Filtern
Erscheinungsjahr
- 2019 (111) (entfernen)
Dokumenttyp
- Vortrag (111)
Referierte Publikation
- nein (111) (entfernen)
Schlagworte
- Additive Manufacturing (11)
- Welding (9)
- Wasserstoff (8)
- Additive Fertigung (7)
- Residual stress (7)
- Additive manufacturing (6)
- Hydrogen (6)
- Schweißen (6)
- Thermography (6)
- Hochfeste Feinkornbaustähle (5)
Organisationseinheit der BAM
- 9 Komponentensicherheit (111) (entfernen)
Eingeladener Vortrag
- nein (111) (entfernen)
A numerical framework simulation of the steady-state thermal behaviour in keyhole mode welding has been developed. It is based on the equivalent heat source concept and consists of two parts: computational thermo-fluid dynamics and heat conduction. The solution of the thermo-fluid dynamics problem by the finite element method for a bounded domain results in a weld pool interface geometry being the input data for a subsequent heat conduction problem solved for a workpiece by proposed boundary element method. The main physical phenomena, such as keyhole shape, thermo-capillary and natural convection and temperaturedependent material properties are taken into consideration. The developed technique is applied to complete-penetration keyhole laser beam welding of a 15 mm thick low-alloyed steel plate at a welding speed of 33 mm/s and a laser power of 18 kW. The fluid flow of the molten metal has a strong influence on the weld pool geometry. The thermo-capillary convection is responsible for an increase of the weld pool size near the plate surfaces and a bulge formation near the plate middle plane. The numerical and experimental molten pools, cross-sectional weld dimensions and thermal cycles of the heat affected zone are in close agreement.
Effect of weld penetration depth on hydrogen-assisted cracking of high-strength structural steels
(2019)
The need for steels with highest mechanical properties is a result of the increasing demands for energy and resource efficiency. In this context, high-strength structural (HSS) steels are used in machine, steel and crane construction with yield strength up to 960 MPa. However, welding of HSS steels requires profound knowledge of three factors in terms of avoidance of hydrogen-assisted cracking (HAC): the interaction of (1) microstructure, (2) local stress/strain and (3) local hydrogen concentration. In addition to the three main factors, the used weld-arc process is also important for the performance of the welded joint, especially when using modern arc variants. In the past, the conventional transitional arc process (Conv. A) was mainly used for welding of HSS grades. In the past decade, the so-called modified spray arc process (Mod. SA) has been used increasingly for welding production. This modified process enables reduced seam opening angles with increased deposition rates compared to the conventional process. Economic benefits of using this arc type are: a reduced number of necessary weld beads and a lower weld seam volume, which result in decreased total welding time and costs. Nonetheless, investigations on a high-strength S960QL showed significantly higher hydrogen concentrations in the weld metal at a reduced seam opening angle with Mod. SA. This indicates an increased susceptibility of the welded component to HAC. Hence, existing recommendations on HAC-avoidance cannot be transferred directly to the Mod. SA-process. In the present study, the susceptibility to HAC of the HSS steel S960QL with same type of filler material was investigated. For that purpose, both Conv. A and Mod. SA were used with same heat input at different deposition rates. For assessment of the HAC susceptibility, the externally loaded implant test was used. Both conducted test series with Conv. A and Mod. SA showed similar crack critical stress of about 280 MPa. Below this value, no delayed fracture appeared. The welds with Mod. SA showed higher hydrogen concentrations. The fracture occurred in the heat-affected zone (HAZ) or in the weld metal (WM). However, the test series with Mod. SA showed a significant extension of the time to failure of several hours compared to tests carried out with Conv. A.
9 %-Cr steel P91 is widely used in power plants due to the excellent creep-resistance. Components of this steel are typically welded and demand for careful welding fabrication, whereas a so-called post weld heat treatment (PWHT), must be conducted to increase the toughness and decrease the hardness of the martensitic as-welded (AW) microstructure. Before the PWHT, a hydrogen removal (or dehydrogenation) heat treatment is necessary as hardened AW martensitic microstructure is generally prone to delayed hydrogen assisted cracking (HAC). The microstructure and temperature dependent hydrogen diffusion is an important issue as it determines how long a potential crack-critical hydrogen concentration could remain in the microstructure. In this context, reliable hydrogen diffusion coefficients of P91 weld metal are rare. Hence, the diffusion behavior of P91 multi-layer weld metal was investigated in two different microstructure conditions: AW and further PWHT (760 °C for 4 h). Two different experimental techniques were used to cover a wide range of hydrogen diffusion temperatures: the electrochemical permeation technique (PT) at room temperature and the carrier gas hot extraction (CGHE) for a temperature range from 100 to 400 °C. From both techniques typical hydrogen diffusion coefficients were calculated and the corresponding hydrogen concentration was measured. It was ascertained that both heat treatment conditions show significant differences in hydrogen diffusivity. The biggest deviations were identified for room temperature. In this case, the AW condition shows significant hydrogen trapping and up to seven times lower diffusion coefficients. Additionally, PT investigations showed a preferred diffusion direction of hydrogen in the weld metal expressed by the diffusion coefficients and the permeability for both heat treatment conditions. The CGHE generally revealed lower diffusion coefficients for the AW microstructure up to 200 °C. In addition, the AW condition showed hydrogen concentrations up to 50 ml/100 g (considering electrochemical charging). Nonetheless, this hydrogen was not permanently (reversibly) trapped. Nonetheless, this temperature is approximately 100 °C below recommended dehydrogenation heat treatment (DHT). This has two main consequences: (I) in case of welding is interrupted or no DHT is conducted, a HAC susceptibility of hardened martensitic P91 weld metal cannot be excluded and (II) DHT can be conducted at temperatures around 200 °C below the recommended temperatures.
9 %-Cr steels like P91 and P92 are widely used in power plants due to the excellent creep-resistance. Components of this steel are typically welded and demand for careful welding fabrication, whereas a so-called post weld heat treatment (PWHT), must be conducted to increase the toughness and decrease the hardness of the martensitic as-welded (AW) microstructure. Before the PWHT, a hydrogen removal (or dehydrogenation) heat treatment is necessary as hardened AW martensitic microstructure is generally prone to delayed hydrogen assisted cracking (HAC). The microstructure and temperature dependent hydrogen diffusion is an important issue as it determines how long a potential crack-critical hydrogen concentration could remain in the microstructure. In this context, reliable hydrogen diffusion coefficients of P91 and P92 weld metal are rare.
Hydrogen was once called “the versatile embrittler” [1], which summarizes very well the effect on reduction of ductility and/or toughness in technical alloys like steel. In that connection, welding is one of the most important component fabrication technologies. During welding, hydrogen can be transferred to the weld pool from manifold sources (like contaminations, residuals at the surface, etc.). As hydrogen embrittles a material, the safety of welded components with hydrogen is always a critical issue. Weld heat input causes additional changes in the microstructure like grain growth or partial dissolution of precipitates and many more. All these things influence the mechanical properties and also represent hydrogen traps. These traps decrease the hydrogen diffusion compared to the ideal lattice. The result can be so-called delayed hydrogen assisted cracking (HAC) of the weld joint due to the significantly decreased diffusivity by trapped hydrogen. This is often an underestimated risk as those cracks can appear in the weld joint even after some days!
It is essential to know about hydrogen ingress during welding and the microstructure specific hydrogen diffusion. Both are depended on weld parameter influence and the chemical composition of the base material and weld metal. For that purpose, gas analytic methods like solid-state carrier gas hot extraction (CGHE) are useful tools to: (1) identify detrimental hydrogen concentrations from weld joints, (2) binding energies from hydrogen traps by thermal desorption analysis or (3) high-temperature diffusion coefficients. Those values are extremely important for welding practice in terms of recommendations on realistic hydrogen removal heat treatment (HRHT) after welding. Considering the increasing use of “digital” experiments, the data is also needed for reliable numerical simulations of HAC process or HRHT-effectiveness.
The present contribution gives an overview on the influence of hydrogen on weld joints, the necessity, methods and standards for hydrogen determination (CGHE) with the aim of fabrication of safe welded and crack-free components.
[1] R. A. Oriani (1987), Corrosion 43(7):390-397. doi: 10.5006/1.3583875
The development of hydrogen technologies is a key strategy to reduce greenhouse gas emission worldwide. Power-to-Gas is a challenging solution, in which hydrogen and methane can be used in mobility, industry, heat supply and electricity generation applications. This presentation deals with the tribological behaviour of polymer materials in hydrogen and methane, both in gas and in liquefied form.
Heute werden in Stahlkonstruktionen zunehmend hochfeste Baustähle (Streckgrenze ≥ 960 MPa) eingesetzt. Daher sind auch in Schweißnähten solche hohen Festigkeiten gefordert. Jedoch können hohe Eigenspannungen aufgrund geringerer plastischer Dehnungsreserven in diesen Schweißnähten die Sicherheit der Bauteile vermindern. Diese sind insbesondere im Zusammenhang mit Wasserstoff und Härtegefügen risskritisch. Niedrige Bauteilbeanspruchungen und Kosteneinsparungen lassen sich heutzutage mit modernen fokussierten Lichtbogenvarianten und engeren Nahtspalten erreichen. Die vorliegende Studie zeigt allerdings, dass diese modernen Schweißprozesse und die angepasste Nahtgeometrie höhere Wasserstoffkonzentrationen und signifikant gesteigerte oberflächennahe Zugeigenspannungsniveaus bedingen. Anhand mehrlagiger Schweißversuche an S960QL unter Variation von Wärmeführung, Lichtbogenvariante und Nahtöffnungswinkel wurden die Effekte und Wechselwirkungen unter Zuhilfenahme von Eigenspannungsanalytik mittels Röntgendiffraktometrie und Wasserstoffanalytik mittels Trägergasheißextraktion systematisch untersucht. Das Schweißgefüge führte unter kritischer mechanischer Beanspruchung und erhöhtem Gehalt an diffusiblem Wasserstoff insbesondere bei geringem Nahtöffnungswinkel und fokussiertem Lichtbogen zu einer deutlichen Ausbildung von Mikrorissen. Die Mikrorisse führten teils zu einer makroskopischen Ausprägung. Durch Analysen zur Nachwärmung aus der Schweißwärme heraus konnten suffiziente Wärmeführungsparameter für eine effektive Prävention solcher Risse erarbeitet werden. Die vorliegende Arbeit zeigt anhand des Interaktionssystems bei der wasserstoffunterstützten Kaltrissbildung Gefüge-Beanspruchung-Wasserstoff, welche Wärmeführungs- und Schweißparameter sich für die hochfesten Feinkornbaustähle zur Kaltrissvermeidung eignen.
Der Implant-Test nach ISO 17642-3 gehört zur Gruppe der fremdbeanspruchten Kaltrisstests, bei dem eine äußere Beanspruchung auf einen zylindrischen Stab (Implant-Probe) definiert aufgebracht wird. Mit dieser Kaltrissprüfung wurde vergleichende Analysen zur Kaltrissempfindlichkeit der modernen hochfesten Feinkornbaustähle S960MC und S960QL durchgeführt.
For metal-based additive manufacturing, sensors and measuring systems for monitoring of the energy source, the build volume, the melt pool and the component geometry are already commercially available. Further methods of optics, spectroscopy and non-destructive testing are described in the literature as suitable for in-situ application, but there are only a few reports on practical implementations.
Therefore, a new BAM project aims to develop process monitoring methods for the in-situ evaluation of the quality of additively manufactured metal components. In addition to passive and active thermography, this includes optical tomography, optical emission and absorption spectroscopy, eddy current testing, laminography, X-ray backscattering and photoacoustic methods. These methods are used in additive manufacturing systems for selective laser melting, laser metal deposition and wire arc additive manufacturing. To handle the sometimes huge amounts of data, algorithms for efficient preprocessing are developed and characteristics of the in-situ data are extracted and correlated to defects and inhomogeneities, which are determined using reference methods such as computer tomography and metallography. This process monitoring and fusion of data of different measurement techniques should result in a significant reduction of costly and time-consuming, destructive or non-destructive tests after the production of the component and at the same time reduce the production of scrap.
Here, first results of simultaneous measurements of optical emission spectroscopy and thermography during the laser metal deposition process using 316L as building material are presented. Temperature values are extracted from spectroscopic data by fitting of blackbody emission spectra to the experimental data and compared with results from a thermographic camera. Measurements with and without powder flow reveal significant differences between welding at a pristine metal surface and previously melted positions on the build plate, illustrating the significant influence of the partial oxidation of the surface during the first welding process on subsequent welding. The measurement equipment can either be mounted stationary or following the laser path. While first results were obtained in the stationary mode, future applications for online monitoring of the build of whole parts in the mobile mode are planned.