- Advanced high strength steels (5) (entfernen)
Organisationseinheit der BAM
Advanced high strength steels are usually coated by a zinc layer for an increased resistance against corrosion. During the resistance spot welding of zinc coated steel grades, liquid metal embrittlement (LME)mayoccur. As a result, cracking inside and around the spot weld indentation is observable. The extent of LME cracks is influenced by a variety of different factors. In this study, the impact of the used electrode geometry is investigated over a stepwise varied weld time.
A spot welding finite element simulation is used to analyse and explain the observed effects. Results show significant differences especially for highly increased weld times. Based on identical overall dimensions, electrode geometries with a larger working plane allow for longer weld times, while still preventing LME within the investigated material and maintaining accessibility.
A method is reported with which heat affected zone (HAZ) cracks in a specific region of spot welded joints, made of advanced high strength steels, could be realised. The influence of HAZ cracks on the fatigue behaviour, which is the focus of the contribution, was studied by evaluating the stiffness characteristics as a function of the number of cycles N in comparison with crack-free specimens, i.e. by analysing HAZ and fatigue cracks on the specimen surface and the surface of fatigue fractures containing beach marks. It was found that the fatigue cracks are not initiated at the HAZ cracks. The number of cycles to failure Nf is not significantly reduced for specimens with HAZ cracks. Overall, the examinations did not reveal any influence of HAZ cracks on the fatigue strength of resistance spot welded joints.
Resistance spot welded joints made of two advanced high strength steels (AHSS) and one high strength steel (HSS) were examined. In the high cycle fatigue regime tests were realised for one loading condition, and the load and the displacement were measured. From the load and displacement range, the stiffness was calculated and in situ normalised to its value after 1000 cycles. It was thus possible to use the normalised stiffness evaluated during the experiment as failure criterion for the fatigue test of resistance spot welded joints. In order to evaluate this failure criterion, fatigue cracks were produced in the three different steel grades mentioned above according to user-specified levels of the normalised stiffness. It was found that the fatigue crack area increases linearly and the through-sheet-thickness crack length exponentially with decreasing stiffness. The comparison of the fatigue crack propagation during the fatigue test of the three different tested base metals showed very similar values. The comparability of fatigue tests performed on spot welded joints might thus be improved by the in situ evaluated stiffness as a failure criterion. This can be also used in further work to verify results of computer simulations of the stress intensity factor at spot welds with the help of experimental results.
Grain-boundary degradation via liquid-metal embrittlement (LME) is a prominent and long-standing failure process in next generation advanced high-strength steels. Here we reveal, well ahead of the crack tip, the presences of nano-scale grains of intermetallic phases in Zn-infiltrated but uncracked grain boundaries with scanning- and 4D transmission electron microscopy. Instead of the often-reported Znrich Fe-Zn intermetallics, the nano-scale phase in the uncracked infiltrated grain boundaries is identified as the G-phase, and its presence reveals the local enhancement of strain heterogeneities in the grain boundary network. Based on these observations, we argue that intermetallic phase formation is not occurring after cracking and subsequent liquid Zn infiltration but is instead one of the primary nanoscopic drivers for grain-boundary weakening and crack initiation. These findings shift the focus of LME from micro- and meso-scale crack investigations to the very early stages immediately following Zn diffusion, after which secondary phase nucleation and growth emerge as the root-cause for failure.
Liquid metal embrittlement (LME) cracking is a phenomenon observed during resistance spot welding (RSW) of zinccoated advanced highstrength steels (AHSS) in automotive manufacturing. In this study, severe cracks are observed at the edge of the sheet under reduced flange widths. These cracks, traversing the AHSS sheet, culminate at the edge with a width of approximately 1.2 mm.
Through combined numerical and experimental investigations, and material testing, these cracks are identified and validated as a new type of LME crack. The mechanism behind this crack formation is attributed to unique geometric conditions that, when compared to center welding, amplify radial material flow by ninefold to 0.87 mm. The resultant tangential tensile stresses approximate 760 MPa, which exceed the yield strength of the examined advanced highstrength steel (AHSS) under heightened temperature conditions, and when combined with liquid zinc, promote the formation of this new type of LME crack.