Grain refinement is an important possibility to enhance the mechanical properties such as strength, ductility and toughness of aluminium weld metal. In this study, grain refinement was achieved through the addition of commercial grain refiner Al Ti5B1 to gas tungsten arc weld metal of the aluminium alloys 1050A (Al 99.5) and 5083 (Al Mg4.5Mn0.7). The grain refiner additions led to a significant reduction of the weld metal mean grain size (Alloy 1050A, 86 %; Alloy 5083, 44 %) with a change in grain shape from columnar to equiaxed. Tensile tests showed for Alloy 5083 that the weld metal's ductility can be increased through grain refinement. No improvement in weld metal strength (i.e. yield strength and ultimate tensile strength) was observed. Furthermore, tear tests with notched specimens revealed that the resistance against initiation and propagation of cracks in the weld metal can be enhanced through grain refinement. The toughness was observed to increase clearly by grain refinement in weld metal of commercial pure Al (Alloy 1050A). In Alloy 5083 weld metal, the toughness was not improved through grain refinement, likely because of a semi-continuous network of brittle intermetallic phases that facilitate crack propagation.
Surface modification of mild steel was undertaken using two covered electrodes and two tubular electrodes. The two covered electrodes are DIN 8555: E6-UM-60 and E10-UM-60GR; however, the two tubular electrodes are E10-GF-60GR1 and E10-GF-60GR2. Chemical analysis for the weld metal and XRD of the flux covering for covered electrodes and flux core for tubular electrodes were conducted. The most important factor in determining the wear resistance is the microstructure of the deposit layers. In similar carbon equivalent electrodes E10-UM-60GR and E10-GF-60GR1, electrode E10-GF-60GR1 (tubular) shows larger carbides area fraction and better wear resistance than electrode E10-UM-60GR (covered). This could be attributed to a lower dilution associated with tubular electrode compared with covered electrode. The two tubular electrodes showed higher wear resistance than the covered electrodes which is mainly due to the larger Fe-Cr carbide precipitation area fraction.
Laser-GMA-hybrid welding of longitudinally welded large-diameter pipes of grades API- X80/ X120
(2015)
Potentials of the hybrid laser arc welding processes were investigated regarding reliable production of longitudinal welds of high strength pipe steels X80 and X120
Hybrid laser arc welding of the root pass:
Significant reduction in the weld cross section – savings of filler material
Lower heat input into the base material - improvement of mechanical properties of the weld joint
The arc type does not have any influence on the character of dilution in the laser part of the hybrid weld
14 mm deep root face was considered as optimum. No penetration of the filler material could be detected beyond this depth limit
Metal powder filler wires, micro alloyed with Ni and partly with Cr and Mo, guaranteed sufficient Charpy impact toughness at low temperature for the both investigated materials:
Hybrid laser arc welding is a very efficient process for the root pass in multi-pass welding and opens a large technical and economic potential for the manufacture of large pipes