Overview of ongoing research and future prospects on polyethylene neutron shielding materials at bam
(2023)
The extension of the interim storage period of radioactive waste before disposal will cause additional challenges for the nuclear waste management in Germany, so that an extensive knowledge of the long-term performance of casks, including their components and inventories, will be required for future extended storage licenses.
Ultra-high and high molecular weight polyethylenes ((U)HMW-PE) are used for neutron shielding purposes in casks for storage and transport of spent fuel and high-level waste due to their extremely high hydrogen content. During their service life of several decades as cask components, the PE materials are exposed to neutron and gamma radiation from the radioactive inventory of the casks, mechanical assembling stresses and temperature. All these combined effects affect the material properties of such components which in turn may be crucial for some possible accident scenarios.
At the Bundesanstalt für Materialforschung und -prüfung (BAM), the effects of high temperature exposure in combination with subsequent or previous irradiation were investigated with a comprehensive aging program including thermal aging at 125 °C for different aging periods up to 5 years and irradiation with doses ranging from 50 to 600 kGy.
This contribution provides an overview of the ongoing research related to the structural changes of (U)HMW-PE induced by gamma irradiation and high temperature exposure and focuses on current research perspectives at BAM with regard to the prediction of the dynamic behavior of the material during extended interim storage in case of an accident scenario. First results of the coupled effect of temperature, radiation and mechanical loading will be presented. The effect of microstructural changes induced by gamma irradiation and high temperature on the mechanical behavior of (U)HMW-PE will be assessed.
Overview of ongoing research and future prospects on polyethylene neutron shielding materials at BAM
(2023)
The extension of the interim storage period of radioactive waste before disposal will cause additional challenges for the nuclear waste management in Germany, so that an extensive knowledge of the long-term performance of casks, including their components and inventories, will be required for future extended storage licenses.
Ultra-high and high molecular weight polyethylenes ((U)HMW-PE) are used for neutron shielding purposes in casks for storage and transport of spent fuel and high-level waste due to their extremely high hydrogen content. During their service life of several decades as cask components, the PE materials are exposed to neutron and gamma radiation from the radioactive inventory of the casks, mechanical assembling stresses and temperature. All these combined effects affect the material properties of such components which in turn may be crucial for some possible accident scenarios.
At the Bundesanstalt für Materialforschung und -prüfung (BAM), the effects of high temperature exposure in combination with subsequent or previous irradiation were investigated with a comprehensive aging program including thermal aging at 125 °C for different aging periods up to 5 years and irradiation with doses ranging from 50 to 600 kGy.
This contribution provides an overview of the ongoing research related to the structural changes of (U)HMW-PE induced by gamma irradiation and high temperature exposure and focuses on current research perspectives at BAM with regard to the prediction of the dynamic behavior of the material during extended interim storage in case of an accident scenario. First results of the coupled effect of temperature, radiation and mechanical loading will be presented. The effect of microstructural changes induced by gamma irradiation and high temperature on the mechanical behavior of (U)HMW-PE will be assessed.
Materials used in military applications have to withstand multiple threats like ballistics and explosions. Thus, high-strength low alloyed (HSLA) steels are used. The main joining technique for metals is welding. Therefore, analysing the dynamic impact behaviour of high-strength welds is very important to fulfil these demands.
Investigation of welds at high strain rates has rarely been conducted in the past. To determine the dynamic impact behaviour of hybrid laser-arc welds, the Split Hopkinson Pressure Bar (SHPB) technique was used. The base material was a quenched and tempered fine-grained armour steel with yield strength of 1100 MPa.
First, a full hybrid laser-arc weld was investigated by extracting specimens consisting of weld metal and heat affected base material. The influence of two variables, the cooling time between 800 °C and 500 °C (t8/5) and strength of filler material, on the impact behaviour was studied. The cooling time t8/5 was varied by preheating to influence the microstructure in the HAZ and to analyse the effect on the hardness and dynamic compressive strength.
Subsequent analysis to detail the original Investigation was carried out by dilatometer heat treatment of specimens to create homogenous subzones of the weld. These specimens have a homogenous microstructure of HAZ and were tested by SHPB to determine the stress-strain characteristics for the different microstructures of HAZ.
The results of the weld specimen showed the effect of preheating and filler material strength on the dynamic compressive behaviour. The analysis of the different microstructures of the HAZ indicated that especially the tempered microstructure caused a reduction in dynamic compressive strength.