The topography of wear scars on the surface of a steel disc coated with a diamond-like carbon (DLC) layer has been investigated with an Atomic Force Microscope (AFM). AFM topography images have been combined together taking advantage of the stitching technique for the study of wear scars in their initial stage. Moreover, the topography of the sample has been acquired before and after the sliding tests. In this way even very small changes of the sample surface (<10 nm) can be detected. Three main phenomena taking place at the very initial stage of wear could be identified: the abrasion of small asperities bulging out of the sample surface, the carving of swallow grooves with depth under 20 nm, and the partial or total closure of cavities present on the surface. This last phenomenon shows that, before the carving of a wear scar, the plastic deformation of particular regions of the sample, i.e. the volume around the cavities, takes place already after few cycles (in this case between 400 and 800) in the initial phase of the sliding test.
The friction and wear behaviour of thin hard coatings, such as TiN and the promising class of C-based coatings (a-C, a-C:H, and diamond for example), are compared under oscillating and reciprocating sliding conditions. The typical effects of test parameters, such as stroke, frequency, normal force, relative humidity and test duration, are described as a basis for the proper selection of test conditions or, conversely, for the selection of suitable coatings for particular practical applications.
Friction and wear data from over 1000 vibrating tests using thin hard coatings against 100Cr6 and against Al2O3 have been compiled in a database. This allows easy manipulation and comparison of test results. Using selection criteria and filter procedures (e. g., lifetime of coatings, friction limits, and critical wear rate), suitable coating systems for different test conditions can be chosen from the database. The effects of test parameters on friction and wear behaviour and changes have anyway to be known for meaningful tribotesting, as well as for the selection of coatings.