Filtern
Erscheinungsjahr
- 2019 (15) (entfernen)
Dokumenttyp
- Beitrag zu einem Tagungsband (15) (entfernen)
Referierte Publikation
- nein (15)
Schlagworte
- Corrosion (8)
- CO2 (3)
- Carbon steel (3)
- Steel (3)
- CCS (2)
- Geothermal (2)
- Utilization (2)
- Alkali-activated materials (1)
- CCU (1)
- CCUS (1)
Organisationseinheit der BAM
- 7.6 Korrosion und Korrosionsschutz (15) (entfernen)
Corrosion of steel reinforcement in concrete is one of the major deterioration mechanisms limiting the service life of reinforced concrete structures. While for conventional (Portland cement-based) concretes a great amount of experience exists in this regard, the factors that determine the onset of reinforcement corrosion in alkali-activated materials are incompletely understood yet. One aspect of corrosion protection is leaching and the accompanying changes of the concrete pore solution. In the present study, alkali-activated fly ash mortars with embedded carbon steel rebars were exposed to de-ionised water for periods up to 330 days, and the electrochemical response of the steel (free corrosion potential, polarisation resistance), the alteration of the mortar (ohmic resistance, mechanical strength, pore size distribution) as well as the pore solution composition were monitored. Although substantial alkali leaching was observed, the pH of the pore solution remained at values sufficient to protect the embedded steel from depassivation. The mortar did not exhibit indications of significant deterioration. Thus, the present results suggest that leaching is not critical for protection of steel reinforcement in alkali-activated fly ash mortars and concretes.
This contribution provides current findings regarding materials susceptibility for carbon capture, utilization and storage (CCUS) applications. Basing on results gathered in 2 German long-term projects (COORAL and CLUSTER) suitable materials are introduced as well as dominating impurities of the CO2-stream and corrosion mechanisms. Investigations cover the whole CCUS process chain and provide material recommendations for certain parts.
Geothermal energy is one of the most promising energy resources to replace fossil fuel. To extract this energy, hot fluids of various salts and gases are pumped up from a geothermal well having a certain depth and location. Geothermal wells in volcanic regions often contain highly corrosive CO2 and H2S gases that can be corrosive to the geothermal power-plants, which are commonly constructed of different steels, such as carbon steel. This research focuses on the corrosion behaviour of carbon steel exposed to an artificial geothermal fluid containing CO2 gas, using an artificial acidic-saline geothermal brine as found in Sibayak, Indonesia. This medium has a pH of 4 and a chloride content of 1,500 mg/L. Exposure tests were conducted for seven days at 70 °C and 150 °C to simulate the operating temperatures for low and medium enthalpy geothermal sources. Surface morphology and cross-section of the specimens from the above experiments were analysed using scanning electron microscope (SEM) and energy dispersive X-ray (EDX). Electrochemical tests via open circuit potential (OCP) and electrochemical impedance spectroscopy (EIS) were performed to understand the corrosion processes of carbon steel in CO2-containing solution both at 70 °C and 150 °C. Localized corrosion was observed to a greater extent at 70 °C due to the less protectiveness of corrosion product layer compared to that at 150 °C, where FeCO3 has a high corrosion resistance. However, a longer exposure test for 28 days revealed the occurrence of localized corrosion with deeper pits compared to the seven-day exposed carbon steel. In addition, corrosion product transformation was observed after 28 days, indicating that more Ca2+ cations incorporate into the FeCO3 structure.
Recent studies have shown that even at a very low concentration of impurities (less than 100 ppmv of SO2, NO2, O2 and H2O) the droplet formation and condensation of sulfuric and nitric acids in dense phase CO2 are possible and observable. To reveal the mechanism of droplet corrosion in dense phase CO2 at high pressure and low temperature, further studies on factors that affect wettability and resulting corrosion behaviors of transport pipeline steels are needed. In this study, effects of surface morphology were investigated by varying surface roughness of carbon steel coupons exposed to CO2 stream containing impurities to measure the wettability by contact angle and to observe the condensation as well as possible droplet corrosion that followed. Other considered factors were: pH of the droplet, temperature, droplet volume, and exposure time.
An important aspect with regard to the service life of zinc based galvanic anodes and the durability of the corrosion protection of steel in concrete is the “galvanic chloride extraction”. Chloride ions move in the electric field generated by the current, flowing between the galvanic anode and the cathodic steel. Migration leads to an accumulation of anions, e.g. chloride ions, at the anode and depletion of chlorides near the steel rebar surface. The ion migration was studied on steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied embedded zinc anode (EZA). The zinc anode was embedded and glued to the concrete surface by a geo-polymer based chloride free binder. The EZA was operated over a period of 1 year and the ion distribution between anode (EZA) and cathode (steel reinforcement) was studied by laser induced breakdown spectroscopy (LIBS) after 5 months, 7 months and 12 months. The results show that chloride ions efficiently migrate in the direction of the zinc-anode and accumulate there. Chloride distribution in the EZA correlates with the distribution of zinc ions generated by the anodic dissolution of the zinc anode in the binder matrix. The microstructure of the binder matrix and its interface to the zinc-anode are studied by REM/EDX – preliminary results will be reported.
Specific amounts of oxidizing and reductive impurities as well as some moisture were added to dense phase CO2 to replicate CO2 streams from sources in a CCS pipeline network. Due to the moisture content being only 50 ppmV no visible acid condensation took place. To simulate stress conditions at the inside pipeline surface due to fluid pressure (10 MPa) specimens were preloaded using a load frame. Experiments conducted at 278 K and at 313 K revealed the highest corrosion rate at lower temperature. Corrosive effect of impurities was strongest applying mixed atmosphere, containing oxidizing and reductive components, closely followed by CO2 streams with pure oxidizing character. By far, the lowest corrosion rate (10x lower) resulted from reductive atmosphere. In general, at constant temperature and pressure the CO2 stream composition strongly influences the morphology, thickness and composition of the corrosion products. Applying oxidizing or mixed impurities, iron hydroxides or oxides (e.g. goethite, hematite) occur as dominating corrosion products, capable to incorporate different amounts of sulfur. In contrast, using reductive atmosphere very thin corrosion layers with low crystallinity were developed, and phase identification by XRD was unfeasible. SEM/EDX analysis revealed the formation of Fe-O compounds, most likely attributed to the oxygen partial pressure in the system induced by CO2 (≥0.985 volume fraction) and volatile H2O. In addition to the surface covering corrosion layer, secondary phases had grown locally distributed on top of the layer. These compounds are characteristic for the applied atmosphere and vary in number, shape and chemical composition.
Investigation of the salinization in marine and offshore environment - test methods and challenges
(2019)
Salinization and contamination of metal surfaces by chloride-containing aerosols is of great importance with regard to corrosion phenomena in the maritime sector and in offshore applications. Especially Offshore Wind Turbines are exposed to extreme corrosive conditions due to high chloride concentrations in the atmosphere and the resulting high chloride deposition rates. It is of great importance to evaluate to what extent salinization of the surface influences the corrosion protection of coatings and pitting occurrence on stainless steels under atmospheric conditions to evaluate the durability of metallic building structures in offshore and marine environments. The evaluation of the scientific literature and regulatory guidelines has shown that there are still many open questions regarding the contamination of metal surfaces by chlorides. This contribution will discuss how salinization of metal surfaces is evaluated and monitored according to current standards and guidelines. Future challenges concerning test methods and the application of evaluated salinization values and deposition rates will be discussed.
Metallene Konstruktionswerkstoffe reagieren infolge ihres thermodynamisch instabilen Zustandes mehr oder weniger stark mit Stoffen aus der Umgebung. Eine große Rolle bei diesen Reaktionen spielt das Feuchtigkeitsangebot an der Metalloberfläche, welches nicht zwingend mit einem sichtbaren Wasserfilm einhergehen muss. An der Atmosphäre bilden sich an sauberen Metalloberflächen bei etwa 80 % relativer Luftfeuchte, bei versalzten Oberflächen auch schon ab etwa 25 % r. F., Feuchtfilme aus. Im Feuchtfilm laufen grundsätzlich die gleichen elektrochemischen Reaktionen ab, wie diese von wässrigen Medien bekannt sind. Dabei geht das Metall zunächst in Ionenform und in nachgelagerten Reaktionen in einen thermodynamisch stabilen Zustand in Form unterschiedlichster Oxid- und Hydroxidverbindungen über. Die so entstehenden Korrosionsprodukte können im Feuchtigkeitsfilm begrenzt löslich oder unlöslich sein und lagern sich auf den Oberflächen der Konstruktionswerkstoffe häufig als feste Korrosionsprodukte ab bzw. wachsen dort auf. Je nachdem wie die Korrosionsprodukte strukturell zum Untergrund passen, können sich dichte, sehr gut haftende Schichten ausbilden oder poröse, dicke Schichten ohne nennenswerte Haftung aufwachsen. Wachsen dichte, porenfreie Schichten mit guter Haftung auf, die im umgebenden Medium unlöslich sind, wird die weitere Auflösung des Metalls stark gehemmt. Man spricht dann von der Ausbildung schützender Deckschichten bzw. von Passivschichten auf welcher der Korrosionsschutz und damit die Dauerhaftigkeit vieler Konstruktionswerkstoffe beruhen. Kaesche bezeichnete die Passivität sehr treffend als „optimalen Grenzfall des Korrosionsschutzes durch Schichten von Korrosionsprodukten“. Aus technischer Sicht hält Kaesche eine Unterscheidung von Deckschichten bzw. Passivschichten für nicht zwingend erforderlich, da beide die Korrosionsgeschwindigkeit in gleichem Maß herabsetzen können. Die Übergänge zwischen den meist dickeren und dadurch sichtbaren Deckschichten und den meist dünnen, nicht sichtbaren Passivschichten sind fließend.
Ein neuer Ansatz bei elektrochemischen Korrosionsuntersuchungen kann durch den Einsatz von gelartigen Elektrolyten als Alternative zu wässrigen Prüfelektrolyten beschritten werden. Gelartige Elektrolyte ermöglichen minimalinvasive Untersuchungen an natürlich gebildeten Zinkdeckschichten. Dadurch können korrosionsrelevante Kennwerte ermittelt werden, die Aussagen zur Deckschichtbildung und zur Stabilität von atmosphärisch gebildeten Deckschichten erlauben. In diesem Beitrag wird anhand verschiedener Untersuchungen an Reinzink der Mehrwert von gelartigen Elektrolyten für die Korrosionsforschung und -prüfung verdeutlicht. Darüber hinaus werden neue Erkenntnisse zur Deckschichtbildung von Zink unter atmosphärischen Bedingungen vorgestellt.