Thin poly(acrylic acid) PAA films were deposited by pulsed plasma polymerization on different organic and inorganic substrates. The structureproperty relationships of the deposited acrylic acid polymers were studied in dependence on the monomer pressure by various techniques and probes. The surface and bulk properties of the plasma deposited films were investigated by X-ray photoelectron spectroscopy, attenuated total reflection infrared, and broad band dielectric spectroscopy. The experimental infrared frequencies of PAA films are compared with those predicted from quantum mechanical calculation. The concentration of the COOH groups in the film (stored in ambient air) decreased by about 15 % compared to the as-prepared sample. The plasma deposited PAA probably form a highly branched product. However, the dielectric measurements show that in addition to the hydrogen bonds, self condensation process was able to hinder the localized fluctuation as well. These processes lead to form a cross-linked network polymer film. Nevertheless, a low energy is sufficient to break these processes during heating at atmospheric pressure. Therefore, homogenized samples with free branches (functional group) were obtained after a first heating with structures close to conventional polymerized acrylic acid. Thus, a thermally stable product was obtained.
Experiments according to a test specified in the UN Recommendations on the Transport of Dangerous Goods, Manual of Tests and Criteria, and numerical simulations by means of a finite element method are employed to determine the self-accelerating decomposition temperature of acrylic acid in a railroad tank car. The results demonstrate that the transport of acrylic acid in big tank cars is safe as long as some basic conditions are taken into account.
The peel strength of aluminium to polypropylene and poly(tetrafluoroethylene) was determined in dependence on the type and the concentration of functional groups on the polymer surface. For this purpose the polymer surface was equipped with monotype functional groups. The first method to produce monotype functionalized surfaces was an introduction of O functional groups using an oxygen plasma treatment and converting these groups to OH groups applying a wet chemical reduction. In result of this two-step treatment the hydroxyl group concentration at the polymer surface could be increased from 34 to 1014 OH groups/100 C atoms. The second method consists in the deposition of a 150 nm adhesion-promoting layer of plasmapolymers or copolymers onto the polymer surface using the pulsed plasma technique. For that purpose functional groups carrying monomers as allyl alcohol, allylamine and acrylic acid were used. Applying the plasma-initiated copolymerization and using neutral monomers like ethylene or butadiene the concentration of the functional groups was varied.
A correlation of peel strength with the ability of forming chemical interactions between Al atoms and functional groups was found: COOH > OH >> NH2 > H(CH2CH2).