Electrochemical noise (EN) enables corrosion research and monitoring in real time and with high sensitivity. In the case of submicroscopic nucleation events of pitting corrosion it has been observed that the cathodic process plays a decisive role in the mechanism as well as in the origin of EN signals, which depend not only on the metallic dissolution reaction but also on the electron-consuming process. EN signals arising from the nucleation process of localized corrosion on stainless steels can only be recorded due to the inhibition effect on the cathodic process achieved by the spontaneous formation of the passive layer. In consequence, passive layer stability becomes a significant factor in influencing EN signals. The way in which the passive layer stability affects the acquisition and analysis of EN signals arising from pitting corrosion on stainless steels is discussed in detail.
Unwanted corrosive phenomena on stainless steel surfaces like rouging had been observed for years occurring at certain service conditions. Rouging consists in the formation of a colored surface film containing mainly iron on metallic surfaces in contact with high-purity waters. In spite of numerous hypotheses and experimental examinations a clear explanation about the origin of rouging on stainless steels is currently still lacking. Because rouging occurs even at well passivated stainless steel surfaces the origin of this corrosive phenomenon should be related to the weakness of the stability of the passive film. In the present paper electrochemical noise measurements regarding the stability of the passive layer of alloy 904L (1.4539, X1NiCrMoCu25-20-5) in high-purity water at 70 °C depending on the cathodic process are presented. In addition, the importance of the cathodic reaction on the passivation and stability of the passive layer is discussed.
Oxygen reduction occurring at the passive layer is probably the most important cathodic reaction involved in corrosion processes on stainless steel. Furthermore, the influence of the surface state on the oxygen reduction reaction is a key point for the understanding of the mechanism of localized corrosion on stainless steel. In this study, electrochemical noise measurements under cathodic polarization were carried out to obtain new information about this influence. It has been confirmed that the surface state of stainless steel plays a very important role in the kinetic of this cathodic reaction. Oxygen reduction kinetics was significantly reduced on passivated surfaces and improved on pre-reduced and ground surfaces. In addition, electrochemical current noise measurements allowed to differentiate between the electrochemical activity produced by the oxygen reduction reaction and that due to the reduction of the passive layer, in direct dependence on the characteristics of the different surface states investigated.
While the possibilities of improving corrosion resistance (especially galvanic corrosion) by alloying are limited, surface finishing of magnesium alloys is the alternative for improving corrosion resistance. Due to the low corrosion potential of Mg and the danger of galvanic corrosion in the case of a coating defect, the choice of coatings is limited. This chapter will summarize the corrosion behavior of magnesium alloys and the metallurgical possibilities to improve the corrosion resistance of the alloys and reviewing critically the most commonly used surface treatments and coatings for magnesium.