Covalent modification of surfaces with carbohydrates (glycans) is a prerequisite for a variety of glycomics-based biomedical applications, including functional biomaterials, glycan-arrays, and glycan-based biosensors. The chemistry of glycan immobilization plays an essential role in the bioavailability and function of surface bound carbohydrate moieties. For biomedical applications the stability over time (shelf life) of a glycan-array is a crucial factor. Basic requirements for the production of microarrays are first of all stable signals without any loss of quality. Therefore, the investigation of the shelf life for carbohydrate microarrays is an important part in the development of glycan-arrays.
Motivated by the need of reliable quality control for glycan microarrays, we developed reference arrays using fluorescent model glycans. Since the long term stability of glycan microarrays is a crucial factor for their clinical application the shelf life at different storage conditions of glycan microarrays was studied in detail using the two model glycan compounds.
Herein, we present a shelf life study of model glycan microarrays on epoxy modified glass surfaces over a period of 320 days. This was carried out using different analyzing techniques such as Time-of-Flight Secondary Ion Mass Spectrometry (ToF-SIMS), X-ray Photoelectron Spectroscopy (XPS) and Fluorescence Spectroscopy. To analyze and interpret the ToF-SIMS dataset the multivariate technique principal component analysis (PCA) was used. The dependence of the array´s shelf life upon storage conditions was specifically studied.
Aiming at the development of a non-destructive optical measurement methods for the characterization of nano-sized airborne particulate pollutants we performed fluorescence spectroscopic investigations of their relevant emission properties. Here, we present first results from studies of soot particles from synthetic aerosols deposited on PTFE membranes.
Substitution of lead oxide in low-melting glasses, e.g., for application in silver metallization pastes, is a current research goal. This work is focused on the investigation of silver diffusion in alkali zinc borate glasses (X2O-ZnO-B2O3, X = Li, Na, K, Rb). In addition, the redox state of silver (Ag) and thus the type of diffusing silver species were studied. For this purpose, a metallic silver coating was applied on glass cubes by means of sputtering. Heat treatment of the samples was performed close to the glass transition temperatures at 470 °C for 2 h under air and nitrogen atmosphere. Coating thickness was 1.8 µm after heat treatment, measured by a white light interferometer.
Silver diffusion profiles were measured by means of secondary neutral mass spectrometry. The silver diffusion coefficients are in the range of ~10-14 cm2/s and indicate no significant differences depending on the type of alkali ions in the glass. Dissolved Ag+-ions and [Agm]n+-clusters in the glasses were differentiated using fluorescence spectroscopy.
Precipitated metallic silver particles in the sodium containing glass were observed by means of transmission electron microcopy. Their mean particle diameter was ~6 nm.