Filtern
Erscheinungsjahr
- 2022 (288) (entfernen)
Dokumenttyp
- Vortrag (155)
- Zeitschriftenartikel (77)
- Beitrag zu einem Tagungsband (41)
- Posterpräsentation (8)
- Buchkapitel (2)
- Sonstiges (2)
- Monografie (1)
- Dissertation (1)
- Forschungsbericht (1)
Sprache
- Englisch (191)
- Deutsch (95)
- Mehrsprachig (1)
- Spanisch (1)
Schlagworte
- Additive Fertigung (32)
- Additive manufacturing (26)
- Laser beam welding (24)
- Additive Manufacturing (15)
- Ultraschallunterstütztes Fräsen (14)
- Eigenspannungen (13)
- Hochfester Stahl (13)
- Ultrasonic-assisted milling (13)
- Alloy 36 (12)
- Surface integrity (12)
Organisationseinheit der BAM
- 9 Komponentensicherheit (288) (entfernen)
Paper des Monats
- ja (2)
Eingeladener Vortrag
- nein (155)
Um den Klimawandel wirksam zu bekämpfen, ist es entscheidend, fossile Brennstoffe durch erneuerbare Energiequellen wie Wind-, Solar- und Wasserkraft sowie alternative Energieträger, beispielsweise grünen Wasserstoff, zu ersetzen. Offshore-Windenergie spielt hierbei eine zentrale Rolle, da sie dank der Kombination aus globaler Verfügbarkeit, relativ geringen Betriebskosten und fortgeschrittenem technischen Entwicklungsstand besonders geeignet ist, zur regenerativen Stromerzeugung beizutragen. Sie ist zudem ein Schlüsselelement für die Umsetzung des Europäischen Green Deals, der das Ziel verfolgt, bis 2050 Klimaneutralität in der EU zu erreichen. Expertenschätzungen zufolge ist eine Steigerung der aktuellen Kapazität von 25 GW im Jahr 2020 auf etwa 450 GW notwendig, um diese ambitionierten Ziele zu erfüllen.
Bei der Entwicklung zukünftiger Offshore-Windparks, insbesondere in tieferen Gewässern, gewinnen Jacket-Gründungsstrukturen an Bedeutung. Diese Strukturen, die eine höhere Steifigkeit bei geringerem Materialeinsatz im Vergleich zu den bisher vorherrschenden Monopile-Gründungen bieten, basieren auf komplexen, räumlich aufgelösten Konstruktionen, die ähnlich den Öl- und Gasplattformen entwickelt werden. Die Herstellung der Jacketknoten, die bislang überwiegend manuell geschweißt wurden, birgt erhebliches Optimierungspotential. Durch Automatisierung und Digitalisierung der Fertigungsprozesse könnten nicht nur die Effizienz gesteigert, sondern auch die Qualität der Endprodukte durch präzise Überwachung und Kontrolle der Produktionsparameter verbessert werden. Diese technologischen Fortschritte sind für die Skalierung der Offshore-Windenergie und die Erreichung der Klimaziele von entscheidender Bedeutung.
Die Bestrebungen zur Verringerung der CO2-Emissionen erfordern hochbelastbare und effiziente Komponenten aus Stahl in der Anlagen-, Verfahrens- und Kraftwerkstechnik. Hierfür sind in zunehmendem Maße auf den Anwendungsfall und Stahlwerkstoff abgestimmte Verschleißschutzschich-ten und definierte, zerspante Oberflächen notwendig. Die hohen Härten dieser Schichten und der Einsatz konventioneller Co-basierter Verschleißwerkstoffe führen oftmals zu unwirtschaftlichen Bauteilen, gerade aufgrund hohen Werkzeugverschleißes bei der Zerspanung mit geometrisch bestimmter Schneide. Er-kenntnisse über den Einsatz Ni-basierter Verschleißwerkstoffe und die Optimierung der Zerspanbarkeit mittels Legierungsmodifikationen und moderner hybrider Fräsprozesse ohne Verschlechterung der Ver-schleißschutzeigenschaften sind deshalb für die Anwender und Verarbeiter zur wirtschaftlichen Fertigung hochbelasteter Stahlbauteile wesentlich. Der vorliegende Beitrag stellt die Untersuchungsmethodik eines aktuell laufenden Vorhabens der TU Clausthal und BAM, Berlin, vor. Fokus liegt hierbei auf den hochin-strumentierten Fräsexperimenten, die eine reproduzierbare Analyse und Korrelation zwischen den mik-rostrukturellen Eigenschaften der auftraggeschweißten Legierungen, dem Zerspanprozess und der Zer-spanbarkeit, insbesondere der resultierenden Oberflächenintegrität, ermöglichen sollen.
Die Wärmeverteilung des Lasers beim Laserstrahltiefschweißen ist für die Formgebung der Dampfkapillare und für die Schweißbaddynamik entscheidend. In dieser Arbeit werden die Laserwärmeverteilung und deren Einflüsse auf die Schweißbadtiefe sowie -breite numerisch anhand des Ray-Tracing-Verfahrens analysiert. Hierbei wird der La-serstrahl in mehreren Strahlenbündeln bzw. Subrays unterteilt. Diesbezüglich soll der Pfad der Subrays präzis berechnet werden, um die Dynamik der Dampfkapillare und des Schweißbades eines realen Schweißprozesses richtig abzubilden. Zu diesem Zweck beschäftigt sich die vorliegende Arbeit mit der Genauigkeitsverbesserung der Kontaktposition und der Reflexionsrichtung der Subrays auf der freien Oberfläche anhand der Level-Set-Methode. Um die Güte dieses Simulationsansatzes zu gewährleisten, wurde eine Gegenüberstellung mit den zwei klassi-schen Ray-Tracing-Verfahren mittels drei verschiedenen Benchmark-Testreihen durchgeführt. Anschließend wur-den die Versuchsergebnisse zur Validierung der implementierten numerischen Ansätze verwendet. Im Rahmen dieser Arbeit kann es gezeigt werden, dass unterschiedliche Wärmeverteilung aufgrund der verschiedenen Ray-Tracing-Verfahren deutlich zu erkennen ist, welche wiederum die Schweißbaddynamik sowie die lokalisierte Dampfkapillardynamik stark beeinflussen. Ferner wurde es bestätigt, dass die implementierte Level-Set-Methode zu einer genaueren Ermittlung der Kontaktposition und der Reflexionsrichtung der Subrays und somit zu einer Ver-besserung der simulierten Schmelzkontur führt.
Die Beschichtung hochfester Stahlfeinbleche beeinflusst das Auftreten von flüssigmetallinduzierter Rissbildung (LME). Daher wurden in dieser Arbeit industrieübliche Beschichtungen bei gleichem Grundwerkstoff hinsichtlich ihres Aufbaus und chemischer Zusammensetzung charakterisiert und bezüglich ihrer LME Anfälligkeit untersucht. Aus dieser vergleichenden Untersuchung heraus wurden Potentiale für die Widerstandsfähigkeit gegen LME identifiziert. Diese Potentiale werden experimentell durch den Einsatz einer von der Forschungsstelle entwickelten Methode überprüft. Gegenstand der Untersuchungen waren neben unbeschichteten Proben industrieübliche Zinküberzüge wie Elektrolytisch verzinkt, Feuerverzinkt, Galvannealed und Zink-Magnesium Beschichtungen.
Die LME Anfälligkeit dieser unterschiedlichen Überzüge wird mit einem Schweißen unter Zugbelastung Versuchsaufbau untersucht. Dabei ergibt sich die resultierende Anfälligkeit aus den auftretenden Risslängen und der Auftrittswahrscheinlichkeit von LME bei den einzelnen Versuchen. Es konnte eine LME Anfälligkeits-Rangfolge für die Zinküberzüge festgestellt werden. Zink-Magnesium Beschichtungen galten als besonders LME Anfällig, gefolgt von Feuerverzinkt und Galvannealed. Die größte LME Resistenz wurde bei elektrolytisch verzinkten Proben festgestellt.
Aus den Ergebnissen werden Handlungsempfehlungen zur Erhöhung der Verarbeitungssicherheit bzw. Schweißpunktqualität abgeleitet.
Hochfeste Nickelbasislegierungen wie Inconel 939 spielen eine wesentliche Rolle im modernen Turbinenbau. Additive Fertigungstechnologien eröffnen hierbei neue Möglichkeiten für die Verarbeitung, jedoch fehlen verlässliche Fügeprozesse für die Absicherung der additiven Prozesskette im Bereich Neuteilfertigung und Instandsetzung. Insbesondere Heißrisse stellen eine große Herausforderung an die Fügetechnik. Die vorliegende Untersuchung befasst sich daher mit dem Verhalten von additiv gefertigten Blechen aus Inconel 939 beim Elektronenstrahlschweißen. Es werden grundlegende Zusammenhänge zwischen Prozessparametern, Härte und Rissneigung betrachtet und Ansätze für eine Optimierung auf Basis statistischer Versuchsplanung aufgezeigt. Hierbei erfolgt eine Einteilung der Risse nach bestimmten Nahtbereichen. Risse am Nahtkopf können durch die Faktoren Vorschub und Streckenenergie sowie die Härte des Schweißgutes beeinflusst werden. Risse im Bereich der parallelen Nahtflanken stehen hingegen im Zusammenhang mit der Härte der Wärmeinflusszone. Ein abschließender Vergleich der angepassten Parameter mit der Ausgangssituation zeigt, dass durch Anwendung der statistischen Optimierung eine deutliche Reduzierung der Rissneigung erreicht werden kann.
Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The actual part qualification and certification procedures make use of spin-tests conducted on production-similar disks. The aim of this work is to present part of a fracture mechanics-based procedure under development which aims at replacing the tests on production-similar disks with lab tests on fracture mechanics specimens. The finite element simulation of the cracked disk considers the real thermal and mechanical loading conditions. In order to design a lab representative specimen, beside the crack driving force, expressed in terms of 𝐽-integral, also the constraint to plastic deformation e.g., stress triaxiality, at the crack-tip must be similar for the same crack in the specimen and in the disk. This has been achieved and as expected, both the highest 𝐽 -integral and constraint factor are calculated at the same location along the crack front for both disk and specimen. The results of the structural integrity assessment in the form of a Failure Assessment Diagram (FAD) show good agreement between designed specimen and disk both in terms of expected failure mode and value of the critical speed. In addition, probabilistic aspects are also considered in the calculations.
Elastomer seals are mounted as barrier seals in lid systems of containers designed for transport and disposal of negligible heat generating radioactive waste and as auxiliary seals in spent fuel storage and transportation casks (dual purpose casks (DPC)). When the behavior of mounted seals under normal and hypothetical accident conditions of disposal and transport is to be simulated, a comprehensive knowledge of their complex mechanical properties at every state of aging is necessary. In previous works, BAM’s efforts in experimental investigations on specimen artificially aged at different temperatures and times and the implementation of the found results in finite element material models were presented. Additionally, our approaches to reproduce the aging process itself and to extrapolate the results of artificially accelerated aging to longer times were presented. Numerical simulations have shown that the behavior of the seal during mounting and one-sided pressurizing and the resulting performance values such as leakage rate strongly depend on the coefficient of friction (COF) between flange and seal. The friction coefficient, in turn, depends on the aging state of the elastomer material as several publications suggest (see below).
Dynamic COF between an exemplary ethylene propylene diene rubber (EPDM) material and a stainless steel ball were determined by using a self-designed linear oscillation tribometer. Unaged and artificially aged EPDM specimen stored for 30 days and 100 days at a temperature of 150 °C were tested. A stainless steel ball (d=10 mm) is brought in contact with the specimen’s surface und loaded by normal forces of 2.5 N, 5 N, 10 N and 20 N. During a reciprocating movement of the EPDM sheet, the horizontal force/friction force is continuously measured, and the COF can be derived.
It is well known that friction is a complex phenomenon especially in soft materials. It cannot be excluded that the measured friction force is influenced by additional force components, resulting from the ball’s grooving through the elastomer’s surface. This force depends on the penetration depth of the ball and on the resistance of the elastomer in its different states of aging. The latter results from microstructural changes i.e., chain scission and additional crosslinking that occur during aging which in turn influence the softening or hardening of the material.
A finite element (FE) ABAQUS® model was developed to reproduce the measurement process. It should help to better understand the physical mechanisms and to quantify the percentage of measured forces resulting from real friction on the one hand and forces resulting from unintended side effects that could falsify the result on the other hand. The behavior of the elastomer in its different states of aging is reproduced by a FE material model already presented in previous works of BAM.
The concept behind this Research Topic (RT) was to collect works, in which Atomic Force Microscopy (AFM) techniques are employed to study tribological phenomena and to push the resolution of measurements towards single asperity contact. Thanks to the direct determination of sample height with sub-nanometer resolution and the possibility of measuring local friction, AFM can be employed after a tribotest to detect topography and friction changes at the nanometer scale. Recently, efforts are being expended to use AFM cantilevers as tribometers, i.e., as probes altering the volume of suitable samples, thereby measuring tip and/or sample wear and friction at the nano/microscale. Thus, single asperity contact, friction, and wear can be investigated. Since friction and wear at the macroscale are the result of asperities interactions, such experiments are of great importance for better understanding of tribological processes.
Elastomer seals are mounted as barrier seals in lid systems of containers designed for transport and disposal of negligible heat generating radioactive waste and as auxiliary seals in spent fuel storage and transportation casks (dual purpose casks (DPC)). When the behavior of mounted seals under normal and hypothetical accident conditions of disposal and transport is to be simulated, a comprehensive knowledge of their complex mechanical properties at every state of aging is necessary. In previous works, BAM’s efforts in experimental investigations on specimen artificially aged at different temperatures and times and the implementation of the found results in finite element material models were presented. Additionally, our approaches to reproduce the aging process itself and to extrapolate the results of artificially accelerated aging to longer times were presented. Numerical simulations have shown that the behavior of the seal during mounting and one-sided pressurizing and the resulting performance values such as leakage rate strongly depend on the coefficient of friction (COF) between flange and seal. The friction coefficient, in turn, depends on the aging state of the elastomer material as several publications suggest (see below).
Dynamic COF between an exemplary ethylene propylene diene rubber (EPDM) material and a stainless steel ball were determined by using a self-designed linear oscillation tribometer. Unaged and artificially aged EPDM specimen stored for 30 days and 100 days at a temperature of 150 °C were tested. A stainless steel ball (d=10 mm) is brought in contact with the specimen’s surface und loaded by normal forces of 2.5 N, 5 N, 10 N and 20 N. During a reciprocating movement of the EPDM sheet, the horizontal force/friction force is continuously measured, and the COF can be derived.
It is well known that friction is a complex phenomenon especially in soft materials. It cannot be excluded that the measured friction force is influenced by additional force components, resulting from the ball’s grooving through the elastomer’s surface. This force depends on the penetration depth of the ball and on the resistance of the elastomer in its different states of aging. The latter results from microstructural changes i.e., chain scission and additional crosslinking that occur during aging which in turn influence the softening or hardening of the material.
A finite element (FE) ABAQUS® model was developed to reproduce the measurement process. It should help to better understand the physical mechanisms and to quantify the percentage of measured forces resulting from real friction on the one hand and forces resulting from unintended side effects that could falsify the result on the other hand. The behavior of the elastomer in its different states of aging is reproduced by a FE material model already presented in previous works of BAM.