Aluminium diethylphosphinate (AlPi-Et) and inorganic aluminium phosphinate with resorcinol-bis(di-2,6-xylyl phosphate) (AlPi-H+RXP) were compared with each other as commercially available halogen-free flame retardants in poly(butylene terephthalate) (PBT) as well as in glass-fibre-reinforced PBT (PBT/GF). Pyrolysis behaviour and flame retardancy performance are reported in detail. AlPi-H+RXP released phosphine at very low temperatures, which can become a problem during processing. AlPi-Et provided better limiting oxygen index (LOI) values and UL 94 ratings for bulk and PBT/GF than AlPi-H+RXP. Both flame retardants acted via three different flame-retardancy mechanisms in bulk as well as in PBT/GF, namely, flame inhibition, increased amount of char, and a protection effect of the char. AlPi-Et was more efficient in decreasing the total heat evolved of PBT in the cone calorimeter test. AlPi-H+RXP reduced the peak heat release rate of PBT more efficiently than AlPi-Et. An optimum loading of AlPi-Et in PBT/GF was found, which was below the supplier's recommendation. This loading provides a maximum increase in LOI and a maximum decrease in total heat evolved.
PET-P-DOPO is a phosphorus-containing polyester prepared from the glycol ether of the hydroquinone derivative of 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) and dimethyl terephthalate. PET-P-DOPO and a blend of PBT with PET-PDOPO were investigated with respect to pyrolysis and fire behavior. PET-P-DOPO achieves a V-0 rating in the UL 94 test and exhibits a high LOI of 39.3%. The outstanding flame-retardant properties of PET-P-DOPO are the result of three different mechanisms (flame inhibition, charring and a protection effect of the intumescent char) that are active in PET-P-DOPO. The fire load and the peak of heat release rate (pHRR) are reduced to 34% and 17%, respectively. The char exhibits an intumescent multicellular structure enabling it to act as an efficient protection layer. As PET-P-DOPO is immiscible with PBT, the blend shows a lower breaking elongation than pure PBT. Compared to pure PET-P-DOPO, the flame retardancy of the blend is decreased according to the fraction of PET-P-DOPO used. Nevertheless, the flame-retardancy of PET-P-DOPO in the blend was good enough to compete with PBT flame-retarded by AlPi-Et (aluminum diethylphosphinate) that was used as a Benchmark.