topological factors controlling the subcritical crack growth with respect to water will be identified from which structural toughening designs for highly fatigue resistant-glasses can be derived.
As subcritical crack growth (SCCG) can reduce tensile strength of glasses by many orders of magni-tude, the potential for improvement of fatigue behaviour is most intriguing in developing ultra-strong glasses. An essential bottleneck is the basic understanding of the numerous interplaying pressure-, temperature- and water-affected relaxation phenomena at the crack tip and related toughening strat-egies. Therefore, the present project aims to advance the basic understanding of structural relaxa-tion effects and local properties caused by increased water concentration and tensile stresses at the crack tip as they are a key for structural toughening designs to develop SCCG-free glasses and glass surfaces.
Our first studies give clear evidence that glass structure and dynamics is strongly modified upon hy-dration of glasses. These changes are highly related to the nature of network formers but are affect-ed as well by the counter ions (network modifier). Results of the 1st project part suggest that struc-tural relaxation below glass transition temperature, i.e. overlapping of short-range (beta) and long-range (alpha) interactions can contribute to SCCG in water-free environments and that structurally dissolved water in the glasses can have decisive impact on this effect.
In the 2nd project stage specific glasses compositions will be investigated to gain an improved un-derstanding on the relation of sub-Tg relaxation and inert SCCG as well as to shed light to the relat-ed effects of dissolved water and its speciation. These glasses cover a broader range of different glass topologies and binding partners, whereby the coupling of alpha and beta relaxations is varied systematically by alkali-, alkaline earth ions and water species concentrations. Preparation of hy-drous glasses (up to 8 wt% water) will be performed by high pressure syntheses. Structure will be resolved by NMR, Raman and IR spectroscopy while structural relaxation is accessed in the temper-ature and frequency domain using dynamic mechanical spectroscopy and ultrasonic damping. We will focus on measurements of inert SCCG (region III) conducting experiments in vacuum and dry gas atmospheres using indentation techniques and stressing of glass specimens in DCB geometry.
Experimental data on SCCG will be provided to SPP groups, which deals with fatigue in metallic glasses and vice versa we will test theoretical predictions of ab-initio simulations of partner within SPP 1594 in order to quantify the effect of water on the crack tip. In summa topological factors con-trolling the subcritical crack growth with respect to water will be identified from which structural toughening designs for highly fatigue resistant-glasses can be derived.
The structural investigation of hydrated borate glasses provides new insights on the influence of water on boron speciation using spectroscopic methods. In the present study three soda–lime–borate glasses (NCBx with x = 5, 15 and 25 corresponding to xNa2O, 10CaO, 90 - xB2O3 in mol%) were prepared with water content up to 8 wt.%. The water speciation in the glasses was derived by near-infrared (NIR) spectroscopy while boron speciation was investigated by 11B MAS NMR (Magic Angle Spinning Nuclear Magnetic Resonance). For the three glasses effective molar absorption coefficients were determined experimentally for the bands at 5200 cm- 1 and 4600 cm- 1, corresponding to combination modes of H2O molecules and OH-groups, respectively. In contrast to silicate glasses, in which at most ~ 2 wt.% H2O are dissociated to OH-groups, the amount of dissociated H2O may even exceed 5 wt.% in borate glasses. The fraction of tetrahedral to total boron (N4 = BIV / BIV + BIII) is predominantly controlled by the ratio of Na2O + CaO / B2O3, but only weakly affected by the water content of the glasses. When increasing the H2O content from 0 to 8 wt.%, N4 increases from 25% to 26% for NCB5 and from 42% to 47% for NCB25 glasses.