Self-mated magnesia stabilized zirconia (Mg-PSZ) ceramic sliding couples have been investigated at 100 N load (P0max= 1324 MPa) in oscillating sliding conditions in different humidity conditions in air and in hot steam. Temperatures have been varied up to 400 °C and pressures up to 6 bars. The results show that the wear behavior of MgO-ZrO2 under high Hertzian contact pressures is strongly dependent on temperature and is similar for both dry oscillating and oscillating in hot steam. However, although the evolution in wear rates on temperature is similar and the wear rates of MgO-ZrO2 plunged above 300 °C in hot steam and air by nearly three orders of magnitude, SEM micrographs revealed in hot steam at 400 °C smooth wear tracks. In contrast, hot steam enhanced the tribochemistry of self-mated alumina couples and reduced wear rates. Hot steam decreased the coefficients of friction of MgO-ZrO2 with increasing temperature, but not the wear rates.
Self-mated magnesia stabilized zirconia (Mg-PSZ) ceramic sliding couples have been investigated at 100 N load (P0max= 1324 MPa) in oscillating sliding conditions in different humidity conditions in air and in hot steam. Temperatures have been varied up to 400 °C and pressures up to 6 bars. The results show that the wear behavior of MgO-ZrO2 under high Hertzian contact pressures is strongly dependent on temperature and is similar for both dry oscillating and oscillating in hot steam. However, although the evolution in wear rates on temperature is similar and the wear rates of MgO-ZrO2 plunged above 300 °C in hot steam and air by nearly three orders of magnitude, SEM micrographs revealed in hot steam at 400 °C smooth wear tracks. In contrast, hot steam enhanced the tribochemistry of self-mated alumina couples and reduced wear rates. Hot steam decreased the coefficients of friction of MgO-ZrO2 with increasing temperature, but not the wear rates.
The talk gives a historical introduction and introduces some of the biggest and most important research institutes in Germany dealing with tribology at Universities, scientific societies and companies. Some examples for research projects and focus areas are given. As an example for a research institute with a long history in tribological research the activities of BAM in Berlin are presented.
In this study the so-called laser-induced periodic surface structures (LIPSS, ripples) were produced on titanium alloy (Ti6Al4V) surfaces upon scan processing in air by a Ti:sapphire femtosecond (fs) laser. The tribological performance of the resulting surfaces was qualified in linear reciprocating sliding tribological tests (RSTT) against balls made of different materials (100Cr6 steel/Al2O3/Si3N4) using different oil-based lubricants. The admixture of the additive 2-ethylhexylzinc-dithiophosphate (ZDDP) to a base oil containing only anti-oxidants and temperature stabilizers disclosed the synergy of the additive with the laser-oxidized nanostructures. This interplay between the laser-textured sample topography and the local chemistry in the tribological contact area reduces friction and wear.