Corrosion of metallic engineering materials accounts for problems during geothermal operation in the Upper Rhine Graben (URG). Herein, we study the electrochemical behaviour of various metal alloys in an 80 °C simulated geothermal environment by using potentiodynamic polarisation and open-circuit potential measurements. Two different natural geothermal waters from URG geothermal sites were used for the experiments. The measurements reveal spontaneous passivation to be a key process for all alloys. This ennoblement protects more noble alloys from significant corrosion (e.g. titanium gr. 2, alloy 625) and brings less noble alloys to failure, mostly due to pitting corrosion (e.g. 316L).
Electrochemical noise measurements on anodically polarised type 304 stainless steel surfaces in contact with buffer solutions of neutral pH were performed to study the effect of chloride ions in the nucleation of pitting corrosion. Passive layer stability and susceptibility to pitting corrosion after pickling and passivation at different environmental conditions were also investigated by means of electrochemical current noise measurements under cathodic and anodic polarisation. According to the obtained experimental results pits nucleate independently on the presence of chloride ions. It has been also shown that protectiveness of stainless steel surfaces after pickling strongly depends on the relative humidity of the environment in which the surface is subsequently passivated.