During aluminium extrusion, the die experience cyclic thermo-mechanical loads that can lead to materials degradation and failure. For a process optimization and a comparison of different hot work tool steels, the finite element method is an appropriate means. Local inelastic strains result from the interaction of the applied temperature and stress loading and can be computed by suitable inelastic constitutive equations. Stress amplitudes and dwell times during extrusion result in creep-fatigue damage. A lifetime consumption model sums increments of a damage variable over time and defines materials failure as the accumulation of the resulting damage variable to a critical value. The procedure for the identification of the material parameters for both the constitutive and the damage model is described in detail, including the material parameters for the description of time-effects, and applied to the hot work tool steel Böhler W300 ISOBLOC (EN 1.2343). The lifetime consumption for two different hot work tool steels is compared on the basis of an example in aluminium extrusion.
During hot extrusion of aluminium alloys, extrusion dies experience cyclic temperature changes as well as multiaxial loadings. To improve the service life of the dies, cleaner and high hot strength materials are designed as well as an optimised process control is performed. For the improvement of the process guiding and a comparison of lifetime behaviour of different hot work tool steels, modelling and simulation are appropriate means. The extrusion process has been simulated using the FE-program Deform to find the stress and temperature history at the inner diameter of the liner, i.e. the boundary conditions for the subsequent cyclic simulation of the container during service. Inelastic constitutive equations have been implemented into Abaqus Standard to describe strain hardening and time recovery effects. They include the Norton viscoplastic flow rule, thermo-mechanical isotropic hardening and two non-linear kinematic hardening laws. A damage-rate model predicts failure and thus the lifetime of the container. The procedure for the identification of material parameters for both the constitutive and the damage model is described in detail for the hot work tool steel Böhler W400 VMR (EN 1.2343).