Phase transformations in austenitic stainless steels during low temperature tribological stressing
(2001)
The tribological behaviour at low temperatures is unknown for many materials even for those widely used in cryogenic engineering. Because of the extension of applications of low temperature technologies there is a need for investigations in this field. It is the aim to study the stability of the austenitic structure of FeCrNi alloys under these harsh conditions. This paper deals with tribological experiments with alloys of different stability of the austenitic structure in the temperature range between room and liquid helium temperature. It was found that alloys stable at room temperature show martensitic transformation under tribological stressing and decreased service temperature. The obtained transformation behaviour does not exhibit a linear tendency down to liquid helium temperature. A maximum could be stated.
Nickel‐free high‐nitrogen‐alloyed stainless steels like the P2000 (X13CrMnMoN18‐14‐3) were developed to enhance the strength and corrosion resistance of austenitic stainless steels like 304 and 316 while keeping the typical high ductility. The mechanical and corrosive properties of P2000 were investigated and compared with 304 and 316 to highlight the application opportunities of this new alloy. The microstructure of the solution‐annealed condition was characterised by electron backscatter diffraction and the mechanical properties were studied by uniaxial tensile tests, Charpy impact tests and hardness measurements. The passivation behaviour was analysed using the electrochemical potentiodynamic reactivation, whereas the pitting corrosion resistance was compared by pitting potentials and pitting temperatures. However, secondary thermal influences or suboptimal heat treatment can impair the corrosion resistance due to the precipitation of secondary phases and the resulting sensitisation. Thermodynamic calculations and artificial ageing treatment in the range of 500–900°C for up to 100 h were used to determine critical time–temperature parameters for sensitisation. The microstructure of the various aged states was evaluated by scanning electron microscopy and compared with the degrading corrosion resistance characterised by the KorroPad method.
Laser-gas metal arc (GMA)-hybrid welding enables a high deposition rate and a stable welding process. Process stability was found to be profoundly dependent on the type of the applied filler wire (solid or tubular cored). Whereas solid wires are deposited in pulsed arc mode, tubular cored wire electrodes are weldable by a stable spray-arc process within a wide operating range. This fact applies above all to a high alloyed metal cored wire electrode, of which the achievable deposition rates exceed the upper limits recommended by the manufacturer. A further interesting aspect is the application of a rutile tubular cored wire for positional laser-GMA-hybrid welding. A modern 20 kW-fibre laser source was available for the experiments. This study is concerned with the weldability of high alloyed tubular cored electrodes for high power laser-GMA-hybrid welding. Results obtained from comparative investigations between tubular cored and solid wire electrodes relating to process stability are summarised.
Samples of the austenitic stainless steel grade X5CrNi18‐10 (1.4301, AISI 304) were ground industrially with various grinding parameters to study their influence on corrosion resistance. The ability of the mechanically ground surfaces to form a stable passive layer was evaluated by KorroPad test and a modified electrochemical potentiodynamic reactivation test based on a single loop (EPR‐SL). Furthermore, the surfaces were characterized by surface analytical methods. The main influence was determined regarding abrasive belt type. Surfaces mechanically ground with granulate abrasive belts constantly had a lower corrosion resistance than surfaces ground with single‐coated grain. The granulate abrasive belts generated more sensitized surface areas and left formations of welded sample material on the mechanically ground surfaces. A post‐treatment with a nonwoven abrasive proved to be an effective finishing process by which the surface defects and sensitized material got removed and the surfaces regained the expected corrosion resistance.
Within the framework of an AiF (The German Federation of Industrial Research Associations) project, investigations were conducted into the solidification behaviour of various high-alloy austenitic steels in laser and laser-GMA hybrid welding. For comparison purposes, reference was made to pure gas metalarc welding tests. It was possible to raise the welding speeds in hybrid welding compared with the individual gas metal-arc (GMA) and laser welding processes. The central subjects of the investigations were the type of solidification and the connected hot cracking behaviour during welding. In this respect, particular attention was paid not only to the kinetic effects during solidification which may be caused by the high solidification rates in laser and hybrid welding but also to their consequences.
The chemical composition of a weld metal determines the resulting solidification mode of stainless steel and the consequent weld metal quality. In this work tungsten inert gas (TIG) welding of EN grade 1.4435 austenitic stainless steel was monitored using laser-induced breakdown spectroscopy (LIBS) for the in situ measurement of chemical composition changes. This research aims to prototype a real-time chemical composition analysis system for welding applications and prove the feasibility of such quality control loop. LIBS was used to investigate in situ the monitoring of metal vaporization during TIG welding. We found Mn vapor formation above the weld pool and subsequent condensation of Mn on the weld metal surface using LIBS. Post-weld line scans were conducted by LIBS on various welds produced with different welding currents. Local changes of Ni and Mn were observed at higher welding currents. The results are in good agreement with the literature and proved that LIBS can be used in situ to inspect the TIG welding process.