By the combination of an optimized granulometry, a reduced water cement ratio and the use of superplasticizers ultra-high performance concrete achieves a compressive strength of over 150 N/mm2 and a high resistance regarding acids and water-soluble salts. In different Research projects the effect of an autoclavation on the mechanical strength and the phase composition was analyzed. In systematic studies, the concrete mix and the process parameters were varied.
The results show that autoclavation leads to an improved pozzolanic and hydraulic reaction and significantly improves the mechanical strength compared to a conventional thermal treatment. If a minimum time-span for hydration is ensured, the achievable strength level is not dependent on the prestorage time. However, the duration of the autoclaving is significant. After the Maximum strength is reached there is only a very slight decrease, even if unrealistically long autoclaving times are applied.
Ultra high performance concrete (UHPC) is characterised by its high compressive strength of more than 150 MPa and its high durability. Due to thermal treatment at 90°C a strength comparable to the 28-days-strength can be achieved immediately after the treatment and in some cases can be even further increased up to 30 %. The explanations for the increase in strength are the accelerated hydration of the clinker minerals and the intensified pozzolanic reaction contributing to a denser microstructure and hence, a high performance in compressive strength.
Former research shows that thermal treatment can lead to inhomogeneities in form of a visible zonation within the cross-section. The width of the margin increases with shorter pre-storage time before the thermal treatment and with omitting protective measures against desiccation during the treatment. Specimens exhibiting a zonation typically show a lower compressive strength compared to the undisturbed reference whereas changes in chemistry, mineral content and microstructure were not reported in detail.
In this study the zonation of thermally treated UHPC is investigated with respect to its chemistry, mineral composition and microstructure to allow predictions on durability and strength development. Measurements show a change in pore sizes, minerals phase composition and element distribution leading to the visible zonation and weaker bending tensile strength compared to the reference.