New fluorinated coordination polymers were prepared mechanochemically by milling the alkaline earth metal hydroxides MII(OH)2·xH2O (MII: Ca, Sr) with tetrafluoroisophthalic acid (H2mBDC-F4). The structures of [{Ca(mBDC-F4)(H2O)2}·H2O] and [{Sr(mBDC-F4)(H2O)2}·H2O] were determined based on ab initio calculations and their powder X-ray diffraction (PXRD) data. The compounds are isomorphous and crystallize in the orthorhombic space group P212121. The determined structures were validated by using extended X-ray absorption (EXAFS) data. The new materials were thoroughly characterized using elemental analysis, thermal analysis, magic angle spinning NMR, and attenuated total reflection-infrared spectroscopy. Further characterization methods such as BET, dynamic vapor sorption, and scanning electron microscopy imaging were also used. Our investigations indicate that mechanochemistry is an efficient method for preparing such materials.
This paper reports the first successful synthesis and the structural characterization of nanocrystalline and stacking-disordered β-cristobalite AlPO4 that is chemically stabilized down to room temperature and free of crystalline impurity phases. Several batches of the title compound were synthesized and thoroughly characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy, selected area electron diffraction, energy dispersive X-ray spectroscopy mapping in SEM, solid-state 31P nuclear magnetic resonance (31P-NMR) spectroscopy including the TRAPDOR method, differential thermal analysis (DTA), gas-sorption methods, optical Emission spectroscopy, X-ray fluorescence spectroscopy, and ion chromatography. Parameters that are critical for the synthesis were identified and optimized. The synthesis procedure yields reproducible results and is well documented. A high-quality XRD pattern of the title compound is presented, which was collected with monochromatic copper radiation at room temperature in a wide 2θ range of 5°–100°.
The structural properties of a borosilicate glass with nominal 16 mol% Na2O, 10 mol% B2O3 and 74mol% SiO2 and water contents between 0 and 8wt% H2O (0–22 mol% H2O)were investigated with IR, Raman and 11BMAS NMR spectroscopy. In addition to the pronounced OH stretching vibration band of weakly H-bonded species at 3580 cm−1 the MIR spectra show a triplet at 2900, 2350 and 1750 cm−1, similar as observed in water-bearing silicate glasses. These bands are assigned to OH groups and water molecules which are strongly H-bonded, to non-bridging oxygen. Water species contents determined from absorption bands in the NIR at 5200 cm−1 (molecular H2O), 4700 cm−1 (B\\OH), and 4500 cm−1 (Si\\OH) indicate that hydroxyl groups dominate up to ~6 wt% total H2O. Based on the absorption coefficients known from literature for silicate and borate glasses the B\\OH/Si\\OH ratio is estimated to be ≈0.8.
As indicated by density, Raman and NMR data the incorporation ofwater has strong structural impacts in particular at low water contents up to 3 wt% H2O. While the nominally dry glasses still contain a significant fraction (12%) of three-fold coordinated boron, almost all boron is four-fold coordinated in hydrous glasses. The increase of band components in the Raman spectra near 900 cm−1 relative to the region N 1050 cm−1 gives evidence for depolymerization of the network upon hydration. Fitting of the spectra with Gaussians implies that silica tetrahedra with two non-bridging oxygen (Q2) are preferentially formed by reactionwithwater on expense of tetrahedra linked to four tetrahedra (Q4).