Filtern
Dokumenttyp
Sprache
- Englisch (3)
Schlagworte
- Mechanical stress (3) (entfernen)
Organisationseinheit der BAM
DNA long-term stability and integrity is of importance for applications in DNA based bio-dosimetry, data-storage, pharmaceutical quality-control, donor insemination and DNA based functional nanomaterials. Standard protocols for these applications involve repeated freeze-thaw cycles of the DNA, which can cause detrimental damage to the nucleobases, as well as the sugar-phosphate backbone and therefore the whole molecule. Throughout the literature three hypotheses can be found about the underlying mechanisms occurring during freeze-thaw cycles. It is hypothesized that DNA single-strand breaks during freezing can be induced by mechanical stress leading to shearing of the DNA molecule, by acidic pH causing damage through depurination and beta elimination or by the presence of metal ions catalyzing oxidative damage via reactive oxygen species (ROS). Here we test these hypotheses under well defined conditions with plasmid DNA pUC19 in high-purity buffer (1xPBS) at physiological salt and pH 7.4 conditions, under pH 6 and in the presence of metal ions in combination with the radical scavengers DMSO and Ectoine. The results show for the 2686 bp long plasmid DNA, that neither mechanical stress, nor pH 6 lead to degradation during repeated freeze-thaw cycles. In contrast, the presence of metal ions (Fe2+) leads to degradation of DNA via the production of radical species.
Optical multimode fibers made of fused silica are widely used for transmission of high power laser pulses. Bending of fibers creates mechanical stress inside the material. The bend stress of a fiber can be calculated from bend radius, geometrical fiber parameters and Young's Modulus of the fiber core material and reaches typically values of 220 MPa. A thermo-elastic model of Kusov et al. predicts a quadratic dependence of laser-induced damage threshold fluence with applied stress.
In the present study, fiber preform material F300 (Heraeus) was loaded mechanically with pressures up to 220 MPa representing 20% of the pressure resistance of fused silica. Bulk laser-induced damage thresholds (LIDT) were evaluated using a longitudinal multimode Q-switched Nd:YAG laser (1064 nm) at a pulse duration of 12 ns with polarization states parallel and perpendicular to the stress direction. LIDT of fused silica samples of about 700 J/cm2 were found. LIDT did not show a dependence on mechanical pressure and polarization state which is a consequence of the small ratio of maximum applied stress (220 MPa) to Young's Modulus of fused silica (72.5 GPa).
Mechanical stress often accelerates the failure of polymer materials. The aim of this research is to study the interaction between the sealing material FKM and biofuels B10 (heating oil with 10% biodiesel). The mechanical stress test was carried out in a special apparatus. Both mechanical and non-mechanical stress tests were conducted on specimens at 20, 40, and 70 °C for 28 days to document changes in mass, volume, and tensile properties. Both increasing temperature and mechanical stress have a significant effect on the tensile strength of the FKM polymer when exposed to B10. The combination of increasing temperature and mechanical stress induced rupture within 2 h. It was also established that FKM polymer with pre-exposure in B10 survived longer during mechanical stress compared to specimens exposed only to air. With the support of infrared (IR) spectroscopy, we were able to confirm the penetration of B10 into the FKM polymer.