Fatigue life evaluation of spar cap materials by four point bending test on width-tapered specimens
(2015)
The presented research project focuses on an effective method to evaluate the fatigue strength of thick unidirectional laminates to be applied in spar caps. Therefore, a width-tapered bending specimen was developed for a four point loading set up. Static and fatigue loading was performed with the load ratio of R=-1. The complex stress state was investigated numerically with a finite element analysis. Finally, the concept was proven experimentally on specimens made of pultruded fibre rods. The fatigue behaviour of continuous tapered width by water jet cutting was compared to discrete tapering by rod-drop.
Carbon Fibre Reinforced Plastics (CFRP) are more and more used in modern civil aircrafts. These days the whole fuselage is made of this material (B787; A350). Due to strict certification standards the normal in-service loading gives a low stress level compared to the static and even the fatigue strength of the material. Hence CFRP are assumed to have an infinite life. To evaluate this assumption, fatigue tests on CFRP-specimens were performed up to 108 load cycles and the first inter-fibre failure was evaluated non-destructively by accompanying X-ray-refraction topography.
A tensile testing machine was integrated in a small angle X-ray scattering (SAXS) setup. X-ray refraction topography was performed while the CFRP-samples were tensile loaded. This non-destructive technique enables the detection of micro-cracking and inter-fibre failure especially for CFRP. For Glass Fibre Reinforced Plastic (GFRP) X-ray refraction and in-situ loading has already been successfully used. The increase of inner surfaces due to inter fibre failure was measured as a function of the stress state. Fatigue tests were performed at and below the limit of inter-fibre failure strength.
State of the art is to assume the failure of the samples under cyclic loading as the fatigue life. Accompanying non-destructive X-ray refraction measurements reflects the damage state and enables to trace its evolution even if the total failure of the specimens does not occur. This investigation technique is of high interest to give the engineer a design value of infinite life which is practically often reached due to knock down factors of certification standards. Finally the infinite life was found for cyclic fatigue loaded CFRP-samples even under high inter fibre transverse and shear loading investigated up to 108 load cycles.
Nondestructive investigation of the VHCF-endurance on cyclically loaded CFRP by X-Ray-Refractography
(2016)
Carbon fiber-reinforced-plastics (CFRP) are already used under high-cycle- (HCF) and very-high-cycle-fatigue (VHCF) at relatively low loads not only in aerospace industry, but also in other growing markets like especially wind energy and increasingly also automotive industry. While the static strength of CFRP is satisfyingly predictable by means of layerwise-strenght-analysis and material data from single layers, it is more and more uncertain to predict residual strength or lifetime as the design lifetime increases. Previous studies showed that local minor cracks and inter-fiber-fracture (IFF) originate long before total failure of single layers. Reliable fatigue estimation for fiber-reinforced-plastics is not available at present. Subsequently safety-related primary structures made out of FRP are over dimensioned.
It is possible to detect the change of inner surface in a specimen by means of X-Ray-Refractography. This includes voids, intact fiber-matrix-interfaces as well as defective ones, cracks and all interfaces in plane with the X-Ray-beam. As the crack-density (including IFF) increases, the inner surface of the material correspondingly increases.
The borderline where even at high cycles no early cracks were detected was identified for selected laminates out of woven and non-crimped fabric with epoxy-matrix.
When no micro-cracks were detected up to 106 cycles, the specimens also lasted in the VHCF-regime. Furthermore for the epoxy resin LY556 in combination with carbon fiber it was distinguished that at a load minor to 50% IFF-load level, no micro cracks were detected and consequently the VHCF-endurance reached.
The integration of the set-up small-sized testing machine into the X-Ray buildup in order to achieve in-situ non-destructive detection of the crack initiation while loading the specimens (CFRP and GFRP- woven fabric and non-crimped-fabric) at the same time will increase the performance of the studies.
In earlier investigations at BAM it was shown, that the matrix has a strong influence on the micro-crack formation and finally on the total lifetime. In order to determine the influence of the matrix properties on the boarderline to infinite life, research is done on laminates while replacing the epoxy-based matrix with an equivalent one with different fracture mechanical properties.
With the evolution of early cracks and IFF monitored as well as the influence of the matrix on the crack propagation investigated we are working on an appropriate model to improve lifetime prediction in CFRP. This work is done within the priority program “infinite life” (SPP 1466) funded by Deutsche Forschungsgemeinschaft (DFG).
Nondestructive investigation of the VHCF-endurance on cyclically loaded CFRP by X-Ray-Refractography
(2016)
Carbon fiber-reinforced-plastics (CFRP) are already used under high-cycle- (HCF) and very-high-cycle-fatigue (VHCF) at relatively low loads not only in aerospace industry, but also in other growing markets like especially wind energy and increasingly also automotive industry. While the static strength of CFRP is satisfyingly predictable by means of layerwise-strenght-analysis and material data from single layers, it is more and more uncertain to predict residual strength or lifetime as the design lifetime increases. Previous studies showed that local minor cracks and inter-fiber-fracture (IFF) originate long before total failure of single layers. Reliable fatigue estimation for fiber-reinforced-plastics is not available at present. Subsequently safety-related primary structures made out of FRP are over dimensioned.
It is possible to detect the change of inner surface in a specimen by means of X-Ray-Refractography. This includes voids, intact fiber-matrix-interfaces as well as defective ones, cracks and all interfaces in plane with the X-Ray-beam. As the crack-density (including IFF) increases, the inner surface of the material correspondingly increases.
The borderline where even at high cycles no early cracks were detected was identified for selected laminates out of woven and non-crimped fabric with epoxy-matrix.
When no micro-cracks were detected up to 106 cycles, the specimens also lasted in the VHCF-regime. Furthermore for the epoxy resin LY556 in combination with carbon fiber it was distinguished that at a load minor to 50% IFF-load level, no micro cracks were detected and consequently the VHCF-endurance reached.
The integration of the set-up small-sized testing machine into the X-Ray buildup in order to achieve in-situ non-destructive detection of the crack initiation while loading the specimens (CFRP and GFRP- woven fabric and non-crimped-fabric) at the same time will increase the performance of the studies.
In earlier investigations at BAM it was shown, that the matrix has a strong influence on the micro-crack formation and finally on the total lifetime. In order to determine the influence of the matrix properties on the boarderline to infinite life, research is done on laminates while replacing the epoxy-based matrix with an equivalent one with different fracture mechanical properties.
With the evolution of early cracks and IFF monitored as well as the influence of the matrix on the crack propagation investigated we are working on an appropriate model to improve lifetime prediction in CFRP. This work is done within the priority program “infinite life” (SPP 1466) funded by Deutsche Forschungsgemeinschaft (DFG).
Faser-Kunststoff Verbunde und insbesondere Kohlenstofffaserverstärkte Kunststoffe werden bereits im Bereich der hohen (HCF) und sehr hohen Lastspielzahlen (VHCF) eingesetzt. Während statische Festigkeiten für diese Materialien bereits gut vorhersagbar sind, gibt es noch keine verlässliche Methode Schwingfestigkeiten zu bestimmen.
Vergangene Studien an Faser-Kunststoff Verbunden an der BAM zeigten, dass bei Schwingbelastung Mikrorisse und Zwischenfaserrisse bereits weit vor dem finalen Versagen auftreten. Diese Schäden erhöhen die innere Oberfläche des Materials. Die Änderung der inneren Oberfläche kann mittels der Röntgenrefraktion bestimmt werden.
Damit konnte im Rahmen der aktuellen Arbeit eine Lastgrenze ermittelt werden, bei der im untersuchten Lastwechselbereich keine Mikrorisse auftreten. Unter den gegebenen Material- und Versuchsparametern kann damit von einer ermittelten Dauerfestigkeitsgrenze gesprochen werden.
Within the scope of a DIN INS project, a flash thermography round robin test that evaluates reliability, comparability, and efficiency of different testing situations was organized. The results give information about the detectability of defects, e.g. depending on their size and depth, the evaluation methods and the materials used. Besides, the influences of equipment and parameters used by the participants on the results were analysed. All of the quantitative results as well as the feedback given by the participants will be presented in a DIN committee in order to contribute to a flash thermography standard.
Amongst various other NDT methods, within the EMRP-project ‘VITCEA’ active thermography is validated for testing of CFRP and GFRP structures constructed for energy application. In this contribution, the optical and thermal properties of CFRP and GFRP reference defect artefact (RDA) and natural defects artefact (NDA) test specimens are characterized. Different excitation techniques and techniques for data analysis are compared for optimizing the number of detected defects.
The increased use of fibre-reinforced plastic (FRP) composites for improved efficiency and reliability in energy related applications e.g. wind and marine turbine blades, nacelles, oil and gas flexible risers, also increases the demand for innovative non-destructive testing technologies. Thus, in order to achieve increased acceptance of suited and optimized non-destructive testing (NDT) methods in industry, the European Metrology Research Programme (EMRP) project ENG57 Validated Inspection Techniques for Composites in Energy Applications (VITCEA) deals with the development and validation of innovative NDT technologies. In this contribution, results concerning thermographic investigations at test specimens during tensile loading and active thermography testing after tensile loading are presented. Additionally, the determination of the optical properties (relative transmittance and directional spectral emissivity) of CFRP and GFRP test specimens is described.
An internal project at BAM (Bundesanstalt für Materialforschung und -prüfung) pursue the goal to develop methods and models to investigate ageing of CFRP (carbon fiber reinforced plastic) composites pressure vessels. One main challenge is the application of appropriate testing methods for detecting the influences of pressure cycles and creep behavior on the material. This contribution presents results we achieved using conventional eddy current testing (ET) and high frequency ET. Before investigating pressure vessels, we studied test samples with artifcial defects. Here, we could show that also conventional ET with low frequencies are useable for CFRP samples which have at bottom holes of different size and depth. On the basis of the received results we deployed conventional ET besides high-frequency applications in order to investigate pressure vessels of different material combinations like steel-CFRP,
Aluminum-CFRP and synthetics-CFRP. The thickness of the CFRP varies from 4 mm up to 8 mm. Here, we could detect both defects in the metal liner and in the CFRP.
Da kohlenstofffaserverstärkte Kunststoffe (CFK) in anspruchsvollen sicherheitsrelevanten Einsatzgebieten wie im Automobilbau und in der Luftfahrt eingesetzt werden, besteht ein zunehmender Bedarf an zerstörungsfreien Prüfmethoden. Ziel ist die Gewährleistung der Sicherheit und Zuverlässigkeit der eingesetzten Bauteile. Aktive Thermografieverfahren ermöglichen die effiziente Prüfung großer Flächen mit hoher Auflösung in wenigen Arbeitsschritten. Ein wichtiges Teilgebiet der Prüfungen ist die Ortung und Charakterisierung von Delaminationen, die sowohl bereits in der Fertigung als auch während der Nutzung eines Bauteils auftreten können, und dessen strukturelle Integrität schwächen.
In diesem Beitrag werden CFK-Strukturen mit künstlichen und natürlichen Delaminationen mit Hilfe unterschiedlich zeitlich modulierter Strahlungsquellen experimentell untersucht. Verwendet werden dabei Anregungen mit Blitzlampen und mit frequenzmodulierten Halogenlampen. Mittels Filterfunktionen im Zeit- und Frequenzbereich wird das Kontrast-zu-Rausch-Verhältnis (CNR) der detektierten Fehlstellen optimiert. Verglichen werden anschließend die Nachweisempfindlichkeit, das CNR und die Ortsauflösung der zu charakterisierenden Delaminationen für die unterschiedlichen Anregungs- und Auswertungstechniken. Ergänzt werden die Experimente durch numerische Simulationen des dreidimensionalen Wärmetransportes.