Electrochemical noise measurements on anodically polarised type 304 stainless steel surfaces in contact with buffer solutions of neutral pH were performed to study the effect of chloride ions in the nucleation of pitting corrosion. Passive layer stability and susceptibility to pitting corrosion after pickling and passivation at different environmental conditions were also investigated by means of electrochemical current noise measurements under cathodic and anodic polarisation. According to the obtained experimental results pits nucleate independently on the presence of chloride ions. It has been also shown that protectiveness of stainless steel surfaces after pickling strongly depends on the relative humidity of the environment in which the surface is subsequently passivated.
CO2-induced corrosion of casing and tubing steels is a relevant safety issue for compressing emission gasses into deep geological layers (CCS, Carbon Capture and Storage). The influence of CO2 and pressure of the surrounding media on steels is demonstrated in laboratory experiments providing a corrosive environment similar to a geological onshore CCS-site in the Northern German Basin (T = 60 °C, p = 1 - 100 bar, Stuttgart Aquifer, CO2-flow rate of 3 l/h, 7008000 h exposure time). Corrosion kinetics and microstructures were characterized using specimens of heat treated 42CrMo4 (1.7225, casing) and soft annealed X46Cr13 (1.4034, tubing).
The lifetime reduction of cyclically loaded AISI 420C (X46Cr13, 1.4034) constantly exposed to highly corrosive CO2-saturated hot thermal water is demonstrated in in situ-laboratory experiments (60 °C, brine: Stuttgart Aquifer, flowing CO2: 30 L/h). SN plots, micrographic-, phase-, fractographic- and surface analysis were applied to obtain sustainable information on the corrosion and corrosion fatigue behavior. Maximum number of cycles (here 12.5 × 106 cycles to failure) is reached at σa = 173 MPa. Hydroxide and siderite layers were found on pits and crack surfaces. No typical fatigue limit exists and pit corrosion prior to crack initiation may be identified as failure cause.
Oxygen reduction occurring at the passive layer is probably the most important cathodic reaction involved in corrosion processes on stainless steel. Furthermore, the influence of the surface state on the oxygen reduction reaction is a key point for the understanding of the mechanism of localized corrosion on stainless steel. In this study, electrochemical noise measurements under cathodic polarization were carried out to obtain new information about this influence. It has been confirmed that the surface state of stainless steel plays a very important role in the kinetic of this cathodic reaction. Oxygen reduction kinetics was significantly reduced on passivated surfaces and improved on pre-reduced and ground surfaces. In addition, electrochemical current noise measurements allowed to differentiate between the electrochemical activity produced by the oxygen reduction reaction and that due to the reduction of the passive layer, in direct dependence on the characteristics of the different surface states investigated.