Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Tagungsband (27)
- Vortrag (24)
- Zeitschriftenartikel (20)
- Beitrag zu einem Sammelband (5)
- Posterpräsentation (5)
Sprache
- Englisch (81) (entfernen)
Schlagworte
- Fatigue (14)
- Non-destructive testing (8)
- Damage evolution (7)
- CFRP (5)
- Composite (5)
- Wind turbine blades (5)
- Crack propagation (4)
- Fracture mechanics (4)
- Fully developed fire (4)
- Polymer matrix composites (4)
Organisationseinheit der BAM
- 5 Werkstofftechnik (32)
- 5.3 Polymere Verbundwerkstoffe (32)
- 8 Zerstörungsfreie Prüfung (8)
- 8.5 Röntgenbildgebung (3)
- 8.0 Abteilungsleitung und andere (2)
- 8.6 Faseroptische Sensorik (2)
- 4 Material und Umwelt (1)
- 4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung (1)
- 5.0 Abteilungsleitung und andere (1)
- 7 Bauwerkssicherheit (1)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (24)
A new patented dynamic mechanical analysis (DMA) is presented, where the tensile, bending- or torsional stiffness of a media can be characterized in-situ during the phase transition from liquid to solid. An epoxy system, e.g. Hexion L285/H287, is filled into an elastomer container, such as a silicone tube. This can be mounted into a conventional OMA and, based on a linear viscoelastic approach, the storage modulus (E';G'), the loss modulus (E'';G'') and the loss angle tan(δ) can be measured at constant temperature as a function of time in order to investigate the liquid to sol-gel to solid transition. With this new method, the stiffness increase as a result of the cure process can be directly measured more precisely than with a rheometer in a shear plate set-up, because using an elastomer container gives a defined cross section for calculating the Young's modulus.
CFRP are more and more used in modern civil aircrafts hence the whole fuselage is made of this material (B787; A350). Due to strict certification Standards finally the normal in-service loading gives a low stress level compared to the static and even the fatigue strength of the material. Hence CFRP are assumed to have an infinite life. To evaluate this assumption, fatigue tests on CFRP-specimens were performed up to 108 load cycles. The first inter-fiber failure was evaluated non-destructively by the fatigue tests accompanying X-ray-refraction topography altemately and in-situ mechanical loading. The basic idea of the investigation is represented in fig. 1. At low load levels it could not be assumed the total failure of the samples. Hence accompanying non-destructive testing (NDT) is mandatory to get information about the damage state of the material.
A shell test bench was developed at BAM 5.3 which allows for static and fatigue testing of curved fiber-reinforced plastic (FRP) structures, during which in-situ the damage state can be non-destructively inspected by thermography and strain-field measurement techniques. Sandwich shell specimens with typical wind turbine blade manufacturing defects were designed and tested. The tested imperfections show a fairly significant reduction (up to 90%) of the shell test specimens‘ lifetime, depending on the type of imperfection. Using the in-situ NDT methods incorporated in the shell test bench, the location and cycle time of the initial defects and the damage evolution was investigated.
Carbon Fibre Reinforced Plastics (CFRP) are more and more used in modern civil aircrafts. These days the whole fuselage is made of this material (B787; A350). Due to strict certification standards the normal in-service loading gives a low stress level compared to the static and even the fatigue strength of the material. Hence CFRP are assumed to have an infinite life. To evaluate this assumption, fatigue tests on CFRP-specimens were performed up to 108 load cycles and the first inter-fibre failure was evaluated non-destructively by accompanying Xray-refraction topography. A tensile testing machine was integrated in a small angle X-ray scattering (SAXS) setup. X-ray refraction topography was performed while the CFRP samples were tensile loaded. This non-destructive technique enables the detection of micro-cracking and inter-fibre failure especially for CFRP. For Glass Fibre Reinforced Plastic (GFRP) X-ray refraction and in-situ loading has already been successfully used. The increase of inner surfaces due to inter fibre failure was measured as a function of the stress state. Fatigue tests were performed at and below the limit of inter-fibre failure strength. State of the art is to assume the failure of the samples under cyclic loading as the fatigue life. Accompanying non-destructive X-ray refraction measurements reflects the damage state and enables to trace its evolution even if the total failure of the specimens does not occur. This investigation technique is of high interest to give the engineer a design value of infinite life which is practically often reached due to knock down factors of certification standards. Finally the infinite life was found for cyclic fatigue loaded CFRP-samples even under high inter fibre transverse and shear loading investigated up to 108 load cycles.
Lightweighting as a cross-cutting technology contributes significantly to achieve the European Green Deal goals. Based on, but not limited to, advanced materials and production technologies, the demand for natural resources and CO2 emmissions are reduced by lightweighting during production, as well as use phase. Therefore, lightweighting is a crucial transformation technology assisting in decoupling economic growth from resource consumption. In this manner, lightweighting contributes significantly as a key technology of relevance for many industrial sectors such as energy, mobility, and infrastructure, towards resource efficiency, climate action and economic strength, as well as a resilient Europe. To strengthen international partnerships, addressing global issues of today at the edge of science with high performance lightweight material based on carbon fibers, an overview about the BAM expertise in carbon fiber reinforced materials is given.
A new approach is discussed for characterizing the damage state of FRP with the appearance of micro cracking and its influence on the residual strength. For the quantitative analysis of micro cracking, X-ray refraction topography was used. Fatigue treatment of carbon fibre reinforced plastics (CFRP) laminates were performed to create defined damage states. With regard to real loading conditions of CFRP, studies on tube samples were performed to investigate two dimensional (tensiontorsion) loads. A rheological material model was presented which described the increase of micro cracking in ±45° CFRP laminates with a continuum mechanical approach. The correlation between the results of the X-ray refraction topography, the damage parameter of the rheological model and the decrease of residual strength were shown. The inter fibre fracture surface of the investigated CFRP materials was determined with tensiontorsion loaded tube specimens of 90°-laminate and a layer-wise strength analysis was done. Micro cracking occurs even at 50% inter-fibre fracture loading and can lead to a distinct strength reduction. The intralaminar fatigue effect itself seems to be an indication for the damage accumulation and the load history.
The damage process of short glass fibre (30% weight) reinforced polyamide caused by mechanical loading was investigated from the beginning on micro cracking level to the incipient crack of mm-dimension. Based on high resolution computer tomography and the X-ray-refraction technique the inner surface due to micro-cracking at the short fibre ends and the fibre matrix debonding of the skin surface of the filament was determined quantitatively. With the knowledge of the fatigue crack propagation rate and fracture toughness of the material from former research projects, it was derived that the total inner surface due to micro cracks measured by X-ray refraction is much higher than the specimen could have withstand the load, supposed the surface is in a localized crack. Hence, the damage process could be described from micro to macro level. Accompanying fractographic investigations endorse the modelling based on the NDT-techniques.