Intermediate-scale testing is indispensable when investigating the fire resistance under simultaneous compressive load of components made of glass- and carbon-fibre-reinforced composites (GFRP and CFRP). BAM is successfully operating an intermediate-scale test stand, developed for a specimen size of 500 mm x 500 mm (1000 mm). The fire resistance in terms of fire stability of CFRP and GFRP sandwiches are investigated, e.g. at 20 % of their compressive failure load at room temperature. Times to failure increase by up to a factor of 4 due to intumescent coatings. For GFRP sandwiches, different core structures with and without additional flame retardants show an astonishing impact on time to failure. CFRP shell structures are investigated on the intermediate scale with and without stringer reinforcements, resulting in completely different mechanical failure behaviour in the ultimate load test as opposed to the fire resistance test. The stringers become the only load-carrying part, while the shell acts as a protective layer. Thus the design exploiting this self-protection potential, i.e. the residue of the front skin protecting the load-bearing structure, is highlighted as a most promising route to enhance the fire resistance of lightweight materials.
Carbon fibre (CF) and glass fibre (GF) reinforced polymers are used for diverse applications such as electronics/electrical engineering, transportation (railway vehicles, shipping, aviation) and construction. The fire behaviour of composites differs in comparison to polymers. Fibres behave often inert with respect to pyrolysis, but they change the melt flow and dripping behaviour, the heat absorption and transfer, the amount and properties of the fire residue and so on. Flame and fire retardancy concepts are needed not only suitable for the different fire protection goals typical for each application, but also tailored for composites. The field is illuminated by examples taken from different projects carried out in the group of the author in the recent years. The examples target on different applications through achieving V0 in UL 94 testing (reaction to small flame controlling the fire risks in the beginning of a fire), reducing heat release rate and fire load in the cone calorimeter (fire risks under forced flaming combusting controlling the contribution to developing fires) and investigating the fire stability when a severe flame is directly applied (key property in fully developed fires). Approaches to halogen-free flame retardancy in GF reinforced thermoplastics and CF reinforced thermosets are presented as well as building up a bench and intermediate scale testing of composites in fire applying mechanical load and direct flame exposure simultaneously.
The understanding of fire behaviour and flame retardancy mode of actions in composites is a promising basis for target-oriented development. The role of flame inhibition, charring and protective layer formation is discussed in composites. Successful concepts are presented for flame retardancy tailored for different application as well as general guidelines for future development. Different phosphorus flame retardants are proposed to achieve halogen-free flame retardancy in applications demanding limited fire risks with respect to ignition and developing fires. Different protective approaches are sketched for addressing the fire resistance of composite that is the most important fire risk for structural applications.
Deckensysteme aus Spannbeton-Hohlplatten (engl.: Hollow Core Slabs, HC-Platten) werden im Hochbau insbesondere aus wirtschaftlichen Gründen eingesetzt. Vorteile gegenüber Massivdecken in Ortbetonweise ergeben sich insbesondere aus dem hohen Vorfertigungsgrad, geringem Eigengewicht und der Möglichkeit großer Spannweiten bei relativ niedrigen Querschnitten. Bei einem 2007 aufgetretenen Brandereignis in einem Parkhaus in Rotterdam kam es infolge Horizontalrissbildung in den Plattenstegen zu einer teilweisen Ablösung des unteren Plattenspiegels. Dies hatte eine europaweite Diskussion zur brandschutztechnischen Bewertung dieser Bauart zur Folge. Mittlerweile liegen gutachterliche Stellungnahmen, Literaturauswertungen und auch jüngere Forschungsarbeiten zum Feuerwiderstand von Konstruktionen aus Spannbeton-Hohlplatten vor. In den Untersuchungen wurde unter anderem das Tragverhalten von HC-Platten bei starrer Auflagerung, insbesondere hinsichtlich der Querkrafttragfähigkeit, untersucht.
Ein bei der Prüfung und Bewertung von Spannbeton-Hohlplatten bisher kaum beachteter Aspekt ist die im Brandfall auftretende Behinderung der Querdehnung infolge umgebender Bauteile oder Tragwerksteile. Im Bauwerk kann für HC-Platten eine Querdehnungsbehinderung im Brandfall auftreten, wenn eine steife Begrenzung des brandbeanspruchten Deckenbereiches vorliegt, z.B. durch Treppenhauskerne oder auch durch umgebende Decken-felder bei lokaler Brandbeanspruchung. Ferner legten Versuchsergebnisse nahe, dass eine Aufbetonschicht die Zwängungen in der HC-Platte verstärkt. Die Problematik der Querdehnungsbehinderung im Brandfall wurde auch in Gremien der Bauaufsicht sowie im zuständigen Sachverständigenausschuss des Deutschen Instituts für Bautechnik (SVA 463 Tragwerksbemessung für Brandeinwirkung) erörtert. Dabei wurde anhand vorgelegter Studien und numerischer Voruntersuchungen deutlich, dass die Bildung von Horizontalrissen in den Plattenstegen auch bei HC-Platten ohne Aufbeton auftreten kann.
Um den Einfluss der Querdehnungsbehinderung zu klären wurden an der BAM entsprechende experimentelle und numerische Untersuchungen an Decken-feldern aus Spannbeton-Hohlplatten mit unterschiedlichem Grad der seitlichen Zwängung durchgeführt. Im Beitrag werden die im Realmaßstab durch-geführten Brandversuche beschrieben und deren Ergebnisse und daraus abgeleiteten Erkenntnisse vorgestellt.
Intumescent coatings are used for decades to increase the fire resistance of steel or wood constructions. Intermediate and full scale tests are used to assess their protection performance. For the product development and screening, cheaper and faster bench-scale tests are demanded that provide information about thermal protection, foaming dynamics and mechanical resistance. In the recent years, we have developed several bench-scale fire resistance tests and used them in different research and developing projects. The influence of distinct binders and fillers, respectively, was studied in intumescent coatings using the Standard Time Temperature modified muffle furnace (STT Mufu+). This bench-scale test evaluates the fire resistance (by means of temperature measurements) and the foaming behaviour (by means of a high-temperature endoscope) during a standard time-temperature exposure. The fire residues were suitable for advance residue analysing techniques like nondestructive μ-computed tomography (μ-CT). Also, scanning electron microscopy was used to investigate the microscopic structure of the surface and inside of the residues. The mechanical resistance of the residues was tested by an impact resistance experiment.
The binder influence on the insulation of the coating was small for the investigated systems. Nevertheless, it was interestingly noted, that coatings with high expansion did not provide the best protection. The great influence of the binder material on the inner structure of the foamed residues was revealed by the μ-CT images. Clear differing morphologies were observed. These led to distinct mechanical resistance properties of the tested coatings. Also the change of a low amount of fillers, such as fibres and clay was investigated with similar effects. What is more, a transition of the residue from black, carbonaceous foam with closed cells into an inorganic, residual open cell sponge occurs at high temperatures during the test. This transition is due to the loss of carbon; the change in microstructure is analysed by scanning electron microscopy.
The bench-scale tool presented outreaches screening; the investigation based on the STT Mufu+ delivers a deeper understanding of the phenomena controlling the performance of intumescent coatings.
From halogenated flame retardants to non-halogenated to nanocomposites, each milestone in flame retardancy research led to an increase in performance and safety. With the rise of ceramic precursors in flame retardants, a new field of applications in extreme fire scenarios has become accessible. Intumescent coatings combined with precursors for ceramics show a high temperature transition to a ceramic foam, which provides much better fire resistance than conventional coatings at temperatures beyond 1200°C. Even a protection at 2000 °C for several minutes can be achieved. Combining the expansion property of traditional intumescent coatings with a ceramification at high temperatures leads to high-performance coatings, whose unique properties may prove useful for emergency insulation systems for re-entry bodies in the aerospace industry or special fire protection applications.
In this study, the protection performance in extreme fire conditions, the development of the expansion and the following ceramic transition of a high-performance coating are investigated. To this end, a small scale high-performance burner setup was created. The coated (2.5/4 mm) steel plates (75 x 75 x 2 mm) were exposed to direct flame treatment of a propane-oxygen-burner controlled by two flow controllers. During the test, temperatures above of 1800 °C were reached and steel and flame temperature were recorded. Fire tests of different durations (1, 2.5, 5, 10 and 20 min) were performed. The residues of the different development stages were analysed with non-destructive µ-computed tomography and scanning electron microscopy. The 3D images of the computed tomography provide an insight into the developing cell structure and state of ceramification of the residues.
Fire resistance testing of components made of carbon fibre reinforced polymers (CFRP) composites usually demands intermediate-scale or full-scale testing. In this study, a bench-scale test is presented as a practicable and efficient method to assess the improvement in structural integrity of CFRP with different protective interlayers during fire.
Fire stability is one of the biggest issues of carbon fibre reinforced polymer (CFRP) composites, particularly when they are using in load bearing applications. As soon as the glass transition temperature of polymer matrix (100-200°C) is achieved, the composite loses its structural integrity, what leads to the distortion and failure. The principal fire stability test is based on simultaneous application of fire and mechanical load. Since the carbon fibres can transfer the tensile loads quite well, the compression load is chosen as a required mechanical load for a test. The fire tests were preceded by a static load test at room temperature to determine ultimate failure load. The specimen was loaded with a compression force until the failure load was reached, which was observed as a buckling. For the fire tests, 10% of compression failure load and direct flame of a fully developed fire (heat flux ≈ 180 kW m-2) were applied simultaneously to the specimen, while the time to failure was measured.
The possibilities of bench-scale fire stability testing were presented by investigating new types of laminate structures, which exhibit promising flame retardancy and fireproof properties. The new approach of CFRP laminate differs with a protective concept. Every system consists of two different interlayers (titanium foil, thermoplastic foil PEI, ceramic layer WHIPOX, rubber tape Pyrostat, basalt fibres and kenaf fibres), where the one layer constitutes the fireproof protection, that delays the rise of temperature in the rest of laminate, and the second layer provides very good structural connection with carbon fibre layers, thus improves the mechanical integrity of CFRP composite in fire.
The time to failure of CFRP composite was 17s. Protective systems significantly enhance the fire stability and increased time to failure by 3 to 10 times. Thicker specimens showed longer resistance time, however CFRP laminate with ceramic layer and titanium foil presented outstanding results and the best performance. The protection with Kenaf and basalt fibres offered a natural fibre solution with also good fire resistance performance
Although bench-scale tests are limited with respect to assessing the performance of components and structures, they are valuable in the assessment of different materials concepts. Furthermore, the reduced effort of conducting bench-scale test (lower costs, time, personnel resources) makes it more practical and effective.