Filtern
Dokumenttyp
- Zeitschriftenartikel (854)
- Vortrag (849)
- Posterpräsentation (346)
- Forschungsdatensatz (84)
- Beitrag zu einem Tagungsband (43)
- Sonstiges (24)
- Forschungsbericht (16)
- Buchkapitel (13)
- Beitrag zu einem Sammelband (10)
- Zeitschriftenheft (Herausgeberschaft für das komplette Heft) (7)
Sprache
- Englisch (2083)
- Deutsch (186)
- Mehrsprachig (4)
- Spanisch (2)
Schlagworte
- Nanoparticles (170)
- SAXS (121)
- Mechanochemistry (109)
- XPS (104)
- Laser-induced periodic surface structures (LIPSS) (71)
- X-ray scattering (65)
- Microplastics (60)
- Electron microscopy (59)
- Mikroplastik (58)
- MALDI-TOF MS (57)
Organisationseinheit der BAM
- 6 Materialchemie (2275) (entfernen)
Paper des Monats
- ja (18)
The scientific and technological interest in graphene has been growing more and more in the late years due to its outstanding properties and diverse promising applications. However, graphene implementation into the industrial market is still limited and many challenges are yet to be addressed before this material can become suitable for the large-scale production. One of the most crucial challenge to overcome is to develop reliable and reproducible ways to characterize the material properties which can heavily affect the product performance. In our study the chemical composition of nine different samples of industrial graphene, graphene oxide and functionalized graphene were investigated. The samples were analysed both in form of powder and pellets. A comparative characterisation of the chemical composition was performed through X-ray Photoelectron Spectroscopy (XPS) and Energy Dispersive X-ray Spectroscopy (EDX). XPS depth resolution is in the order of 10 nm, while for EDX the analysis was performed at two different energy levels, i.e. 5 keV and 15 keV, and thus varying the analysis depth from 200 nm to 2000 nm. The XPS measurement area is 300x700 µm² while the EDX measurement was performed by analysing a grid of 25 locations (5x5) of 150 x 150 ?m2 area, covering the whole pellet surface of 5 mm diameter and then calculating the mean of the elemental concentration. The results of the elemental concentration values from XPS and EDX analyses show a good agreement for all the elements presents in the samples, despite the different spatial resolutions of the two techniques. Therefore, the samples appear homogeneous both in the lateral and vertical directions. The results relative to powder and pellets samples do not differ in a significant way except for a slight increase in the carbon content regarding the pellet samples, probably due to a minor contamination effect introduced through pressing. Nevertheless, pellets samples appear to be quite representative for the material while being much more convenient in terms of handling and safety compared to nano-powders and providing a regular flat surface for EDX analysis. Finally, this approach correlating XPS and EDS represents a simple, fast and reliable way for characterizing the chemical composition and the homogeneity of industrial graphene. This study is part of the project ?Standardisation of structural and chemical properties of graphene? (ISO-G-SCoPe) which has received funding from the EMPIR programme co-financed by the Participating States and from the European Union?s Horizon 2020 research and innovation programme under Grant agreement No. 19NRM04.
Since its discovery, graphene has got growing attention in the industrial and application research due to its unique properties . However, graphene has not been yet implemented into the industrial market, in particularly due to the difficulty of properly characterizing this challenging material. As most of other nanomaterials, graphene’s properties are closely linked to its chemical and structural properties, such as number of layers, flake thickness, degree of functionalisation and C/O ratio. For the commercialization, suitable procedures for the measurement and characterization of the ultrathin flakes, of lateral dimensions in the range from µm to tens of µm, are essential.Surface chemical methods, especially XPS, have an outstanding role of providing chemical information on the composition. Thereby, one well-known problem for surface analytical methods is the influence of contamination on the composition as in the case of adventitious carbon. The differentiation between carbon originated from the contamination or from the graphene sample itself is often not obvious, which can lead to altered results in the determination of the composition. To overcome this problem, Hard Energy X-ray Photoelectron Spectroscopy (HAXPES) offers new possibilities due to its higher information depth. Therefore, XPS measurement obtained with Al Kα radiation (E = 1486. 6 eV) were compared with analyses performed with a Cr Kα (E = 5414. 8 eV) excitation on functionalized graphene samples. Differences are discussed in terms of potential carbon contamination, but also of oxygen on the composition of the samples. Measurements are performed on O-, N- and F-functionalized graphene. Different preparation procedures (powder, pellet, drop cast from liquid suspension) will be also discussed, correlation of the results with the flakes morphology as well as their validation with other independent methods are in progress.
A comparative analysis is performed by XPS, HAXPES and SEM of industrial functionalised graphene powder of different morphology. The chemical analysis carried out by XPS, which probing depth is around 10nm, and HAXPES, which can reach up to 30nm probing depth. By combining these two techniques is possible to get a rough, non-destructive depth profiling of the sample's surface. The results show a higher concentration of the functionlisation elements on the surface of the sample and the influence of the morphology on the functionalisation process and the C/O ratio.
The presentation shows the results of the mini-interlaboratory comparison focused on the measurement of the morphology of graphene oxide flakes using scanning electron microscopy. In this work, a route for the sample preparation, SEM measurement and image analysis is proposed. The results of the image analysis, performed on 200+ flakes per sample, are presented by comparing the distributions of the size and shape descriptors calculated according to two different approaches. The influences of a different SEM measurement operator, analysis approach and analysis operator on the final size and shape distributions are highlighted.
Lignin is a highly aromatic low value biomass residue, which can be utilized for chemicals, fuels and materials production. In recent years, significant attention has focused on adsorber materials based on lignin. However, only 5% of the available lignin is exploited worldwide, thus significant opportunities for materials development still exist. Lignin has been vastly utilized as a feedstock for the synthesis of adsorbers for the removal of dyes and toxic organic molecules . To improve adsorption capacity, lignin can be chemically modified with oxygen-, nitrogen-, or sulfur-containing functional groups. Most frequently the phenolic groups of lignin were modified. In order to extend the application of lignin as adsorbers, we are especially interested in the chemical modification of this natural resource with a bio-based linear difluoro oligomers LOx (di- or monofunctional) or a heterocyclic monomer (Figure).
We present the optical sensing of phthalate Esters (PAEs), a group of endocrine-disrupting chemicals. The sensing takes place as changes in the fluorescence emission intensity of aminopyrene covalently bound to the organic ligands of the metal−organic framework compound ZIF-8. In the presence of PAEs, a quenching of the fluorescence emission is observed. We evaluated strategies to engineer colloidal size distribution of the sensing particles to optimize the sensory response to PAEs. A thorough characterization of the modified ZIF-8 nanoparticles included powder X-ray diffractometry, transmission electron microscopy, high-performance liquid chromatography, and photophysical characterization. The presented capability of the fluorophore-functionalized ZIF-8 to sense PAEs complements established methods such as chromatography-based procedures, which cannot be used on-site and paves the way for future developments such as hand-held quick sensing devices.
Zeolitic imidazolate framework (ZIF) hybrid fluorescent nanoparticles and ZIF antibody conjugates have been synthesized, characterized, and employed in lateral-flow immunoassay (LFIA). The bright fluorescence of the conjugates and the possibility to tailor their mobility gives a huge potential for diagnostic assays. An enzyme-linked immunosorbent assay (ELISA) with horseradish peroxidase (HRP) as label, proved the integrity, stability, and dispersibility of the antibody conjugates, LC-MS/MS provided evidence that a covalent link was established between these metal-organic frameworks and lysine residues in IgG antibodies.
The development of quick and simple optical sensing technologies for Endocrine Disrupting Chemicals (EDCs) is needed to facilitate monitoring of these substances to ensure consumer safety. Optical sensing was achieved against phthalates acting as EDC that have host guest interaction with an intercalated Metal-organic framework (MOF), resulting in a fluorescence emission upon excitation. The fluorescent turn-on signal was generated by using a fluorophore with a structural component that has little fluorescence unless excimers are formed. Strategies to engineer functional MOF structures suitable for sensing EDC phthalates were developed, and the characterization of the MOFs with and without present phthalates was done by single crystal XRD, PXRD, RAMAN and Thermogravimetry. Extensive photo-physical characterization of host-guest complexes of different phthalates and the MOF as well as the resulting exciplex fluorescence was performed. Photo physical characterization revealed an analyte specific fluorescence fingerprint that allows discerning even minute changes in chemical structures of the analyte and therefore paving the way for sensing tools in real world analytical applications. The presented capability of MOFs to sense EDCs is envisioned to complement established methods from analytical chemistry such as mass spectrometry based methods which can’t be used on site and are often associated with infrastructural capacity constraints
Iron nitride (Fe3N) and iron carbide (Fe3C) nanoparticles can be prepared via sol−gel synthesis. While sol−gel methods are simple, it can be difficult to control the crystalline composition, i.e., to achieve a Rietveld-pure product. In a previous in situ synchrotron study of the sol−gel synthesis of Fe3N/Fe3C, we showed that the reaction proceeds as follows:
Fe3O4 → FeOx → Fe3N → Fe3C. There was considerable overlap between the different phases, but we were unable to ascertain whether this was due to the experimental setup (side-on heating of a quartz capillary which could lead to thermal gradients) or whether individual particle reactions proceed at different rates. In this paper, we use in situ wide- and small-angle X-ray scattering (wide-angle X-ray scattering (WAXS) and small-angle X-ray scattering (SAXS)) to demonstrate that the overlapping phases are indeed due to variable reaction rates. While the initial oxide nanoparticles have a small range of diameters, the size range expands considerably and very rapidly during the oxide−nitride transition. This has implications for the isolation of Rietveld-pure Fe3N, and in an extensive laboratory study, we were indeed unable to isolate phasepure Fe3N. However, we made the surprising discovery that Rietveld-pure Fe3C nanoparticles can be produced at 500 °C with a sufficient furnace dwell time. This is considerably lower than the previous reports of the sol−gel synthesis of Fe3C nanoparticles.