It has been shown that tetraethoxysilane-derived precursors are suitable solutions for impregnating pine sapwood to improve its dimensional stability. Tailored sol–gel syntheses result in precursors with nano-scaled silica species which are able to penetrate into the cell walls of wood. The physical fixation of those species inside the cell walls was verified by ESEM/EDX investigations. There is evidence that the silica species are chemically bonded to wood components. Nonreacted alkoxy groups can exist in the wood composites after impregnation. The amount of these organic residues depends on the composition of the precursors, especially their condensation degree and reactivity. Treatments for finishing the composites after the impregnation step to get clean products and stable properties are discussed in this context. An explanation of the complex relationship between solids content in the impregnation solutions and percentage weight gain and bulking of the composites is given. It can be demonstrated that high WPG values (>20 %) are pre-conditions for an effective protection of the resulting composites but they only guarantee efficient improvements if connected with the incorporation of the inorganic component inside the cell walls. Therefore, the sol–gel syntheses have to be carried out in such a manner that very small (<2 nm) as well as reactive species are sufficiently available. This demands syntheses using sub-stoichiometric water contents (H2O/TEOS <4, better <2).
The antileaching efficacy of sol-gel-derived TiO2- and SiO2-based precursors has been evaluated through laboratory leaching trials with pine sapwood in two different ways. In a one-step process, wood was vacuum impregnated by the precursor solutions containing CuCl2. The copper (Cu) emission rates of the sol-gel-based impregnated woods were up to 70% lower than that of wood treated with pure CuCl2 solution at the same level of concentration. More improvement (80%) could be achieved in a two-step process, in which sol-gel precursors were introduced into an already CuCl2-treated wood. The refinement was attributed to several effects. In the one-step approach, Cu was embedded in the TiO2/SiO2 gels formed in the wood texture. During a two-step impregnation, gel layers that were formed in the wooden interior acted as an effective diffusion barrier. The sol-gel impregnations made wood more hydrophobic; therefore, the low amount of water that penetrated the cell wall was less efficient to leach out Cu.